Panchroma PLA Matte Army

Ref.: PCHR-PLA-AMAT-BEIGE-175-1000

16.52 €

Tax excl.

Diameter

Format

Colour

Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 15 - 21 days Available for shipment within 15 - 21 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Wednesday 12 February - Thursday 20 February

Available

Returns

Ask about this product

The PLA Matte Army filament from the Panchroma series offers a distinctive and practical option for 3D printing, combining ease of use with a rugged, military-inspired aesthetic. With a matte finish and minimal visible layer lines, this filament is perfect for creating durable prototypes and industrial-style decorative pieces. The army-inspired color palette provides a bold, earthy tone that adds a unique and robust character to any project, making it ideal for designs that require a strong, commanding presence.

The color range of the PLA Matte Army filament

Image 1: The color range of the PLA Matte Army filament. Source: Panchroma.

The Panchroma collection is renowned for its expansive selection of colors, surface finishes, and filament effects, each meticulously formulated for optimal printability and excellent visual results. Every filament is engineered to provide consistent, high-quality output while enhancing the final product’s aesthetic appeal. Whether you're creating detailed prototypes or functional designs, the Panchroma range ensures precision and reliability for a wide variety of applications.

The PLA Matte Army filament in Army Purple

Image 2: The PLA Matte Army filament in Army Purple. Source: Panchroma.

Printing with PLA Matte Army is straightforward and efficient, with an extrusion temperature range of 190-230 ºC and a bed temperature of 25-60 ºC. It supports printing speeds of up to 300 mm/s, offering versatility for both high-speed and detailed projects without compromising on quality. Featuring an anti-slip edge, the filament’s smart spool design ensures smooth operation, particularly when used with automatic material handling systems like the Bambu Lab AMS, making it a reliable and adaptable choice for a range of 3D printing needs.

General information
Material	PLA
Format	1 kg
Density	1.37 g/cm³
Filament diameter	1.75 mm
Filament tolerance	±0.03 mm
Filament length	±303.5 m

Printing properties
Printing temperature	190 - 230 ºC
Print bed temperature	25 - 60 ºC
Chamber temperature	✗
Cooling fan	✓
Recommended printing speed	Max. 300 mm/s

Mechanical properties
Charpy impact strength	(ISO 179) 10.0 ± 0.8 KJ/m²
Elongation at break	- %
Tensile strength	(ISO 527) XY: 28.1 ± 0.5 MPa / Z: 15.4 ± 0.2 MPa
Tensile modulus	(ISO 527) XY: 2049 ± 64 MPa / Z: - MPa
Flexural strength	- MPa
Flexural modulus	- MPa
Surface hardness	-

Thermal properties
Softening temperature	(ISO 306) 62 ºC

Other
HS Code	3916.9
Spool diameter (outer)	200 mm
Spool diameter (inner hole)	55 mm
Spool width	65.6 mm

Other information

PLA Matte Army HEX Codes

Beige #CCA897

Blue #062B4D

Brown #724E3D

Dark Green #515234

Light Green #A78403

Purple #-

Red #AC1A17

Like any 3D printing filament, the Panchroma PLA filaments should be stored properly in order to avoid their deterioration and, in consequence, extrusion problems and inferior print quality. The spool can be stored in an airtight plastic bag, in a resealable bag with a desiccant capsule, or in a smart filament container. If the filament has absorbed too much moisture, it must be dried before printing in a filament dryer for 6 hours at 55 ºC or in the PolyDryer solution. The recommended settings are setting 1 for Panchroma PLA Silk and others, and settings 1-3 for PLA Matte and Satin.

The Panchroma PLA filaments should be extruded at a temperature of 190-230 ºC on a bed heated to 25-60 ºC. It is recommended to use the cooling fan at 100% but a printer with a heated chamber is not needed. As far as the printing speed, it is recommended to use max. 200 mm/s for the PLA Silk and other Panchroma PLA varieties, max. 300 mm/s for the PLA Satin and Matte PLA, and max. 400 mm/s for CoPE.

Complex parts can be 3D printed with the Panchroma PLA filaments with the help of support filaments such as the PolySupport filament or the PolyDissolve S1 filament.

Panchroma PLA Glow and Panchroma PLA Luminous are glow-in-the-dark materials enriched with an abrasive additive, making a hardened nozzle essential for printing. These filaments should not be used in AMS systems with plastic gears or tubes due to their abrasive nature.