The PLA Marble filament from the Panchroma collection offers a striking option for 3D printing, designed to mimic the natural texture and appearance of marble. This unique finish is achieved through the inclusion of fine additive particles within the filament, creating subtle patterns and depth for a realistic stone-like effect. Perfect for design projects, artistic creations, and architectural prototypes, PLA Marble adds a sophisticated touch to any print, combining aesthetic appeal with practicality.
As part of the Panchroma range, the PLA Marble filament exemplifies the commitment to innovative materials that ensure both high printability and visual quality. Its carefully engineered composition allows creators to achieve consistent results while enhancing their projects with a realistic marble texture. Whether for functional prototypes or decorative items, this filament is a superb choice for achieving an elegant, high-end look.
Recommended extrusion temperatures for the PLA Marble filament range from 190-230 ºC, with a bed temperature of 25-60 ºC, and optimal print speeds fall between 30-70 mm/s to ensure the best results. Its spool design, featuring an anti-slip edge, ensures smooth handling and compatibility with automated material systems like the Bambu Lab AMS, making it both versatile and reliable for advanced 3D printing applications.
General information |
|
Material | PLA |
Format | 1 kg |
Density | 1.19 g/cm³ |
Filament diameter | 1.75 mm |
Filament tolerance | ±0.03 mm |
Filament length | ±349.4 m |
Printing properties |
|
Printing temperature | 190 - 230 ºC |
Print bed temperature | 25 - 60 ºC |
Chamber temperature | ✗ |
Cooling fan | ✓ |
Recommended printing speed | 30 - 70 mm/s |
Mechanical properties |
|
Charpy impact strength | (ISO 179) 3.3 ± 0.2 KJ/m² |
Elongation at break | 2 % |
Tensile strength | (ISO 527) XY: 52.3 ± 0.3 MPa / Z: 40.5 ± 0.5 MPa |
Tensile modulus | (ISO 527) XY: 3427 ± 65 MPa / Z: - MPa |
Flexural strength | 39 MPa |
Flexural modulus | 2700 MPa |
Surface hardness | - |
Thermal properties |
|
Softening temperature | (ISO 306) 63 ºC |
Other |
|
HS Code | 3916.9 |
Spool diameter (outer) | 200 mm |
Spool diameter (inner hole) | 55 mm |
Spool width | 65.6 mm |
Other information | |
HEX codesWhite #CFCCD6 Slate Grey #91C2CC Brick - Limestone - Sandstone - |
Like any 3D printing filament, the Panchroma PLA filaments should be stored properly in order to avoid their deterioration and, in consequence, extrusion problems and inferior print quality. The spool can be stored in an airtight plastic bag, in a resealable bag with a desiccant capsule, or in a smart filament container. If the filament has absorbed too much moisture, it must be dried before printing in a filament dryer for 6 hours at 55 ºC or in the PolyDryer solution. The recommended settings are setting 1 for Panchroma PLA Silk and others, and settings 1-3 for PLA Matte and Satin.
The Panchroma PLA filaments should be extruded at a temperature of 190-230 ºC on a bed heated to 25-60 ºC. It is recommended to use the cooling fan at 100% but a printer with a heated chamber is not needed. As far as the printing speed, it is recommended to use max. 200 mm/s for the PLA Silk and other Panchroma PLA varieties, max. 300 mm/s for the PLA Satin and Matte PLA, and max. 400 mm/s for CoPE.
Complex parts can be 3D printed with the Panchroma PLA filaments with the help of support filaments such as the PolySupport filament or the PolyDissolve S1 filament.
Panchroma PLA Glow and Panchroma PLA Luminous are glow-in-the-dark materials enriched with an abrasive additive, making a hardened nozzle essential for printing. These filaments should not be used in AMS systems with plastic gears or tubes due to their abrasive nature.
Extra Tools to Enhance the Printing Experience
To further facilitate the 3D printing experience, support tools such as app.polymaker.com, an interactive comparison tool for mechanical, technical, and color properties among different filaments, and wiki.polymaker.com, a quick and comprehensive guide on using our products and 3D printing recommendations, can be utilized.