Industrial ABS - HARZ Labs

Reference: HL-IND-ABS-LCD-1000

Brand: HARZ Labs

Condition: New product

6 Item Items

Quantity

100,00 €

Ask for information

Engineering resin compatible with LCD and DLP printers, enabling the production of prototypes or final parts.

Add to wishlist

More info
Data sheet
Download
Usage tips
Specifications

HARZ Labs is a resin manufacturer with extensive experience in chemicals, especially polymers, developing and producing high quality materials for all types of resin 3D printer technologies (DLP / LCD, SLA, CJP and others).

Industrial ABS is a resin developed for LED-LCD and DLP 3D printers that allows the manufacture of final parts or functional prototypes. Parts made with this polyurethane-based resin, once cured, have mechanical properties that are close to those of injected ABS: high hardness and toughness. In terms of chemical properties, they are similar to those of polyurethane and as strong as those of injected ABS.

Part 3D printed with Industrial ABS resin

Image 1: Part 3D printed with Industrial ABS resin. Source: Harz Labs.

Due to its characteristics, Industrial ABS resin is a suitable material for the printing of parts for the automotive industry, among others. This resin offers high precision and is odourless.

One of the biggest advantages is that this resin is compatible with almost any type of DLP LCD resin 3D printer: UniZ, Zortrax, ANYCUBIC, etc.

Hide color variations	(Hide color variations)

Ind ABS safety datasheet

Download

Ind ABS datasheet

Download

Once an impression has been completed, the part must be removed from the manufacturing platform with the metal spatula, taking care not to damage the surface of the platform. The part is then immersed in IPA for 6-10 minutes, depending on the colour of the resin and the size of the part, to remove the uncured resin from the outer walls of the part. After this time, air pressure should be applied to the piece until it is completely dry. To achieve the maximum properties that HARZ Industrial ABS can provide, it is necessary to cure the resin for 10-20 minutes at a temperature of 60 ºC (to eliminate internal stresses) in a curing centre (Form Cure) with a wavelength of 405 nm.

Before removing the parts from the manufacturing base, the user must be equipped with a series of safety measures. The use of gloves is recommended to prevent resin and alcohol from contacting the skin. It is also crucial to wear safety glasses for any drops that may arise during the washing of the parts.

General information
Manufacturer	HARZ Labs (Russia)
Technology	LCD / DLP
Material	Photopolymer
Wavelength	UV 405 nm
Format	1 kg 0.5 kg (on request, contact us)
Colour	Translucent
Compatible 3D printers	UniZ, WANHAO, zortrax, ANYCUBIC, ASIGA, B9 Creator, PRUSA, Elegoo.
Printing properties
Layer height	100-50-25 μm
Layer exposure time	See manufacturers' recommended print values in the following link.
Layer cooling time
Elevation height
Exposure of the lower layers
Number of lower layers
Curing and washing properties
Washing time	2 х 3 min
Curing time	Recommended: 10 - 20 min Total curing time: 35 min
Curing temperature	60 ºC
Mechanical properties
Izod impact resistance (ASTM D4812)	9.5 ± 2.7 KJ/m²
Charpy impact resistance	-
Elongation at break (ASTM D638)	7.2 ± 2.5 %
Tensile strength (ASTM D638)	25.8 ± 5.2 MPa
Traction module	-
Flexural strength (ASTM D790)	47.9 ± 0.5 MPa
Bending module (ASTM D790)	2098 ± 160 MPa
Surface hardness (ASTM D2240)	84 ± 2 Shore D
Thermal properties
Softening temperature
Further information
Lifetime (from manufacture)	24 months
HS Code	2916.1

* The typical values detailed in this table should be considered as a reference. Actual values may vary depending on the 3D printer model used, part design and printing conditions. We recommend that you confirm the results and final properties with your own test. For further information, please refer to the product data sheet.