Hyper Speed PLA Raise3D

RAISE-PLA-HYPER-WHITE-175-1000
36.00 € 36.00 €
Tax excl.
Diameter
Format
Colour
Quantity

In stock 10 units available for immediate shipping.
units available for shipping in 7 - 10 days Available for shipment within 7 - 10 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Thursday 5 December
Available

The Hyper Speed PLA filament was developed by Raise3D as part of the high-speed line for FFF printing. The main feature of this filament is that when used with the Hyper Speed Upgrade KIt (HUK3) for the Pro3 series, it can print within the impressive range of 150-300 mm/s (vs. 50-150 mm/s without the Hyper FFF upgrade) with acceleration of 10000 mm/s2 and yet still maintain high quality. In the words of the manufacturer, The Hyper Speed filaments offer 100 % the quality and 300 % the productivity.

Video 1: The benefits of printing with the Hyper Speed filaments. Source: Raise3D.

Whenever standard PLA is extruded at high speeds (rapidly fed into the heat block), the polymer has very little time to pass from solid to molten state, which can cause nozzle clogging and poor bonding quality between layers. With the Hyper Speed PLA, Raise3D has intended to solve this problem by optimizing the molecular weight and tuning the flowability of the PLA.

The colors of Hyper Speed PLA filament

Image 1: The colors of Hyper Speed PLA filament. Source: Raise3D.

This way, Hyper Speed PLA is able to achieve faster melting in the hot end and much faster cooling after the material is extruded. As a result of the upgrades, the surface quality of parts printed with the Hyper Speed PLA filaments is smooth and most of the sharp details are kept. Thanks to optimized molecular weight, Hyper Speed PLA also shows excellent interlayer bonding quality and Z-direction strength.

The Premium PLA filament vs. the Hyper Speed PLA filament

Image 2: The Premium PLA filament vs. the Hyper Speed PLA filament. Source: Raise3D.

According to Raise3D statistics, when prototyping is 200 % faster, design iterations can be completed within a day, the yield of a 3D printer increases to up to over 4 times, and the lead time for a single part is 66 % shorter. When the Hyper Speed filaments are used in small batch production, the productivity increases by even 500 %, shortening the response time from weeks to days. As far as in-house supply, using the Hyper Speed filaments can lead to even 1000 % increases in productivity. Thanks to its high speed extrusion capabilities, excellent mechanical properties of the parts and their great surface finish, Hyper Speed PLA can be used for the purposes of rapid prototyping, the printing of concept models and figures, to make manufacturing aids or even in art and scultpure applications, and in education and visualization.

The properties of the Hyper Speed PLA filament

Image 3: The properties of the Hyper Speed PLA filament. Source: Raise3D.

It must be kept in mind that in order to extrude with the Hyper Speed PLA filamet at speeds of over 150 mm/s, it is necessary to be using the Pro 3 or Pro 3 Plus 3D printers with the Hyper Speed Upgrade Kit installed and the Hyper Speed Mode in ideaMaker set (the most recent version ideaMaker 4.4.0 Alpha must be installed).

General information
Material PLA
Format 1 kg
Density 1.21 g/cm³
Filament diameter 1.75 mm
Filament tolerance - mm
Filament length ±343.6 m

Printing properties
Printing temperature 200 - 230 ºC
Print bed temperature 45 - 60 ºC
Chamber temperature -
Cooling fan ✓
Recommended printing speed 50 - 300 mm/s

Mechanical properties
Elongation at break (ISO 527) 15.0 ± 0.8 %
Tensile strength (ISO 527) 59 ± 1 MPa
Tensile modulus (ISO 527) 2600 ± 215 MPa
Flexural strength (ISO 178) 81 ± 2 MPa
Flexural modulus (ISO 178) 2700 ± 154 MPa
Surface hardness -
Impact strength 4.3 KJ/m²

Thermal properties
Softening temperature (ISO 75 @ 0.45 MPa) 53 ºC

Other
HS Code 3916.9
Spool diameter (outer) - mm
Spool diameter (inner hole) - mm
Spool width - mm

It is recommended to print the Raise3D Hyper Speed PLA at a temperature of 200-230 °C at 50-300 mm/s, on a bed heated to 45-60 °C with the layer fan on. To print in the 150-300 mm/s range, it is necessary to install the Hyper Speed Upgrade Kit.

This filament should be dried at 40°C for approximately 8 hours before printing in a filament dryer. Despite the low moisture absorption properties of this filament, it should be stored properly, preferably in a vacuum sealed container or in a sealed bag with a desiccant capsule until use or in a drying case, such as the Fiber Three drying case.

ideaMaker print profiles for Hyper Speed PLA filament are available on the ideaMaker website.

Featured properties

Printing temperature
200 - 230 ºC
Filament diameter
1.75 mm
High speed compatible
Yes
Density
1,21 g/cm³