TPU 85A Ultrafuse

Ref.: BASF-UF-TPU85A-NATURAL-175-750

33.71 €

Tax excl.

Diameter

Format

Colour

Quantity

In stock 18 units available for immediate shipping.
units available for shipping in 3 - 5 days Available for shipment within 3 - 5 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Thursday 26 December

Available

Returns

Ask about this product

TPU is often called a bridge between rubber and plastic thanks to its outstanding toughness and strength combined with a wide range of “hardness”, from rubber-like to plastic-like. The BASF Ultrafuse TPU 85A filament has a Shore hardness 85A, which places it in the hard category (shoe heel hardness) but different degrees of hardness can be achieved depending on the design. The most distinguishing features of the Ultrafuse TPU 85A filament are:

Excellent resistance to hydrolysis.
High chemical resistance to oils, greases, oxygen and ozone.
Good flexibility at low temperatures.
Resistance to slip, wear, abrasion and tear propagation.
Good damping behavior.
High tensile strength.

Furthermore, the Ultrafuse TPU 85A exhibits resistance to microbiological attack and has successfully passed biocompatibility tests for cytotoxicity XTT, skin irritation and skin sensitisation. Nevertheless, the biocompatibility of a filament does not necessarily mean that the 3D printed part will have the same features, which is why each part and application should be carefully assessed case by case. The biocompatibility statement can be consulted in the Downloads section.

A gripper 3D printed with the Ultrafuse TPU 85A filament

Image 1: A gripper 3D printed with the Ultrafuse TPU 85A filament. Source: BASF.

The outstanding thermal, mechanical and chemical properties of the Ultrafuse TPU 85A filament combined with its biocompatibility and resistance to microbiological attack make it an ideal material for applications in the fields of footwear, sports and leisure, as well as medical. In those fields, the Ultrafuse TPU 85A filament could be used to 3D print objects that need to be in contact with the patient’s skin and will get a significant amount of use, and therefore have to be resistant to wear and abrasion, but also strong and pleasant to the touch. The Ultrafuse TPU 85A filament could also be used in the automotive sector as well as in industrial manufacturing or agriculture and construction thanks to its chemical and heat resistance, great flexibility and low temperatures, damping properties and resistance to wear and abrasion.

General information
Material	TPU/TPE
Format	0.75 kg
Density	1.11 g/cm³
Filament diameter	1.75 / 2.85 mm
Filament tolerance	±0.05 - 0.1 mm
Filament length	(Ø 1.75 mm - 750 g) ±280.9 m / (Ø 2.85 mm - 750 g) ±105.9 m

Electrical properties
Volumetric resistivity	(IEC 62631-3-1) 2.6E+11 Ω/cm
Dielectric strength	(IEC 60243-1) 21 kV/mm

Printing properties
Printing temperature	200 - 220 ºC
Print bed temperature	40 ºC
Chamber temperature	-
Cooling fan	✗
Recommended printing speed	15 - 40 mm/s

Mechanical properties
Izod impact strength	(ISO 180) (notched) no break KJ/m²
Charpy impact strength	(ISO 179-2) (notched) no break / (notched @ -30 ºC) 47.3 KJ/m²
Elongation at break	(ISO 527) 600 %
Tensile strength	34 MPa
Tensile modulus	(ISO 527) 20 MPa
Flexural strength	- MPa
Flexural modulus	- MPa
Surface hardness	Shore 85 A

Thermal properties
Softening temperature	(ISO 306 @ 10 N) 114 ºC

Specific properties
Chemical resistance	✓

Other
HS Code	3916.9
Spool diameter (outer)	200 mm
Spool diameter (inner hole)	50.5 mm
Spool width	55 mm

Correct storage is as important for successful 3D prints as any other factor. The Ultrafuse TPU 85A filament should be stored in dry conditions before, during and after printing, at a temperature of 15-25 ºC. The spool can be kept in its original packaging, with a filament drying capsule, or in a vacuum sealed bag. An intelligent filament container can also be used to protect the filament from humidity. During printing, the spool can be placed in the Fiber Three filament drying case or an inline filament dryer. If the Ultrafuse TPU 85A filament absorbs excess moisture (which manifests in, among others, oozing, bubbles, sizzling and surface imperfections on the part), it should be dried at 70 °C in a hot air dryer or vacuum oven for at least 5 hours.

It is recommended to 3D print the Ultrafuse TPU 85A filament at a nozzle temperature of 200-220 ºC at a speed of 15-40 mm/s. The bed temperature should be set to 40 ºC and no adhesion products are necessary for great results, a clean glass bed is enough. The recommended extrusion system to use with the Ultrafuse TPU 85A filament is a direct drive extruder. Indirect drive extruders are prone to clogging or inconsistent throughput with flexible filaments.