The Flexible Resin is used to print flexible parts, which need to be folded or compressed for the correct functioning of the model. It presents a hardness Shore 80A, which is the one that gives the name and that attributes a soft and pleasant touch to the pieces.
The hardness and finish of Flexible 80A resin is very similar to the soles of shoes or tyres, as it simulates the flexibility of rubber or thermoplastic polyurethane.
Thanks to its low modulus of traction and high elongation, this material is suitable for printing:
Flexible 80A resin is a reformulation of the previous Flexible FormLabs resin, which has been improved in several aspects and has the following advantages:
Flexible 80A resin is the most rigid soft-touch material in Formlabs' Flexible and Elastic family of resins. By combining flexibility and resilience, Flexible 80A Resin can withstand bending and compressive stresses, even over repeated cycles.
Properties | Flexible 80A resin post-curated | Elastic 50A resin Post-curated |
---|---|---|
Elongation at break | 120 % | 160 % |
Tensile strength | 8.9 MPa | 3.2 MPa |
Hardness | 80A | 50A |
If a less rigid flexible material is required, Elastic Resin 50A should be chosen.
This resin is compatible with:
Compatible printers | Compatible resin tanks |
---|---|
Form 2, Form 3, Form 3B | Form 2 LT, Form 3 |
It should be noted that parts printed in 3D with this material require curing to achieve their optimum mechanical properties.
FormLabs' flexible 80A resin allows the user to manufacture functional prototype or end parts that require a certain level of flexibility and high mechanical properties.
Elongation at break (%) | 160 |
Tensile strength (MPa) | 8.9 |
Surface hardness | 4 |
Elasticity | Elasticity |
Flexibility | Flexibility |
Hide color variations | (Hide color variations) |
Below, a series of usage tips are cited that must be taken into account at all times with the use of FormLabs resins:
Changing the resin cartridge of the FormLabs printers is very simple, just close the top cap of the ventilation duct (vent) and remove the cartridge by holding it by the handle it has. Then the other is inserted and the vent plug is opened in case an impression is to be started. To avoid drips through the 3D printer, this process must always be carried out with the resin tank mounted.
After finishing each impression the vent plug must be closed so that the resin maintains its properties. In addition, if you don't use the printer for some time, you should keep the cartridge in its original box to keep the properties of the resin intact.
Each type of resin must have its resin tank, which must be changed after using 2L of resin. FormLabs has developed a more powerful tank, the Resin Tank LT, which has a life up to 20 times longer than the standard tank.
To protect and store the excess resin in the tank after each printing, FormLabs supplies a lid that ensures a perfect closure. Once the tank is closed, it is recommended to store it (with resin and lid) in the original box so that the resin doesn't lose its properties when exposed to UV rays for a long time. Another point to keep in mind is that the tanks can't be cleaned with any cleaning product or similar (for example, isopopyl alcohol), since they lose certain qualities that can cause continuous failed impressions.
When an error occurs in printing may be because solid parts of a previous printing have fallen to the resin tank. In this case, a spatula at 45° must be passed through the printing tank, gathering all the solid parts in a corner and removing them. To ensure that the tank resin doesn't contain any solid parts, the resin should be cast with a 190 μm paper filter. Once cast, it is put back into the tank and it is ready to be used again.
Isopropyl alcohol is the key to the washing and post-processing of parts and you should know when it is time to change it. In the Finish Kit the moment to change it's when the IPA (Isopropyl Alcohol) is so saturated with resin particles, that after washing the pieces are still sticky. At that point you must remove all the liquid, clean the container well and throw new IPA, but never fill in on the previous one.
In the Form Wash, the wash center itself indicates through its screen when it is time to change the isopropyl alcohol.
If you wish you can contract our SLA 3D printing training courses (online or in person) by contacting us through the contact form. The training is oriented to obtain a wide knowledge and know how to use the 3D SLA FormLabs printers from the beginning and t.hus avoid major errors.
General information | |
---|---|
Manufacturer | FormLabs (Massachusetts, USA) |
Technology | SLA / LFS |
Material | Photopolymer |
Wavelength | UV 405 nm |
Format | 1 liter |
Compatible 3D printers | Form 2, Form 3, Form 3L |
Print settings | |
Layer height | 100-50 microns |
Exposure Time | It is not necessary to configure the printing parameters in the Formlabs printers. The chip incorporated in the resin cartridges detects the type of material by configuring the printing automatically. |
Off time | |
Lifting height | |
Bottom exposure | |
Bottom layers | |
Curing and washing properties | |
Washing time (FormWash) | 10 + 10 min |
Curing time (FormCure) | 10 min / 60ºC |
Mechanical properties (without curing / with curing) | |
Izod impact strength (ASTM D256-10) | - |
Charpy impact strength | - |
Elongation at break (ASTM D 638-10) | 100 % - 120 % / 100 % - 120 % |
Tensile strength (ASTM D 638-10) | 3.7 - 8.9 MPa / 3.7 - 8.9 MPa |
Tensile Modulus (ASTM D638-10) | - |
Flexural strength (ASTM D 790-15) | - |
Flexural modulus (ASTM C790-10) | - |
Surface hardness (ASTM 2240) | Shore 70 - 80 A / 70 - 80 A |
Thermal properties (without curing / with curing) | |
Softening temperature (ASTM D 648-16 / @ 0.45 MPa) | - |
Additional Information | |
Lifetime (since manufacturing) | 24 months |
HS Code | 2916.1 |
* The typical values detailed in this table should be considered as a reference. Actual values may vary depending on the 3D printer model used, part design and printing conditions. We recommend confirming the results and final properties with own tests. For more information you should consult the technical data sheet of the product.
295,00 €
125,00 €
111,15 € -5% 117,00 €
199,00 €
92,15 € -5% 97,00 €
44,95 €
199,00 €
43,95 €
100,00 €
58,95 €
399,00 € -5% 420,00 €
299,00 €
128,00 €
249,00 €
135,00 €
124,45 € -5% 131,00 €
337,25 € -5% 355,00 €
169,00 €
399,00 € -5% 420,00 €
156,20 €
268,04 € -5% 282,15 €
240,35 € -5% 253,00 €
214,05 €
418,00 € -5% 440,00 €
96,00 €
280,25 € -5% 295,00 €
123,14 €
110,00 €