PolyLite PLA

Ref.: PLA-POLYLITE-WHITE-175-1000

29.95 €

Tax excl.

Diameter

Format

Colour

Quantity

In stock 4 units available for immediate shipping.
units available for shipping in 0 - 0 days Available for shipment within 0 - 0 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Thursday 26 December

Available

Returns

Ask about this product

PolyLite™ is a family of 3D printing filaments developed by Polymaker and manufactured with the best raw materials to offer exceptional quality and reliability. PolyLite™ covers the most popular 3D printing materials to meet everyday needs for design and prototyping or final part creation.

Polymaker's PolyLite™ PLA filament is composed of polylactic acid. PLA is a biodegradable plastic obtained from natural resources, specifically from starch extracted from corn, sugar beet and wheat.

Video 1: Introduction to Polylite PLA. Source: Polymaker.

PLA is one of the most common materials in the world of 3D printing thanks to its ease of printing, good results and wide range of colours. In addition, PLA is biodegradable and does not emit fumes or noxious odours.

The ease of use of this material derives from several factors:

It does not require a heated bed, although in case it is available, it is recommended to use it at 50ºC.
It is printed at low temperatures (between 190ºC and 220ºC).
It is a material with an almost non-existent warping (warping is the deformation of the pieces with respect to the base).

In addition, thanks to Polymaker's patented "Jam-Free" technology, Polylite PLA significantly improves thermal stability by increasing the softening temperature, resulting in a "Jam-Free" filament.

Jam Free Technology

Image 1: Polymaker Jam Free Technology. Source: Polymaker.

In addition to all its properties, Polymaker's PolyLite™ PLA filament is a PLA with a great price/performance ratio. If enhanced mechanical properties are required, Polymaker's Polymax PLA filament is recommended.

Parts 3D printed with the PolyLite PLA

Image 2: Parts 3D printed with the PolyLite PLA. Source: Polymaker.

The packaging in which Polymaker presents its filaments is highly studied and carefully designed to preserve the quality and condition of its filaments. In this case, PolyLite™ PLA is presented inside a vacuum-sealed bag together with a desiccant sachet to prevent the filament from getting wet. This bag is self-sealing, so once the filament has been used, it can be put back into the bag. In addition, all of this is enclosed in a high quality printed box, to avoid knocks and breakages during shipping.

Polymaker's PolyLite™ PLA is an ideal material for the manufacture of decorative parts or non-functional prototypes for various industries.

General information
Material	PLA
Format	50 g / 1000 g / 3000 g / 5000 g
Density	1.24 g/cm³
Filament diameter	1.75 / 2.85 mm
Filament tolerance	± 0.05 mm
Filament length	(Ø 1.75 mm -1 kg) ±335m / (Ø 2.85 mm -1 kg) ±126m / (Ø 1.75 mm -3 kg) ±1005.9m / (Ø 2.85 mm -3 kg) ±379.2m / (Ø 1.75 mm -5 kg) ±1676.4m

Printing properties
Printing temperature	190 - 220 ºC
Print bed temperature	40 - 45 ºC
Chamber temperature	✗
Cooling fan	✓
Recommended printing speed	60 mm/s

Mechanical properties
Charpy impact strength	2.7 ± 0.2 KJ/m²
Elongation at break	(ASTM D638) 1.9 ± 0.2 %
Tensile strength	(ASTM D638) 46.6 ± 0.9 MPa
Tensile modulus	(ASTM D638) 2636 ± 330 MPa
Flexural strength	(ASTM D790) 85.1 ± 2.9 MPa
Flexural modulus	(ASTM D790) 3283 ± 132 MPa
Surface hardness	-

Thermal properties
Softening temperature	(ISO 306) 63 ºC

Specific properties
Transparency	✗

Other
HS Code	3916.9
Spool diameter (outer)	200 mm
Spool diameter (inner hole)	55 mm
Spool width	68 mm

Although the ideal printing temperature of PolyLite™ PLA may vary for each 3D printer, the ideal printing temperature is between 190 and 220 ºC. If a heated bed is available, it is recommended to use the bed at a temperature between 40 and 55°C.

It is advisable to use the layer fan. Because of this it is important to adjust the ideal temperature depending on the extruder used. PolyLite™ PLA filament is suitable for any type of nozzle. In terms of printing speed, it is advisable to print at around 60 mm/s, although it is possible to print slower for 3D prints with a better finish.

The shrinkage for a 0.5 mm nozzle is 1 mm. Therefore, following this rule can be applied to any nozzle ratio.

PolyLite™ PLA filament is moderately hygroscopic. In case the filament contains more moisture than it should, it is recommended to dry the filament in a dedicated drying machine such as the Print Dry Pro filament dryer.

Moisture can cause errors and even failed 3D prints. To avoid it at all times and not require the use of a filament dryer, it is recommended to use Polybox during the entire printing process and then store the filament in the self-sealing bag provided by Polymaker.