Panchroma CoPE

Ref.: PCHR-COPE-BLACK-175-1000

16.52 €

Tax excl.

Diameter

Format

Colour

Volume discounts

Quantity	Discount	Price
5	5% 5%	15.69 € 15.69 €
10	8% 8%	15.20 € 15.20 €

Quantity

In stock 11 units available for immediate shipping.
units available for shipping in 15 - 21 days Available for shipment within 15 - 21 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Friday 19 September

Available

Returns

Ask about this product

The CoPE (Regular) filament is a cutting-edge material from the Panchroma range designed for enhanced 3D printing performance. Its advanced formula improves printability by enabling better bridging and overhang capabilities while broadening the printing temperature range. Additionally, it supports printing speeds of up to 400 mm/s, making it ideal for high-speed production on standard FDM 3D printers without requiring hardware modifications.

Video: Introduction to Polymaker’s Panchroma CoPe 3D filament.

What to keep in mind

Due to its exceptional bed adhesion, Panchroma CoPE (Regular) is not recommended for use on textured PEI surfaces, as it could cause bed damage. For optimal print release, applying Magigoo Original is advised. Combining this filament with standard PLA or other Panchroma effects within the same print is discouraged, as adhesion between these materials may be inconsistent.

The CoPE filament is available in many vibrant colors

Image 1: The CoPE filament is available in many vibrant colors. Source: Panchroma.

It is recommended to print with the CoPE filament using an extrusion temperature range of 190-230 ºC and a bed temperature of 25-60 ºC. This filament supports speeds of up to 400 mm/s, enabling both rapid production and fine detailing. The filament’s spool is equipped with an anti-slip edge for smooth handling, particularly when used with automated material systems like the Bambu Lab AMS, making it a reliable and adaptable choice for a variety of 3D printing applications.

General information
Material	PLA
Format	1 kg
Density	1.30 g/cm³
Filament diameter	1.75 mm
Filament tolerance	±0.03 mm
Filament length	±319.8 m

Printing properties
Printing temperature	190 - 230 ºC
Print bed temperature	25 - 60 ºC
Chamber temperature	✗
Cooling fan	✓
Recommended printing speed	Max. 400 mm/s

Mechanical properties
Charpy impact strength	(ISO 179) 2.9 ± 0.1 KJ/m²
Elongation at break	- %
Tensile strength	(ISO 527) XY: 51.6 ± 0.3 MPa / Z: 36.1 ± 1.2 MPa
Tensile modulus	(ISO 527) XY: 2515 ± 71 MPa / Z: - MPa
Flexural strength	- MPa
Flexural modulus	- MPa
Surface hardness	-

Thermal properties
Softening temperature	(ISO 306) 66 ºC

Other
HS Code	3916.9
Spool diameter (outer)	200 mm
Spool diameter (inner hole)	55 mm
Spool width	65.6 mm

Other information

HEX codes

Polymaker Teal #4CC0C7

Black #080A0D

White #E2DEDB

Steel Grey #616469

Grey #8C9099

Purple #6C47B2

Red #E72F1D

Brown #55331A

Orange #F67405

Yellow #F3B400

Green #06924D

Blue #003776

Like any 3D printing filament, the Panchroma PLA filaments should be stored properly in order to avoid their deterioration and, in consequence, extrusion problems and inferior print quality. The spool can be stored in an airtight plastic bag, in a resealable bag with a desiccant capsule, or in a smart filament container. If the filament has absorbed too much moisture, it must be dried before printing in a filament dryer for 6 hours at 55 ºC or in the PolyDryer solution. The recommended settings are setting 1 for Panchroma PLA Silk and others, and settings 1-3 for PLA Matte and Satin.

The Panchroma PLA filaments should be extruded at a temperature of 190-230 ºC on a bed heated to 25-60 ºC. It is recommended to use the cooling fan at 100% but a printer with a heated chamber is not needed. As far as the printing speed, it is recommended to use max. 200 mm/s for the PLA Silk and other Panchroma PLA varieties, max. 300 mm/s for the PLA Satin and Matte PLA, and max. 400 mm/s for CoPE.

Complex parts can be 3D printed with the Panchroma PLA filaments with the help of support filaments such as the PolySupport filament or the PolyDissolve S1 filament.

Panchroma PLA Glow and Panchroma PLA Luminous are glow-in-the-dark materials enriched with an abrasive additive, making a hardened nozzle essential for printing. These filaments should not be used in AMS systems with plastic gears or tubes due to their abrasive nature.

Extra Tools to Enhance the Printing Experience

To further facilitate the 3D printing experience, support tools such as app.polymaker.com, an interactive comparison tool for mechanical, technical, and color properties among different filaments, and wiki.polymaker.com, a quick and comprehensive guide on using our products and 3D printing recommendations, can be utilized.