Tarfuse PA CF10 filament

Reference:

Brand: Grupa Azoty

Condition: New product

2 Item Items

Diameter

Format

Colour

Quantity

55,95 €

Ask for information

Nylon filament reinforced with carbon fiber for antistatic and electrically conductive parts.

Add to wishlist

More info
Data sheet
Download
Usage tips
Specifications

Tarfuse PA CF10 belongs to the group of advanced 3D printing materials from Grupa Azoty. Tarfuse PA CF10 is a polyamide 6 material reinforced with high quality chopped carbon fibers. PA CF10 is characterized by high polymer crystallinity, high interlayer strength (excellent layer adhesion), elevated strength, and reduced water absorption. The addition of carbon fibers gives this material antistatic and electrically conductive properties.

A part 3D printed with the Tarfuse PA CF10 filament

Image 1: A part 3D printed with the Tarfuse PA CF10 filament. Source: Grupa Azoty.

Tarfuse PA CF10 is the perfect material for the 3D printing of functional and technical parts that need to perform well and maintain their dimensional stability in harsh environments. Furthermore, the antistatic properties make Tarfuse PA CF10 adequate for the production of tools, jigs and fixtures, and all sorts of parts that will be used in the manufacturing of electronic equipment. The antistatic properties will allow the electrostatic discharge evacuate safely along the surface of the part 3D printed with Tarfuse PA CF10, thus helping avoid critical or latent damage to sensitive electronic equipment. Materials with antistatic properties are also highly recommended in environments with explosive atmospheres or in the aerospace industry, and the mechanical strength makes Tarfuse PA CF10 great for applications in the automotive sector.

Elongation at break (%)	2
Tensile strength (MPa)	80
Tensile modulus (MPa)	5100
Flexural strength (MPa)	110
Lightweight	Lightweight
Fiber reinforced	Fiber reinforced
Chemical resistance	Chemical resistance

Tarfuse PA CF10 Datasheet

Download

The spool should be stored properly to avoid potential printing and part quality issues. It is recommended to store the spool in a tightly sealed plastic bag with a desiccant or in an intelligent filament container. If the filament absorbs excess moisture, it is recommended to dry the filament in a dryer with an air dehumidifier for 4-16 h at 80 ºC.

This material should be printed at a temperature of 270-280 ºC on a bed heated to 30-110 ºC. The recommended chamber temperature is 20-90 ºC and the optimal printing speed is 30-60 mm/s. The recommended bed material is glass, PC or a PA mat + PVA glue.

General information
Manufacturer	Grupa Azoty
Material	PA CF10
Format	Spool of 1000g
Density (ISO 1183)	1.18 g/cm³
Diameter of filament	1.75 or 2.85 mm
Diameter tolerance	± 0.05 mm
	±352.3 m (Ø 1.75 mm-1 Kg) ±132.8 m (Ø 2.85 mm-1 Kg)
Color	Black
RAL/Pantone	-
Print settings
Printing temperature	270-280 ºC
Print bed temperature	30-110 ºC
Chamber temperature	20-90 ºC
Cooling fan	-
Printing speed	30-60 mm/s
Mechanical properties
Izod impact strength	-
Charpy impact strength	-
Elongation at break (ISO 527-1,-2)	XY: 2 % XZ: 2 %
Tensile strength (ISO 527-1,-2)	XY: 80 MPa XZ: 96 MPa
Tensile Modulus (ISO 527-1,-2)	XY: 5100 MPa XZ: 7000 MPa
Flexural strength (ISO 178)	XY: 110 MPa XZ: 4900 MPa
Flexural modulus	-
Thermal properties
Softening temperature	-
Melting temperature (ISO 11357-1-3)	220 ºC
Additional Information
HS Code	3916.9
Spool Diameter (outer)	-
Spool Diameter (inner hole)	-
Spool Width	-

* The typical values detailed in this table should be considered as a reference. Actual values may vary depending on the 3D printer model used, part design and printing conditions. We recommend confirming the results and final properties with own tests. For more information you should consult the technical data sheet of the product.