Panchroma PLA Dual Matte

Ref.: PCHR-PLA-2MAT-CAMOUF-175-1000

18.17 €

Tax excl.

Diameter

Format

Colour

Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 15 - 21 days Available for shipment within 15 - 21 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Thursday 23 January - Friday 31 January

Available

Returns

Ask about this product

The PLA Dual Matte filament from the Panchroma range brings a bold and innovative touch to 3D printing, combining ease of use with visually striking results. This filament merges two carefully selected colors in a single spool, creating a mesmerizing color-changing effect through smooth transitions. With its refined matte surface finish and barely visible layer lines, PLA Dual Matte is ideal for producing prototypes and decorative objects with a modern, professional aesthetic. Its vibrant dual-tone combinations make it perfect for projects that require both functionality and artistic impact.

The colors available in the PLA Dual Matte range

Video 1: The colors available in the PLA Dual Matte range. Source: Panchroma.

The Panchroma range of 3D printing filaments stands out with its broad selection of color options, surface textures, and creative filament effects. Each formulation is optimized to ensure smooth printability and top-tier visual results. PLA Dual Matte is particularly suited for projects where precision and eye-catching aesthetics are equally important, making it an excellent choice for designers looking to elevate their creations with unique, high-quality finishes.

Cubes 3D printed with the PLA Dual Matte filament

Image 1: Cubes 3D printed with the PLA Dual Matte filament. Source: Panchroma.

Printing with PLA Dual Matte is simple and effective, with recommended extrusion temperatures of 190-230 ºC and a bed temperature of 25-60 ºC. Capable of reaching speeds of up to 300 mm/s, it offers versatility for both high-speed and detailed prints. Its spool design features an anti-slip edge, ensuring seamless operation with automatic material handling systems like the Bambu Lab AMS, making it an adaptable and reliable option for modern 3D printing needs.

General information
Material	PLA
Format	1 kg
Density	1.37 g/cm³
Filament diameter	1.75 mm
Filament tolerance	±0.03 mm
Filament length	±303.5 m

Printing properties
Printing temperature	190 - 230 ºC
Print bed temperature	25 - 60 ºC
Chamber temperature	✗
Cooling fan	✓
Recommended printing speed	Max. 300 mm/s

Mechanical properties
Charpy impact strength	(ISO 179) 10.0 ± 0.8 KJ/m²
Elongation at break	- %
Tensile strength	(ISO 527) XY: 28.1 ± 0.5 MPa / Z: 15.4 ± 0.2 MPa
Tensile modulus	(ISO 527) XY: 2049 ± 64 MPa / Z: - MPa
Flexural strength	- MPa
Flexural modulus	- MPa
Surface hardness	-

Thermal properties
Softening temperature	(ISO 306) 62 ºC

Other
HS Code	3916.9
Spool diameter (outer)	200 mm
Spool diameter (inner hole)	55 mm
Spool width	65.6 mm

Other information

PLA Dual Matte Color Combinations

Camouflage - Dark Green + Brown

Chameleon - Teal + Yellow

Flamingo - Pink + Red

Foggy Orange - Grey + Orange

Foggy Purple - Grey + Purple

Glacier Blue - Ice + Blue

Mixed Berries - Red + Dark Blue

Shadow Black - White + Black

Shadow Orange - Orange + Black

Shadow Red - Black + Red

Sunrise - Red + Yellow

Like any 3D printing filament, the Panchroma PLA filaments should be stored properly in order to avoid their deterioration and, in consequence, extrusion problems and inferior print quality. The spool can be stored in an airtight plastic bag, in a resealable bag with a desiccant capsule, or in a smart filament container. If the filament has absorbed too much moisture, it must be dried before printing in a filament dryer for 6 hours at 55 ºC or in the PolyDryer solution. The recommended settings are setting 1 for Panchroma PLA Silk and others, and settings 1-3 for PLA Matte and Satin.

The Panchroma PLA filaments should be extruded at a temperature of 190-230 ºC on a bed heated to 25-60 ºC. It is recommended to use the cooling fan at 100% but a printer with a heated chamber is not needed. As far as the printing speed, it is recommended to use max. 200 mm/s for the PLA Silk and other Panchroma PLA varieties, max. 300 mm/s for the PLA Satin and Matte PLA, and max. 400 mm/s for CoPE.

Complex parts can be 3D printed with the Panchroma PLA filaments with the help of support filaments such as the PolySupport filament or the PolyDissolve S1 filament.

Panchroma PLA Glow and Panchroma PLA Luminous are glow-in-the-dark materials enriched with an abrasive additive, making a hardened nozzle essential for printing. These filaments should not be used in AMS systems with plastic gears or tubes due to their abrasive nature.