xPRO410 resin Nexa 3D

Reference:

Brand: Nexa 3D

This product could be delivered in a longer time than the standard.

Condition: New product

6 Item Items

Format

Quantity

99,00 €

Ask for information

High accuracy rigid resin with great surface finish for prototyping and production.

Add to wishlist

More info
Data sheet
Download
Usage tips
Specifications

The xPRO410 3D printing resin is the result of a collaboration between Nexa 3D and Henkel. Nexa 3D, an American manufacturer of ultrafast resin 3D printing equipment and materials, has developed the xPRO410 resin based on Henkel's LOCTITE PRO410 polymer, optimizing and personalizing it to be used with the Nexa 3D printers.

Video 1: Introducing the Nexa 3D xPRO410 resin. Source: Nexa 3D.

The xPRO410 resin is a rigid (Shore 79D) photopolymer that produces isotropic parts with extreme accuracy (within 0.2 % after post curing), capable of working in temperatures of up to 70 ºC. Furthermore, parts made with the xPRO410 resin have an exceptional surface finish, exhibit low shrinkage during printing, and involve a lower cost per part compared to competitive materials.

Parts 3D printed with the xPRO410 resin

Image 1: Parts 3D printed with the xPRO410 resin. Source: Nexa 3D.

In combination with the Nexa 3D ultrafast XiP 3D printer, the xPRO410 resin allows for the production of general purpose prototypes and small series at an astonishing rate of 18 cm per hour thanks to the Nexa 3D proprietary LSPc and Everlasting Membrane technologies. The xPRO410 resin comes in the format of an easy-to-use 1 kg cartridge as well as a 5 kg bottle for refilling the cartridge.

Parts 3D printed with the xPRO410 resin

Image 2: Parts 3D printed with the xPRO410 resin. Source: Nexa 3D.

The fast build speed applies to all Nexa 3D resins and printers, and allows for same-day or next-day fullfilment of orders and up to twentyfold productivity gains for projects and businesses of all sizes. The ideal applications for the xPRO410 resin are models for quick design verification, display models, and models where accuracy and resolution are critical.

Elongation at break (%)	5.5
Tensile strength (MPa)	41
Tensile modulus (MPa)	2365
Surface hardness	8
Softening temperature (ºC)	61

Parts 3D printed with the Nexa 3D xPRO410 resin will achieve their specific properties only after being subjected to post-processing by washing and curing. If applicable, the support structures must be removed from the part before curing and the part must be washed. Nexa3D recommends 2 wash intervals (2 minutes each) in IPA alcohol or xClean. It is recommended to use two buckets in the cleaning process, especially when working with multiple resin colors, to prevent resin residue from sticking to the part.

Once washed, the parts 3D printed with the xPRO410 resin must be dried and then cured either with the help of an LED or wide spectrum lamp, or in the Nexa 3D Wash+Cure station developed especially for the washing and curing of parts 3D printed on the XiP 3D printer. The recommended washing, drying and curing times can be consulted on the manufacturer's website for each Nexa 3D resin.

Certain precautions must be taken when working with 3D printing resins. The user must ensure that the working space is adequately ventilated, and that protective goggles, gloves and garments are worn at all times. The xPRO410 resin should be stored in a tightly closed container/resin vat to avoid resin deterioration due to UV exposure. The container/vat should be kept in a cool, well ventilated area away from heat, sparks and open flame.

More information on how to print and post-process the Nexa 3D resins can be found here.

General information
Manufacturer	Nexa 3D
Technology	mSLA/LSPc
Material	Photopolymer
Wavelength	-
Format	1 kg 1.5 kg 5 kg
Color	Black
Compatible 3D printers	Nexa 3D
Printing properties
Layer height	-
Layer exposure time	-
Layer cooling time	-
Lifting height	-
Exposure of bottom layers	-
Number of bottom layers	-
Curing and washing properties
Washing time	Washing time
Curing time	Curing time
Curing temperature	Curing temperature
Mechanical properties
Izod impact resistance (ASTM D256)	25 J/m (notched)
Charpy impact resistance	-
Elongation at break (ASTM D638M)	5.5 %
Tensile strength (ASTM D638M)	41 MPa
Tensile modulus (ASTM D638M)	2365 MPa
Flexural strength	-
Flexural modulus	-
Surface hardness (ASTM D2240)	Shore 79D
Thermal properties
Softening temperature (ASTM D648)	61 ºC (@ 0.45 MPa)
Brightness value	-
Additional information
Service life	-
HS Code	3906.10

* The typical values listed in this table should be considered as a reference. Actual values may vary depending on the 3D printer model used, part design and printing conditions. We recommend confirming the final results and properties with your own tests. For further information please refer to the product data sheet.