PolyTerra Dual PLA


New product

69 Items

23,65 €
23,65 €

Ask for information

Easy to print and post-process PLA filament with dual color effect. 

The PolyTerra Dual PLA is a PLA filament created by Polymaker as part of their PolyTerra filament family. The PolyTerra materials are sustainable bioplastics characterized by ease of use, high printing quality, speed and reliability, as well as eco-friendly packaging and increased biodegradability (in industrial conditions). PolyTerra PLA also stands out due to its stunning matte finish, a wide range of colors, and ease of post-processing by painting and sanding.

The Polyterrra Dual PLA colors Chameleon, Shadow Orange, Shadow Red and Mixed Berries

Image 1: The Polyterrra Dual PLA colors Chameleon, Shadow Orange, Shadow Red and Mixed Berries. Source: Polymaker.

PolyTerra Dual PLA is a filament available in numerous color options, each being a unique combination of two colors creating a color changing effect. The available colors are:

  • Shadow Black (white - black).
  • Shadow Red (black - red).
  • Shadow Orange (black - orange).
  • Foggy Orange (gray - orange).
  • Foggy Purple (gray - purple).
  • Glacier (ice - blue).
  • Flamingo (pink - red).
  • Chameleon (teal - yellow).
  • Sunrise (red - yellow).
  • Camouflage (dark green - brown).
  • Mixed Berries (red - dark blue).

The Polyterrra Dual PLA colors

Image 2: The Polyterrra Dual PLA colors. Source: Polymaker.

PolyTerra Dual PLA prints just like standard PLA, with an extrusion temperature of 190-230 ºC, a bed temperature of 25-60 ºC, and a recommended printing speed of 30-70 mm/s. More instructions and information about the PolyTerra Dual PLA filament can be found in the Downloads section.

Polymaker spool adapter

In the download section you will find the STL and STEP files to 3D print your own Polymaker spool adapter. This durable spool adapter helps reduce friction by creating a structured running surface, and also avoids the dust build-up associated with similar adapter solutions. The spool adapter was created with the Polymaker cardboard spools in mind to compensate for any spool deformation that could influence spool stability.

Video 1: The Polymaker spool adapter. Source: Polymaker.

This Polymaker spool adapter is compatible with all multi-material stations, such as Bambu Lab's AMS or Ultimaker's Material Station. Printing the adapter requires about 40 minutes and 30 g of filament. Recommended materials are PLA, PolyLite PETG, PolyLite ASA or PolyMax PLA for durability and longevity. To extend the life of the spool adapter, Polymaker suggests first removing the locating pin before removing the edge clips to reduce stress on the adapter when changing spools.

Elongation at break (%) 35
Tensile strength (MPa) 20
Tensile modulus (MPa) 1882
Flexural strength (MPa) 40
Flexural modulus (MPa) 2695
Softening temperature (ºC) 63
Biodegradable Biodegradable

PolyTerra Dual PLA should be properly stored to avoid the filament from getting humid. An ideal solution is to store it in a vacuum sealed packaging (with the Slice Engineering filament drying capsule for even better results), an intelligent filament container or in the PolyBox storage box that keeps the filament dry during printing. If the filament absorbs too much moisture, it should be dried at 55 ºC for 6 hours.

The recommended printing settings for the PolyTerra Dual PLA filament are a 190-230 ºC extrusion temperature at a speed of 30-70 mm/s, on a bed heated to 25-60 ºC, with the layer fan turned on. More printing instructions can be found in the product's technical datasheet in the Downloads section.

Complex structures can be 3D printed with the PolyTerra Dual PLA and a support filament, for example the PolySupport filament. A 3D printer with at least two extruders is required to print with supports.

General Information
Manufacturer Polymaker
Material PolyTerra Dual PLA
Format 1 kg spool
Density (ISO1183) 1.31 g/cm³
Filament diameter 1.75 mm
Diameter tolerance ±0.05 mm
Filament length ±317.4 m
Color Shadow Black (white - black), Shadow Red (black - red), Shadow Orange (black - orange), Foggy Orange (gray - orange), Foggy Purple (gray - purple), Glacier (ice - blue), Flamingo (pink - red), Chameleon (teal - yellow), Sunrise (red - yellow), Camouflage (dark green - brown), Mixed Berries (red - dark blue).
RAL/Pantone -
Printing Properties
Printing temperature 190-230 °C
Bed temperature 25-60 °C
Chamber temperature
Layer fan
Recommended print speed 30-70 mm/s
Drying conditions 6 h @ 55 °C
Mechanical properties
Izod impact resistance -
Charpy impact resistance  (ISO 179) XY: 5.7 ± 0.4 kJ/m²
Z: -
Elongation at break (ISO 527) XY: 34.5 ± 8.1%
Z: 2.51 ± 0.83%
Tensile strength (ISO 527) XY: 20.9 ± 2.0 MPa
Z: 18.0 ± 0.3 MPa
Tensile modulus (ISO 527) XY: 1882 ± 141 MPa
Z: 20.9 ± 2.0 MPa
Bending strength (ISO 178) XY: 39.6 ± 1.1 MPa
Z: -
Bending modulus (ISO 178) XY: 2695 ± 541 MPa
Z: -
Surface hardness -
Thermal properties
Softening temperature (ISO 306) 62.7 °C
Melting temperature (DSC, 10°C/min) 162.6 °C
Specific properties
Transparency -
FDA certification -
Additional information
HS Code 3916.9
Spool diameter (outer) 200 mm
Spool diameter (inner hole) 55 mm
Reel Width 65 mm

* The typical values detailed in this table should be considered as a reference. Actual values may vary depending on the 3D printer model used, part design, and printing conditions. We recommend confirming the results and final properties with your own tests. For more information, refer to the product's technical data sheet.