PC-ABS V0 pellets

Ref.: NANOVIA-PELLETS-PC-ABS-V0-500

20.65 €

Tax excl.

Format

Quantity

In stock 4 units available for immediate shipping.
units available for shipping in 11 - 16 days Available for shipment within 11 - 16 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Friday 13 September

Available

Returns

Ask about this product

Nanovia's PC-ABS V0 pellets are a material that combines the printability of ABS with the mechanical and thermal properties of polycarbonate, making the latter suitable for printing on a wide variety of 3D printers. This material is ideal for demanding technical environments and is ideal for the production of impact-resistant components.

PC-ABS V0 pellets can be used in the manufacture of filament for FDM 3D printers using Filastruder or any other filament extruder.
It is possible to use a pellet extruder for 3D printing directly.

With the combination of PC-ABS V0 pellets and a good filament extruder such as Filastruder, it is possible to obtain 3D printing filament with qualities similar to those of a commercial filament.

When using PC-ABS V0 Pellets to make filament with a filament extruder such as Filastruder or using a pellet extruder for direct 3D printing, it should be noted that the extrusion temperature must be regulated in relation to the extrusion speed used. For optimal results, it is recommended to read the product's usage tips.

General information
Manufacturer	Nanovia
Material	PC-ABS
Format	0.5 / 5 kg
Density	1.18 g/cm³

Mechanical properties
Izod impact strength	(ISO 179/1eA @ 23 ºC) 50 KJ/m²
Charpy impact strength	(ISO 179/1eA @ 23 ºC) 40 KJ/m²
Elongation at break	(ISO 527) 43 %
Tensile strength	(ISO 527) 45 MPa
Tensile modulus	(ISO 527) 2560 MPa
Flexural strength	- MPa
Flexural modulus	- MPa
Surface hardness	-

Thermal properties
Melting temperature	- ºC
Softening temperature	- ºC
Processing temperature	270 - 290 ºC
Glass transition temperature	- ºC
Heat deflexion temperature	- ºC