No products

To be determined Shipping

0,00 € Tax

0,00 € Total

Check out

Product successfully added to your cart

0 products in the cart 1 product in the cart

Quantity:

Checkout

Our webstore uses cookies to offer a better user experience and we recommend you to accept their use to fully enjoy your navigation.

More information Gestionar cookies

I accept

View larger

BASF Ultracur3D® EPD 2006

Reference:

Brand: BASF

This product could be delivered in a period exceeding the standard.

Condition: New product

Colour

Quantity

337,25 €

-5%

355,00 €

Ask for information

Rigid resin with daylight technology ideal for the manufacture of large objects.

Add to wishlist

More info
Download
Usage tips
Specifications

BASF is a renowned manufacturer specialising in the development of chemical products. Its product range includes products for the production of 3D printing materials for FDM, resin and SLS.

Ultracur3D® EPD 2006 resin is a resin for daylight resin technology, i.e. for use in visible light printers such as Photocentric printers. Daylight is a lower energy, longer wavelength light that ensures more reliable polymerisation than UV light.

Photocentric has teamed up with BASF to create a range of Engineering Plastic Daylight (EPD) materials for a wide range of applications.

Image 1. Part made with Ultracur3D® EPD 2006 resin. Source: BASF

Ultracur3D® EPD 2006 resin is a daylight reactive urethane photopolymer for daylight resin technology that features high stiffness and temperature resistance. This resin, available in black, is ideal for the manufacture of large objects, highly detailed and textured parts, custom tooling, etc.

Technical sheet 2006

Download

EPD 2006 Safety Datasheet ES

Download

Before starting a print, the resin should be shaken well and, if possible, vacuumed to remove any bubbles that may have formed.

Once printed, the pieces should be cleaned with isopropyl alcohol. To do this it is advisable to immerse the pieces in a container with isopropyl alcohol and place this container in an ultrasonic cleaner for 4 minutes. It is recommended not to immerse the piece for long periods of time to avoid deformation and softening.

After cleaning, the pieces should be dried for 30 minutes at 40 ºC. Once dry, parts printed with BASF Ultracur3D resins should be cured at room temperature to obtain optimum properties. Curing conditions will depend on the characteristics of the printer used and the curing equipment.

All customers who have purchased any resin from the BASF Ultracur3D range can request the appropriate user guide. This can be done using the contact form by selecting "Technical Support" in the subject line and the order number of the resin.

General information
Manufacturer	BASF
Technology	EPD
Material	Daylight reactive urethane photopolymer
Wavelength	-
Format	5 kg
Colour	Black
General properties
Viscosity (30 ºC)	310 mPas
Viscosity (50 ºC)	88 mPas
Density (solid) (ASTM D792)	1.2 g/cm³
Density (liquid)	-
Mechanical properties
Young's modulus (ASTM D638)	-
Tensile strength (ASTM D412C)	50 MPa
Elongation at break (ASTM D412C)	10.3 %
Bending modulus (ASTM D790)	2210 MPa
Bending strength (ASTM D790)	90 MPa
Impact resistance	-
Impact resistance at 23 °C (Izod indented ASTM D256)	11 J/m
Impact resistance at 23 ºC (Charpy indented ISO 179-1)	0.7 kJ/m2
Hardness (Shore D, ASTM D2240)	80
Wear resistance	-
Resilience	-
Compression at 23 ºC, 72h	-
Thermal Properties
HDT to 0.45 MPa (ASTM D648)	81 °C
HDT to 1.82 MPa (ASTM D648)	61 °C
Flammability (UV 94 1.5 mm)	-
Other
Service life	12 months
HSCODE	2916.1

* The typical values listed in this table should be considered as a reference. Actual values may vary depending on the 3D printer model used, part design and printing conditions. We recommend confirming the final results and properties with your own tests. For further information please refer to the product data sheet.