Fiberon PPS-CF10

Name: Fiberon PPS-CF10
Brand: Fiberon
SKU: FIBERON-PPSCF10
Price: 66.11 EUR
Availability: InStock

Ref.: FIBERON-PPSCF10-BLACK-175-500

66.11 €

Tax excl.

Diameter: 1.75 mm

Format: Spool 500 g

Colour: Black

Ver todas las opciones

Volume discounts

Buy 5 units

Save 5%

314.02 € Tax excl. Unit price 62.80 € 66.11 €

Buy 10 units

Save 8%

608.21 € Tax excl. Unit price 60.82 € 66.11 €

Quantity

In stock 5 units available for immediate shipping.
units available for shipping in 15 - 21 days Available for shipment within 15 - 21 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Friday 15 May

Returns

Ask about this product

The PPS-CF10 filament, part of the Fiberon line of ultra-performance polymers, is a high-strength material infused with 10% carbon fibers, which enhances the strength of the printed parts and imparts metal-like stiffness and superior dimensional stability. PPS-CF10 enables the production of precise and stable parts without deformation issues and with elevated moisture insensitivity, even in demanding environments. With a heat deflection temperature exceeding 250 ºC, the PPS-CF10 filament is suitable for high-temperature applications. Its natural flame-retardant properties (V0 rating per UL 94) and broad chemical resistance to acids, alkalines, fuels, and solvents position it as an excellent choice for applications in aerospace, electronics, and molding, where stringent durability and safety standards are required.

Part 3D printed with the PPS-CF10 filament

Image 1: Part 3D printed with the PPS-CF10 filament. Source: Fiberon.

The PPS-CF10 filament balances advanced properties with user-friendly printing characteristics, including low creep and compatibility with high-speed printing up to 300 mm/s. The filament does not require an actively heated chamber, enabling reliable results at room temperature. Optimal for 3D printers such as the Bambu Lab X1E, PPS-CF10 also supports multimaterial systems, like Bambu Lab's AMS module. To ensure nozzle longevity and consistent print quality, an abrasion-resistant nozzle is recommended, such as a hardened steel or ruby tip nozzle.

High quality components 3D printed with the PPS-CF10 filament

Image 2: High quality components 3D printed with the PPS-CF10 filament. Source: Fiberon.

Parts 3D printed with the PPS-CF10 filament present great properties and performance. However, to boost the thermal and mechanical performance, PPS-CF10 parts can be annealed at 125 ºC for 16 hours. In fact, the mechanical properties presented in the Specifications tab come from tests conducted on parts that underwent this annealing process. To prevent deformation, 24 hours should pass after printing to relieve internal stresses. Adding support structures (with PolySupport for PA12) for parts with overhangs, thin walls, or bridging structures will also help. For optimal results, parts should be placed in the oven in the same orientation as during printing, ideally on the build plate itself, ensuring precise dimensional accuracy and long-term stability.

General information
Material	PPS
Format	500 g / 3 kg
Density	(ISO 1183) 1.29 g/cm³
Filament diameter	1.75
Filament length	(Ø 1.75 mm-0.5 Kg) ±161.1 m / (Ø 1.75 mm-3 Kg) ±966.9 m

Printing properties
Printing temperature	310 - 350 ºC
Print bed temperature	80 - 90 ºC
Chamber temperature	20 - 25 ºC
Cooling fan	✗
Recommended printing speed	Max. 300 mm/s
Recommended nozzle	Hardened Steel

Mechanical properties
Charpy impact strength	(ISO 179) 5.3 ± 0.2 KJ/m²
Elongation at break	(ISO 527) XY: 1.4 ± 0.1 % / Z: 1.6 ± 0.2 %
Tensile strength	(ISO 527) XY: 59.4 ± 1.3 % / Z: 32.0 ± 5.1 MPa
Tensile modulus	(ISO 527) XY: 5446.7 ± 149.0 MPa / Z: 2790.0 ± 152.6 MPa
Flexural strength	(ISO 306) XY: 94.3 ± 1.9 MPa / Z: 30.0 ± 5.2 MPa
Flexural modulus	(ISO 178) XY: 4646.9 ± 136.9 MPa / 2619.3 ± 155.3 MPa
Surface hardness	-

Electrical properties
Surface electrical resistivity	(ANSI ESD S11.11) OL, >10¹² Ohm

Thermal properties
Melting temperature	(DSC) 279.7 ºC
Softening temperature	(ISO 306) 267.5 ºC
Heat deflexion temperature	(ISO 75) @ 0.45 MPa: 252.5 ºC / @ 1.8 MPa: 133 ºC

Specific properties
Transparency	✗
Flammability classification	UL 94 V0 @ 1.5 mm
Chemical resistance	✓

Other
HS Code	3916.9
Spool diameter (outer)	(0.5 kg) 200±1 mm / (3 kg) 250±1 mm
Spool diameter (inner hole)	(0.5 kg) 55±1 mm / (3 kg) 55±1 mm
Spool width	(0.5 kg) 65.6±2 mm / (3 kg) 117.2±2 mm

To achieve optimal print quality with the Fiberon PPS-CF10 filament, it is recommended to set the extrusion temperature between 310-350 ºC, and the print bed should be maintained between 80-90 ºC. A room temperature for the build chamber is sufficient, and it is best to keep the cooling fan turned off. Fiberon PPS-CF10 supports high-speed printing with speeds of up to 300 mm/s, making it suitable for projects where efficiency is crucial.

Proper filament storage is essential for maintaining the quality of Fiberon PPS-CF10. To prevent compromised print quality due to moisture, it should be stored in a sealed container with desiccant. If the filament absorbs excess moisture, drying it at 100 ºC for 10 hours in a filament dryer is recommended (or PolyDryer at level 3 for 18 hours) to restore its optimal printing properties.

Since the Fiberon PPS-CF10 filament contains abrasive carbon fibers, it is highly recommended to use an abrasion resistant nozzle (hardnened steel, vanadium, ruby tip, etc) to avoid its excessive wear and, in consequence, inferior part quality.