Flex V0 pellets

NANOVIA-PELLETS-FLEX-V0-500
30.00 € 30.00 €
Tax excl.
Format
Quantity

In stock 2 units available for immediate shipping.
units available for shipping in 11 - 16 days Available for shipment within 11 - 16 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Friday 22 November
Available

Nanovia's Flex V0 pellets are a meticulously designed 3D printing material tailored for environments where flexibility and fire resistance are crucial. These pellets feature a Shore 90A/40D rating and meet the UL-94 V0 classification at a minimal thickness of 0.8 mm, ensuring compliance with rigorous safety standards. Available also in filament format, the Flex V0 material offers versatility for various applications ranging from furniture and packaging to construction and automotive and aerospace industries, as well as manufacturing, safety equipment, medical devices, and outdoor gear.

Video 1: Self-extinction test of a part 3D printed with the Nanovia Flex V0 material. Source: Nanovia. 

Nanovia Flex V0 excels in mechanical performance, with a tensile strength of 27 MPa. The material maintains its structural integrity under stress, achieving 7 MPa at 100% elongation and 10 MPa at 300% elongation. With an ultimate elongation at break of 524%, Flex V0 ensures flexibility without compromising on strength, making it suitable for demanding industrial applications that require durability and resilience. The superior interlayer and bed adhesion properties of Nanovia Flex V0 contribute to enhanced part quality and dimensional stability, reducing the risk of deformation. 

General information
Manufacturer Nanovia
Material TPU/TPE
Format 500 g / 5 kg / 25 kg
Density 1.21 g/cm³

Mechanical properties
Elongation at break (VDE282.10) 524 %
Tensile strength (VDE282.10) 27 MPa
Tensile modulus - MPa
Flexural strength - MPa
Flexural modulus - MPa
Surface hardness Shore 90 A

Thermal properties
Melting temperature - ºC
Softening temperature - ºC
Processing temperature 235-245 ºC

Specific properties
Flammability classification (UL 94 @0.8 mm) V0

Other
HS Code 3901.1

The ideal printing temperature for Flex V0 is between 235 ºC and 245 ºC on a heated bed at 20-40 ºC. Since the Flex V0 pellets are a flexible material, it is recommended to reduce the printing speed of maximum volumetric speed should under-extrusion occur. It is crucial to store the Flex V0 pellets properly as processing of moist material may cause degradation of polymer chains, brittleness, poor layer adhesion, stringing and oozing. It is best to store the pellets in a tightly sealed bag or container with a desiccant.