BASF Ultracur3D® EPD 2006

BASF-2006-BLACK
355.00 € 355.00 €
Tax excl.
Colour
Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 4 - 6 days Available for shipment within 4 - 6 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Thursday 12 December - Monday 16 December
Available

BASF is a renowned manufacturer specialising in the development of chemical products. Its product range includes products for the production of 3D printing materials for FDM, resin and SLS.

Ultracur3D® EPD 2006 resin is a resin for daylight resin technology, i.e. for use in visible light printers such as Photocentric printers. Daylight is a lower energy, longer wavelength light that ensures more reliable polymerisation than UV light.

Photocentric has teamed up with BASF to create a range of Engineering Plastic Daylight (EPD) materials for a wide range of applications.

Pieza impresa con Ultracur 2006
Image 1. Part made with Ultracur3D® EPD 2006 resin. Source: BASF

Ultracur3D® EPD 2006 resin is a daylight reactive urethane photopolymer for daylight resin technology that features high stiffness and temperature resistance. This resin, available in black, is ideal for the manufacture of large objects, highly detailed and textured parts, custom tooling, etc.

Curing, washing, and sintering properties
Washing time -
Curing time -
Curing temperature - ºC

General information
Manufacturer BASF
Material Photopolymer
Format 5 kg
Technology EPD
Wavelength - nm
Viscosity @ 30 ºC: 310 mPa·s / @ 50 ºC: 88 mPa·s
Density (solid) (ASTM D792) 1.2 g/cm³

Printing properties
Layer height - µm
Layer exposure time -
Layer off time -
Lifting height - mm
Bottom layer exposure -
Bottom layer count -

Mechanical properties
Izod impact strength - KJ/m²
Charpy impact strength (ISO 179-1) 0.7 KJ/m²
Elongation at break (ASTM D412C) 10.3 %
Tensile strength (ASTM D412C) 50 MPa
Tensile modulus 2370 MPa
Flexural strength (ASTM D790) 90 MPa
Flexural modulus (ASTM D790) 2210 MPa
Surface hardness (ASTM D2240) Shore 80 D

Thermal properties
Softening temperature 81 ºC
Flammability classification (UL94) HB @ 1.5 mm
Heat deflexion temperature (ASTM D648) @ 0.45 MPa: 81 ºC / @ 1.82 MPa: 61 ºC

Specific properties
Maximum water absorption (ASTM D570) 24 h: 0.61 %

Other
HS Code 2916.1
Lifetime (since manufacturing) 12 M

Before starting a print, the resin should be shaken well and, if possible, vacuumed to remove any bubbles that may have formed.

Once printed, the pieces should be cleaned with isopropyl alcohol. To do this it is advisable to immerse the pieces in a container with isopropyl alcohol and place this container in an ultrasonic cleaner for 4 minutes. It is recommended not to immerse the piece for long periods of time to avoid deformation and softening.

After cleaning, the pieces should be dried for 30 minutes at 40 ºC. Once dry, parts printed with BASF Ultracur3D resins should be cured at room temperature to obtain optimum properties. Curing conditions will depend on the characteristics of the printer used and the curing equipment.