BASF Ultracur3D RG35

Ref.: BASF-RG35-NAT

106.00 €

Tax excl.

Format

Colour

Type of resin

Quantity

In stock 33 units available for immediate shipping.
units available for shipping in 4 - 6 days Available for shipment within 4 - 6 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Friday 27 December

Available

Returns

Ask about this product

Ultracur RG35, developed by BASF (Forward AM) is a medium-viscosity, highly reactive urethane photopolymer tailored for rigid applications. Known for its exceptional stability and stiffness, RG35 provides high accuracy and low shrinkage, making it an ideal choice for producing high-performance functional parts. Available in both natural (RG35) and black (RG35B) formulations, this resin combines good temperature resistance with low water uptake, ensuring reliability in various conditions.

The impressive material properties of Ultracur RG35 further enhance its appeal for demanding applications. With a Young’s modulus of 2600 MPa and a tensile strength of 80 MPa, RG35 exhibits remarkable rigidity and durability. It also features a heat deflection temperature of 83°C, allowing it to maintain performance under elevated thermal conditions. The Shore hardness of 85 D adds to its robustness, making it suitable for applications such as automotive housings, jigs and fixtures, molds and inserts, and electrical castings. Additionally, RG35 is easy to polish, facilitating post-processing for a high-quality finish.

A part 3D printed with the RG35 resin in natural color

Image 1: A part 3D printed with the RG35 resin in natural color. Source: BASF (Forward AM).

Ultracur RG35 is compatible with various resin 3D printing technologies, including SLA, LCD, and DLP, ensuring smooth integration into existing production workflows. This versatility enables users to achieve high-quality results across a broad spectrum of projects, from rapid prototyping to the development of intricate, high-performance components. Manufacturers benefit from the streamlined processes facilitated by RG35, promoting efficiency and consistency in their production operations.

A part 3D printed with the RG35 resin in black color

Image 2: A part 3D printed with the RG35 resin in black color. Source: BASF (Forward AM).

For users seeking comprehensive information about Ultracur RG35's capabilities, a detailed technical datasheets that cover essential properties such as long-term UV resistance, industrial chemical resistance, biocompatibility, and sterilization is available in the Attachments section. The accompanying user manual serves as a practical guide for storage, printer settings, and post-processing techniques, ensuring optimal use of this versatile material. Additionally, the BASF (Forward AM) Settings Navigator assists users in identifying suitable printer configurations for specific equipment, guaranteeing optimal print outcomes and maximizing the effectiveness of RG35 resin across various applications.

Curing, washing, and sintering properties
Washing time	-
Curing time	-
Curing temperature	- ºC

General information
Manufacturer	BASF
Material	Urethane-acrylate oligomers
Format	1 kg / 5 kg
Technology	SLA / LED-LCD / DLP
Wavelength	385 / 405 nm
Viscosity	(@ 25 ºC) RG35: 900 mPas; RG35B: 950 mPas / (@ 30 ºC) RG35: 600 mPas; RG35B: 630 mPas
Density (solid)	(ASTM D792) 1.2 g/cm³
Density (liquid)	(ASTM D4052-18a) RG35: 1.12 g/cm³ / RG35B: 1.11 g/cm³

Electrical properties
Dielectric strength	(DIN EN 50243-1) RG35: 37 kV/mm

Printing properties
Layer height	- µm
Layer exposure time	-
Layer off time	-
Lifting height	- mm
Bottom layer exposure	-
Bottom layer count	-

Mechanical properties
Izod impact strength	- KJ/m²
Charpy impact strength	(ISO 179-1) (RG35) 0.6 kJ/m² / (RG35B) 1.3 KJ/m²
Elongation at break	(ASTM D412C) (RG35) 6 % / (RG35B) 10 %
Tensile strength	(ASTM D412C) (RG35) 80 MPa / (RG35B) 62 MPa
Tensile modulus	(ASTM D638) (RG35) 2600 MPa / (RG35B) 2600 MPa
Flexural strength	(ASTM D790) (RG35) 110 MPa / (RG35B) 108 MPa
Flexural modulus	(ASTM D790) (RG35) 2400 MPa / (RG35B) 2300 MPa
Surface hardness	(ASTM D2240) (RG35) Shore 85 D / (RG35B) Shore 83 D

Thermal properties
Softening temperature	(ASTM D648) (RG35) 83 ºC / (RG35B) 87 ºC
Flammability classification	(UL94, 1.5 mm) HB

Specific properties
Maximum water absorption	(ASTM D570, 24 h) RG35: 0.33 %, RG35B: 0.42 % / (ASTM D570) RG35, >4000 h: 2.4 %; RG35B, >2800 h: 2 %

Other
HS Code	2916.1
Lifetime (since manufacturing)	12 M

The Ultracur3D resins from BASF exhibit high light sensitivity, so they should always be stored in their closed container and away from light.

Before starting a print, it is necessary to shake the resin well and, if possible, place it under vacuum to eliminate any bubbles that may have formed.

Once printed, the cleaning of the parts must be done with isopropyl alcohol. It is recommended to submerge the parts in a container with isopropyl alcohol and place this container inside an ultrasonic cleaner for 4 minutes. It is advisable not to immerse the part for extended periods to avoid deformation and softening.

After cleaning, the parts should dry for 30 minutes at 40 ºC. Once dry, the parts printed with BASF Ultracur3D resins should cure at room temperature to achieve optimal properties. The curing conditions will depend on the characteristics of the printer used and the curing equipment.