xPRO1100 Black resin Nexa 3D

Reference:

Brand: Nexa 3D

This product could be delivered in a longer time than the standard.

Condition: New product

Format

Quantity

240,00 €

Ask for information

Engineering resin ideal for the 3D printing of automotive and aerospace parts, or consumer products.

Add to wishlist

More info
Data sheet
Download
Usage tips
Specifications

The xPRO1100 Black resin from the Nexa3D portfolio of engineering resins is meticulously designed to meet the rigorous demands of industrial applications, offering unparalleled performance and reliability. With its versatile applications spanning across automotive components, aerospace prototypes, engineering parts, and consumer products, this resin sets a new standard in additive manufacturing.

Part 3D printed with the xPRO1100 Black resin

Image 1: Part 3D printed with the xPRO1100 Black resin. Source: Nexa3D.

Nexa3D's commitment to quality is demonstrated through extensive testing under hostile industrial environments. Parts 3D printed with the xPRO1100 Black resin undergo rigorous assessments, including glow-wire test, hot-wire ignition (HWI), flammability, and accelerated UV ageing, ensuring exceptional resistance to UV rays, extreme temperatures, chemical agents, and pressure.

Parts 3D printed with the xPRO1100 Black resin perform well in accelerated UV ageing tests

Image 2: Parts 3D printed with the xPRO1100 Black resin perform well in accelerated UV ageing tests. Source: Nexa3D.

One of the hallmark features of the xPRO1100 Black resin is its superior UV resistance, with minimal color alteration and negligible loss of properties even after prolonged exposure. Moreover, the xPRO1100 Black resin boasts industrial-grade chemical resistance, as evidenced by weight and mechanical performance measurements of submerged parts in substances like acetone, brake fluid, engine oil, and sodium hydroxide.

Part 3D printed with the xPRO1100 Black resin

Image 3: Part 3D printed with the xPRO1100 Black resin. Source: Nexa3D.

For comprehensive insights into the performance metrics, detailed test results are readily available in the Technical Datasheet in the Downloads section. Elevate your additive manufacturing capabilities with the xPRO1100 Black resin, engineered for precision, durability, and unmatched reliability in the most demanding industrial settings.

Elongation at break (%)	5
Tensile strength (MPa)	67
Tensile modulus (MPa)	2870
Flexural strength (MPa)	125
Flexural modulus (MPa)	2790
Surface hardness	9
UV resistance	UV resistance
Chemical resistance	Chemical resistance

xPRO1100 Black Datasheet

Download

xPRO1100 Black Safety Datasheet

Download

Parts 3D printed with the Nexa 3D xPRO1100 Black resin will achieve their specific properties only after being subjected to post-processing by washing and curing. If applicable, the support structures must be removed from the part before curing and the part must be washed. Nexa3D recommends using xClean (max. 2 minutes) followed by IPA alcohol (max. 5 minutes).

Once washed, the parts 3D printed with the xPRO1100 Black resin must be dried and then cured either with the help of an LED or wide spectrum lamp, or in the Nexa 3D Wash+Cure station developed especially for the washing and curing of parts 3D printed on the XiP 3D printer. The recommended washing, drying and curing times can be consulted on the manufacturer's website for each Nexa 3D resin. After the post-curing, parts 3D printed with the xPRO1100 Black resin can be subjected to an additional thermal treatment. The instructions can be found in the product's Technical Datasheet in the Downloads section.

Certain precautions must be taken when working with 3D printing resins. The user must ensure that the working space is adequately ventilated, and that protective goggles, gloves and garments are worn at all times. The xPRO1100 Black resin should be stored in a tightly closed container/resin vat to avoid resin deterioration due to UV exposure. The container/vat should be kept in a cool, well ventilated area away from heat, sparks and open flame.

More information on how to print and post-process the Nexa 3D resins can be found here.

General information
Manufacturer	Nexa 3D
Technology	mSLA/LSPc
Material	Photopolymer
Wavelength	-
Format	1.5 kg
Color	Black
Compatible 3D printers	Nexa 3D
Printing properties
Layer height	-
Layer exposure time	-
Layer cooling time	-
Lifting height	-
Exposure of bottom layers	-
Number of bottom layers	-
Curing and washing properties
Washing time	Washing time
Curing time	Curing time
Curing temperature	Curing temperature
Mechanical properties
Izod impact resistance (ASTM D256)	21 J/m (notched)
Charpy impact resistance (ISO179-1)	1.11 kJ/m²
Elongation at break (ASTM D638)	4 %
Tensile strength (ASTM D638)	71 MPa
Tensile modulus (ASTM D638)	3010 MPa
Flexural strength (ASTM D790)	125 MPa
Flexural modulus (ASTM D790)	2790 MPa
Surface hardness (ASTM D2240)	Shore 84 D
Thermal properties
Softening temperature	-
Brightness value	-
Additional information
Service life	-
HS Code	2916.1

* The typical values listed in this table should be considered as a reference. Actual values may vary depending on the 3D printer model used, part design and printing conditions. We recommend confirming the final results and properties with your own tests. For further information please refer to the product data sheet.