Smartfi GLACE
search
Compare
You must be logged in to manage your wishlist.

Smartfil GLACE

SMF-GLACE-NATURAL-175-750
32.15 € 32.15 €
Tax excl.
Diameter
Format
Quantity

In stock -2 units available for immediate shipping.
units available for shipping in 0 - 0 days Available for shipment within 0 - 0 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Out of Stock

Smartfil Glace is a filament that offers what many users of a 3D FDM printer look for, almost 100% translucent pieces.

This thermoplastic polymer shows impact resistance, high flexibility and other mechanical properties superior to ABS and PLA. Smartfil Glace does not present the problematic warping effect, giving the possibility of making really large pieces without errors and with an excellent finish.

Smartfil Glace is a filament that can be post-processed with alcohol, such as PolySmooth, to achieve different finishes. Within these finishes, the possibility of achieving a very high translucency, close to 100 %, or polishing the surface to eliminate roughness, obtaining a pearly finish. In addition, this polishing with alcohol increases the structural strength by strengthening the bond between layers and ensures the tightness of the piece.

Piece printed with SMF GLACEPiece printed with SMF GLACE and post-processed with IPA alcohol

Image 1: Piece printed with Smarfil GLACE before and after being post-processed with IPA alcohol. Source: SmartMaterials

The union of all the aforementioned properties, affirm that Smartfil Glace is an ideal filament to make resistant and translucent pieces, recommended to print containers and housings for industrial applications, where it is necessary to check the correct functioning of the system that is inside.

All users who want the (almost) transparent finish can visit the "Tips for Use" section to know how to perform post-processing.

General information
Material PVB
Format 50 g / 750 g
Density (ISO 1183) 1.10 g/cm³
Filament diameter 1.75 / 2.85 mm
Filament tolerance ± 0.05 mm
Filament length (Ø 1.75 mm - 0.750 Kg) ± 283 / (Ø 2.85 mm - 0.750 Kg) ± 106 m

Mechanical properties
Elongation at break 1.8 %
Tensile strength (ASTM D882) 54 MPa
Tensile modulus - MPa
Flexural strength (ASTM D790) 76 MPa
Flexural modulus 1923 MPa
Surface hardness -
Impact strength 9 KJ/m²

Printing properties
Printing temperature 205 - 235 ºC
Print bed temperature 0 - 70 ºC
Chamber temperature -
Cooling fan ✓
Recommended printing speed 20 - 30 mm/s

Thermal properties
Softening temperature (ASTM D1525) 84 ºC

Specific properties
Transparency -

Other
HS Code 3916.9
Spool diameter (outer) 200 mm
Spool diameter (inner hole) 55 mm
Spool width 50 mm

To achieve pieces close to 100% translucency, it is recommended to print models with a single layer of thickness so that the alcohol penetrates homogeneously on the material. Another important aspect is to use nozzle with large outlet diameter, 0.8 mm or more, to obtain pieces with sufficient wall thickness to maintain the necessary mechanical strength. If the user wishes to achieve the closest to transparency finish, it is recommended to use the "Spiral Vase" printing mode, with which the part is manufactured in a continuous layer.

How to get transparent parts

To achieve this finish, the user must use alcohol (ethyl or isopropyl) with a concentration higher than 70º, taking into account that the higher the graduation, the faster it will be in post-processing, but the more complex it will be to control it. The methods of application of alcohol are:

Direct application by immersion: You must completely submerge the piece in a container with alcohol for a few seconds, taking into account that this process is very aggressive, causing deformations if the time is excessive. The piece is then removed and allowed to drain until the alcohol evaporates completely.

Direct application in piece: The user must spray the surfaces of the piece directly with alcohol and then let the alcohol evaporate naturally. This method causes the piece to soften a little due to the absorption of alcohol, but this is eliminated once all the alcohol has evaporated.

Application by evaporation: In a completely closed container the piece to be post-processed and a paper impregnated with alcohol are introduced, so that it surrounds the piece. The user must ensure that the paper is not in contact with the piece, as that will deform it. If, after evaporating all the alcohol from the paper, the finish is not desired, the process can be repeated.

These processes, in addition to increasing translucency, improve the appearance of the piece by smoothing the surface, regardless of geometry.

Featured properties

Printing temperature
205 - 235 ºC
Filament diameter
1.75 / 2.85 mm
Density
1,1 g/cm³

Related products