PolyCore ASA-3012 pellets

Reference:

Brand: Polymaker

This product could be delivered in a longer time than the standard.

Condition: New product

Format

Quantity

268,75 €

Ask for information

ASA pellets with glass fiber. Ideal for outdoor applications or tooling.

Add to wishlist

More info
Data sheet
Download
Usage tips
Specifications

The PolyCore ASA-3012 pellets by Polymaker are made of ASA reinforced with 20 % of glass fiber. These pellets were developed specially for BAAM (Big Area Additive Manufacturing) and can be extruded with the help of equipment such as the CEAD AM Flexbot, the CEAD E25 extruder, the Mahor V4 pellet extruder, or the Dyze Pulsar extruder.

The Quanzhou Bridge 3D printed with the ASA-3012 pellets

Image 1: The Quanzhou Bridge 3D printed with the ASA-3012 pellets. Source: Polymaker.

The PolyCore ASA-3012 pellets are characterized by excellent printability, low warping, great colorability and strong mechanical properties. Thanks to the materials superior weather resistance and UV stability, parts 3D printed with the PolyCore ASA-3012 pellets can be used outdoors, for example in big-scale architecture (bridges, horticulture, landscape) or furniture. What's more, this material will perform great in low-to-mid temperature tooling applications.

Flexural strength (MPa)	67
Flexural modulus (MPa)	3320
Softening temperature (ºC)	105
UV resistance	UV resistance
Fiber reinforced	Fiber reinforced
Hide color variations	(Hide color variations)

ASA-3012 Datasheet

Download

ASA-3012 Safety Datasheet

Download

The proper storage of 3D printing materials is key to smooth extrusion, and great surface quality and mechanical properties of the 3D printed part. The PolyCore ASA-3012 pellets should be stored in a closed package in dry conditions at temperature below 50 ºC, protected from UV-light at all times. If the pellets absorb excess moisture, they should be dried for 4 hours at 80 ºC. The recommended processing temperature for the PolyCore ASA-3012 pellets is 210 - 230 ºC.

General Information
Material	ASA
Format	25 kg
Density	1.2 g/cm³
Color	Natural
Mechanical Properties
Izod Impact Strength	-
Charpy Impact Strength (ASTM D256)	3D printing: XY: 5.0 ± 0.32 kJ/m² Z: 2.3 ± 0.2 kJ/m² Injection molding: 8.5 ± 0.5 kJ/m²
Elongation at Break (ASTM D638)	3D printing: XY: - Z: - Injection molding: 2.6 ± 0.3 %
Tensile Strength (ASTM D638)	3D printing: XY: - Z: - Injection molding: 101.3 ± 2.4 MPa
Tensile Modulus (ASTM D638)	3D printing: XY: - Z: - Injection molding: 7237 ± 136 MPa
Flexural Strength (D790)	3D printing: XY: 66.6 ± 3.5 MPa Z: 27.2 ± 2.1 MPa Injection molding: 149.6 ± 2.1 MPa
Flexural Modulus (D790)	3D printing: XY: 3320 ± 160 MPa Z: 1646 ± 170 MPa Injection molding: 7094 ± 89 MPa
Surface Hardness	-
Thermal Properties
Processing Temperature	210-230 ºC
Glass Transition Temperature	-
Melting Temperature	220 ºC
MFR Ratio	(@ 220 ºC, 10 kg) 6-10 g/10 min
Additional Information
HS Code	3901.1

* The typical values detailed in this table should be considered as reference. We advise confirming the results and final properties with your own tests. For more information, consult the product's technical datasheet.