Fiberon PPS-GF20

Ref.: FIBERON-PPS-GF20-175-500G

57.84 €

Tax excl.

Diameter

Format

Volume discounts

Quantity	Discount	Price
5	5% 5%	54.95 € 54.95 €
10	8% 8%	53.21 € 53.21 €

Quantity

In stock 10 units available for immediate shipping.
units available for shipping in 15 - 21 days Available for shipment within 15 - 21 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Wednesday 10 September

Available

Returns

Ask about this product

Fiberon PPS-GF20 from Polymaker represents the standard in high-performance filaments for 3D printing in industrial, automotive, and electronics applications demanding maximum strength and reliability. This filament reinforced with 20% glass fiber combines outstanding stiffness and mechanical strength with dimensional stability, enabling parts that retain shape and functionality even at temperatures up to 236 °C.

Advanced Technical Properties for Demanding Environments

The electrical insulation capability of Fiberon PPS-GF20 is unmatched, with a dielectric strength of 6.05 kV/mm and a low dielectric constant of 2.71 @ 1 MHz, making it ideal for electrical housings, advanced ADAS sensor enclosures, and structural components in 5G base stations. Its UL94 V0 certification at 1.5 mm ensures certified flame resistance, while its resistance to acids, bases, oils, and solvents guarantees reliable performance even in the harshest environments.

Video 1: Presentation of Fiberon PPS-GF20 high-performance filament for electronics and automotive applications.

Precision and Reliability in Every Print

This industrial filament is optimized for precise and fast printing, supporting speeds up to 250 mm/s with minimal warping and maximum Z-axis stability. Its neutral gray color reduces heat absorption and simplifies post-processing, while vacuum packaging and AMS system compatibility ensure tangle- and moisture-free filament, providing consistent results in any environmental condition.

Parts printed with advanced reinforced PPS-GF20 filament

Photo 1: Parts printed with advanced reinforced PPS-GF20 filament. Source: Fiberon

Fiberon Material Comparison

Material	Nozzle Temp	Bed Temp	Print Speed	Chamber Temp	Flame Rating	HDT	Young's Modulus (X-Y)	Layer Adhesion (Z)	Charpy Impact (X-Y)	Fiber Reinforcement	Recommended Support	Drying
Fiberon PPS-GF20	310–350 °C	80–90 °C	Up to 250 mm/s	Ambient	V0 (1.5 mm)	236.3 °C (0.45 MPa)	4552.0 ± 54.6 MPa	22.9 ± 0.8 MPa	27.3 ± 1.1 kJ/m²	20% glass	PolySupport for PA12	100 °C · 10 h
Fiberon PPS-CF10	310–350 °C	80–90 °C	Up to 300 mm/s	Ambient	V0 (1.5 mm)	252.5 °C (0.45 MPa)	5446.7 ± 149.0 MPa	32.0 ± 5.1 MPa	11.4 ± 0.7 kJ/m²	10% carbon	PolySupport for PA12	100 °C · 10 h
Fiberon PA612-ESD	280–300 °C	40–50 °C	Up to 300 mm/s	Ambient	HB	157.0 °C (0.45 MPa)	4293.7 ± 116.4 MPa	21.5 ± 2.7 MPa	24.1 ± 2.4 kJ/m²	—	PolySupport for PA12	100 °C · 10 h
Fiberon PETG-ESD	250–290 °C	70–80 °C	Up to 500 mm/s	Ambient	HB	76.0 °C (0.45 MPa)	1983.0 ± 74.9 MPa	20.7 ± 0.6 MPa	29.3 ± 2.2 kJ/m²	—	N/A	65 °C · 3 h
Fiberon PET-CF17	270–300 °C	70–80 °C	Up to 300 mm/s	Ambient	HB	147.5 °C (0.45 MPa)	5481.0 ± 223.7 MPa	27.9 ± 1.3 MPa	25.1 ± 2.8 kJ/m²	17% carbon	PolySupport for PA12	100 °C · 10 h
Fiberon PA6-GF25	280–300 °C	40–50 °C	Up to 300 mm/s	Ambient	HB	191 °C (0.45 MPa)	5356.9 ± 211.0 MPa	60.7 ± 1.1 MPa	27.4 ± 0.5 kJ/m²	25% glass	PolyDissolve S1	100 °C · 10 h
Fiberon PA12-CF10	260–300 °C	40–50 °C	Up to 300 mm/s	Ambient	HB	131 °C (0.45 MPa)	3311.2 ± 134.9 MPa	52.2 ± 0.8 MPa	33.7 ± 1.4 kJ/m²	10% carbon	PolySupport or PolyDissolve	100 °C · 10 h

Conclusion

Fiberon PPS-GF20 combines superior mechanical performance, thermal resistance, electrical insulation, and flame resistance, providing maximum confidence for critical components and mission-essential parts. Every print demonstrates reliability, durability, and industrial precision, making this filament the ultimate choice for engineers and professionals seeking excellence in additive manufacturing projects.

Parts printed with advanced reinforced PPS-GF20 filament. Source: Fiberon

Photo 2: Parts printed with advanced reinforced PPS-GF20 filament. Source: Fiberon

General information
Material	PPS GF
Format	0.5 Kg \| 3 Kg
Density	(ISO 1183) 1.36 g/cm³
Filament diameter	1.75 mm
Filament length	[0.5 Kg] 152.8 m \| [3 Kg] 305.7 m

Printing properties
Printing temperature	310-350 ºC
Print bed temperature	80-90 ºC
Cooling fan	✗
Recommended printing speed	< 250 mm/s

Mechanical properties
Charpy impact strength	(ISO 179) 7.3 KJ/m²
Elongation at break	(ISO 527) 2.0 %
Tensile strength	(ISO 527) 64.1 MPa
Tensile modulus	(ISO 527) 4552.0 MPa
Flexural strength	(ISO 178) 7.3 MPa
Flexural modulus	(ISO 178) 4110.7 MPa

Thermal properties
Melting temperature	DSC, 10ºC/min 279.6 ºC
Softening temperature	(ISO 306) 272.5 ºC

Specific properties
Chemical resistance	✓

Other
HS Code	3916.9

The Fiberon PPS-GF20 requires a full-metal hotend capable of reaching temperatures between 310 °C and 350 °C, and a heated bed between 80 °C and 90 °C. It is recommended to keep the layer fan off during printing to avoid warping and ensure good layer adhesion. Print speed can be up to 250 mm/s, depending on the part complexity and your printer’s capabilities.

For printers with a Direct Drive system, the recommended retraction distance is 1 to 3 mm with a retraction speed of 20 to 40 mm/s. These parameters help prevent stringing and oozing without affecting print quality.

The filament must be kept dry; if it has absorbed moisture, it is recommended to dry it at 100 °C for 10 hours before printing. Depending on ambient humidity, a filament dryer may be required. After printing, a post-annealing at 130 °C for 10 hours can improve mechanical properties and thermal stability.

Among the equipment requirements, it is important to have a full-metal hotend capable of reaching the proper temperature and a hardened nozzle to resist wear from fiber-reinforced filament. Keeping the filament dry when not in use and periodically checking nozzle cleanliness will ensure consistent, high-quality prints.

Finally, it is recommended to print in a stable area, free of drafts, check bed leveling and adhesion before starting large parts, and adjust retraction if stringing or oozing occurs during printing. These measures will ensure optimal results and longer-lasting prints with Fiberon PPS-GF20.

For more information, refer to the documentation available in the Attachments tab.