PolyCore PETG-1013 pellets
search
  • PolyCore PETG-1000 pellets
  • PolyCore PETG-1013 pellets
Compare
You must be logged in to manage your wishlist.

PolyCore PETG pellets

POLY-PELLETS-PETG1013-25KG
231.25 € 231.25 €
Tax excl.
Format
Material
Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 15 - 21 days Available for shipment within 15 - 21 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Thursday 12 December - Friday 20 December
Available

The PolyCore PETG pellets by Polymaker are available in as simple PETG (PETG-1000) or the 30 % glass fiber composite PETG-1013.

Both varieties were developed specially for BAAM (Big Area Additive Manufacturing) and can be extruded with the help of equipment such as the CEAD AM Flexbot, the CEAD E25 extruder, the Mahor V4 pellet extruder, or the Dyze Pulsar extruder.

The PolyCore PETG-1000 pellets are very easy to work with, have a unique surface finish, and are perfect for indoor applications, for example in the BAAM as well as MAAM (Medium Area Additive Manufacturing) of furniture, lighting or decoration.

The PolyCore PETG-1013 pellets, on the other hand, give the 3D printed parts excellent dimensional stability, overall mechanical strength, and weather resistance thanks to the added glass fibers. Thus, the PolyCore PETG-1013 pellets will be the perfect material for outdoor applications where the 3D printed part must withstand impact, stress, wear and tear, and rough handling. 

General information
Manufacturer Polymaker
Material PETG
Format 25 kg
Density 1.3 g/cm³

Mechanical properties
Elongation at break (ASTM D638) (PETG-1000) 3D printing: -; Injection molding: 4.5 ± 0.9 % / (PETG-1013) 3D printing: - / Injection molding: - %
Tensile strength (ASTM D638) (PETG-1000) 3D printing: -; Injection molding: 50 ± 1.1 MPa / (PETG-1013) 3D printing: - / Injection molding: - MPa
Tensile modulus (ASTM D638) (PETG-1000) 3D printing: -; Injection molding: - / (PETG-1013) 3D printing: - / Injection molding: - MPa
Flexural strength (ASTM D790) (PETG-1000) 3D printing: (XY) 77.3 ± 8.7 MPa; (Z) 75.3 ± 3.9 MPa; Injection molding: 71 ± 2.4 MPa / (PETG-1013) 3D printing: (XY) 128.1 ± 7.8 MPa; (Z) 46.8 ± 3.3 MPa / Injection molding: - MPa
Flexural modulus (ASTM D790) (PETG-1000) 3D printing: (XY) 1576 ± 140 MPa; (Z) 1480 ± 84 MPa; Injection molding: 2150 ± 64 MPa / (PETG-1013) 3D printing: (XY) 6094 ± 1344 MPa; (Z) 2701 ± 366 MPa / Injection molding: - MPa
Surface hardness -
Impact strength 5.2 KJ/m²

Thermal properties
Melting temperature 220 ºC
Softening temperature - ºC
Processing temperature 230-240 ºC
MFR Ratio (PETG-1000) (@ 220 ºC, 2.16 kg) 4 g/10 min; (@ 240 ºC, 2.16 kg) 11 g/10 min / (PETG-1013) (@ 220 ºC, 10 kg) 11 g/10 min; (@ 240 ºC, 10 kg) 11 g/10 min
Glass transition temperature - ºC
Heat deflexion temperature - ºC

Specific properties
Chemical resistance ✓

Other
HS Code 3901.1

Proper storage of 3D printing materials is crucial for smooth extrusion and high surface quality and mechanical properties of the 3D printed part. PolyCore PETG pellets should be stored in a sealed package in dry conditions at a temperature below 50 °C, protected from UV light at all times. If the pellets absorb excess moisture, they should be dried for 8 hours at 70 °C (PETG-1000) or for 8-12 hours at 60-65 °C (PETG-1013). The recommended processing temperature for PolyCore PETG pellets is 210 to 230 °C.