CPE CF112 Carbon pellets

Ref.: FILL-PELLETS-CPECF112-1KG

38.71 €

Tax excl.

Format

Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 8 - 24 days Available for shipment within 8 - 24 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Thursday 16 January - Friday 7 February

Available

Returns

Ask about this product

CPE, a modified version of PETG, is an engineering material developed specially for the 3D printing of durable and tough technical parts with high dimensional stability and precision, a smooth matte surface finish, resistance to chemicals (acids, alkalis, alcohols), and ease of printing (255-275 ºC).

Reinforcing the CPE base with carbon fibers creates the CPE CF112 Carbon pellets by Fillamentum. These pellets have all those qualities of CPE boosted with creep resistance (deformation under long-term load), wear resistance, low warping, and heat resistance (up to 100 ºC).

Part 3D printed with CPE CF112 Carbon

Image 1: Part 3D printed with CPE CF112 Carbon. Source: Fillamentum.

Furthermore, CPE CF112 is 25 % bio-based, recyclable, and free of BPA and styrene. These porperties make the pellets safe to use and more environmentally-friendly.

The CPE CF112 Carbon pellets were created specially for BAAM (Big Area Additive Manufacturing) and MAAM (Middle Area Additive Manufacturing) in mind. They can be extruded with the help of FGF manufacturing solutions such as the CEAD AM Flexbot, the CEAD E25 extruder, the Mahor V4 pellet extruder, or the Dyze Pulsar extruder. This material is also available in filament format.

General information
Manufacturer	Fillamentum
Material	PET
Format	1 kg / 5 kg / 15 kg
Density	1.16 g/cm³

Electrical properties
Volumetric resistivity	10¹² Ohm/cm

Mechanical properties
Charpy impact strength	(ISO 179) 106 KJ/m²
Elongation at break	(ISO 527) 8 %
Tensile strength	(ISO 527) 38 MPa
Tensile modulus	(ISO 527) 2200 MPa
Flexural strength	- MPa
Flexural modulus	- MPa
Surface hardness	(ISO 7619) Shore 77 D

Thermal properties
Melting temperature	- ºC
Softening temperature	- ºC
Processing temperature	(ISO 306) 255-275 ºC
MFR Ratio	-
Glass transition temperature	(ISO 11357) 102 ºC
Heat deflexion temperature	- ºC

Specific properties
Chemical resistance	✓

Other
HS Code	3901.1

The proper storage of 3D printing materials is key to smooth extrusion, and great surface quality and mechanical properties of the 3D printed part. The CPE CF112 Carbon pellets should be stored in a closed package in dry conditions at temperature below 50 ºC, protected from UV-light at all times. If the pellets absorb excess moisture, they should be dried for 5 hours at 70 ºC. The recommended processing temperature for the CPE CF112 Carbon pellets is 255 - 275 ºC.