Panchroma PLA Dual Silk

PCHR-PLA-2SILK-AUBER-175-1000
22.31 € 22.31 €
Tax excl.
Diameter
Format
Colour
Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 15 - 21 days Available for shipment within 15 - 21 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Tuesday 17 December - Monday 6 January
Available

The PLA Dual Silk filament from the Panchroma series introduces a unique feature with its captivating color change effect, thanks to the blend of two carefully chosen, smoothly transitioning colors. This combination creates a striking, glossy finish that enhances the visual appeal of any project. The filament produces a smooth, high-quality surface with minimal layer lines, making it ideal for decorative objects or prototypes. With its range of vibrant color options, PLA Dual Silk ensures an eye-catching and refined aesthetic while offering reliable and easy printing performance.

The color range of the PLA Dual Silk filament

Image 1: The color range of the PLA Dual Silk filament. Source: Panchroma.

The Panchroma range of 3D printing filaments offers a wide selection of colors, surface textures, and filament effects, each carefully crafted to deliver optimal printability and exceptional visual appeal. The formulation of PLA Dual Silk ensures superior results across all projects, making it ideal for high-precision applications where both aesthetics and functionality are crucial. This filament is perfect for designers looking to produce prototypes or end products with a premium finish.

Video 1: The captivating color change effect of the PLA Dual Silk filament. Source: Panchroma.

Printing with PLA Dual Silk is simple and efficient, with a recommended extrusion temperature between 190-230 ºC and a bed temperature of 25-60 ºC. For optimal results it is recommended to use printing speeds in the range of 40-60 mm/s. Its innovative spool design features an anti-slip edge, providing smooth operation, especially when used with automatic material handling systems like the Bambu Lab AMS, enhancing its adaptability for a range of modern 3D printing setups.

General information
Material PLA
Format 1 kg
Density 1.20 g/cm³
Filament diameter 1.75 mm
Filament tolerance ±0.03 mm
Filament length ±346.5 m

Printing properties
Printing temperature 190 - 230 ºC
Print bed temperature 25 - 60 ºC
Chamber temperature ✗
Cooling fan ✓
Recommended printing speed 40 - 60 mm/s

Mechanical properties
Charpy impact strength (ISO 179) 2.9 ± 0.1 KJ/m²
Elongation at break - %
Tensile strength (ISO 527) XY: 57.9 ± 1.5 MPa / Z: 20.2 ± 5.7 MPa
Tensile modulus (ISO 527) XY: 3364 ± 89 MPa / Z: - MPa
Flexural strength - MPa
Flexural modulus - MPa
Surface hardness -

Thermal properties
Softening temperature (ISO 306) 67 ºC

Other
HS Code 3916.9
Spool diameter (outer) 200 mm
Spool diameter (inner hole) 55 mm
Spool width 65.6 mm

Other information

PLA Dual Silk HEX Codes

Aubergine - Silk Lime #91C500 + Silk Magenta #990050

Beluga - Silk Sliver #818C9F + Silk Blue #0151BA

Chameleon - Silk Yellow #E9C200 + Silk Blue #0151BA

Caribbean - Silk Blue #0151BA + Silk Green #008C63

Crown - Silk Gold #B56600 + Silk Sliver #818C9F

Sovereign - Silk Gold #B56600 + Silk Purple #150074

Banquet - Silk Gold #B56600 + Silk Magenta #990050

Jadeite - Silk Green #008C63 + Silk Chrome #384657

Sunset - Silk Gold #B56600 + Silk Red #CB0100

Like any 3D printing filament, the Panchroma PLA filaments should be stored properly in order to avoid their deterioration and, in consequence, extrusion problems and inferior print quality. The spool can be stored in an airtight plastic bag, in a resealable bag with a desiccant capsule, or in a smart filament container. If the filament has absorbed too much moisture, it must be dried before printing in a filament dryer for 6 hours at 55 ºC or in the PolyDryer solution. The recommended settings are setting 1 for Panchroma PLA Silk and others, and settings 1-3 for PLA Matte and Satin.

The Panchroma PLA filaments should be extruded at a temperature of 190-230 ºC on a bed heated to 25-60 ºC. It is recommended to use the cooling fan at 100% but a printer with a heated chamber is not needed. As far as the printing speed, it is recommended to use max. 200 mm/s for the PLA Silk and other Panchroma PLA varieties, and  max. 300 mm/s for the PLA Satin and Matte PLA.

Complex parts can be 3D printed with the Panchroma PLA filaments with the help of support filaments such as the PolySupport filament or the PolyDissolve S1 filament.

Panchroma PLA Glow and Panchroma PLA Luminous are glow-in-the-dark materials enriched with an abrasive additive, making a hardened nozzle essential for printing. These filaments should not be used in AMS systems with plastic gears or tubes due to their abrasive nature.

Featured properties

Printing temperature
190 - 230 ºC
Filament diameter
1.75 mm
High speed compatible
Yes
Density
1.20 g/cm³