PolyCore ASA-3012 pellets

Ref.: POLY-PELLETS-ASA3012-25KG

268.75 €

Tax excl.

Format

Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 15 - 21 days Available for shipment within 15 - 21 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Thursday 23 January - Friday 31 January

Available

Returns

Ask about this product

The PolyCore ASA-3012 pellets by Polymaker are made of ASA reinforced with 20 % of glass fiber. These pellets were developed specially for BAAM (Big Area Additive Manufacturing) and can be extruded with the help of equipment such as the CEAD AM Flexbot, the CEAD E25 extruder, the Mahor V4 pellet extruder, or the Dyze Pulsar extruder.

The Quanzhou Bridge 3D printed with the ASA-3012 pellets

Image 1: The Quanzhou Bridge 3D printed with the ASA-3012 pellets. Source: Polymaker.

The PolyCore ASA-3012 pellets are characterized by excellent printability, low warping, great colorability and strong mechanical properties. Thanks to the materials superior weather resistance and UV stability, parts 3D printed with the PolyCore ASA-3012 pellets can be used outdoors, for example in big-scale architecture (bridges, horticulture, landscape) or furniture. What's more, this material will perform great in low-to-mid temperature tooling applications.

General information
Manufacturer	Polymaker
Material	ASA
Format	25 kg
Density	1.2 g/cm³

Mechanical properties
Charpy impact strength	(ASTM D256) (3D printing) XY: 58.5 ± 0.5.0 ± 0.32 kJ/m², Z: 2.3 ± 0.2 kJ/m² / (Injection molding) KJ/m²
Elongation at break	(ASTM D638) (3D printing) - / (Injection molding) 2.6 ± 0.3 %
Tensile strength	(ASTM D638) (3D printing) - / (Injection molding) 101.3 ± 2.4 MPa
Tensile modulus	(ASTM D638) (3D printing) - / (Injection molding) 7237 ± 136 MPa
Flexural strength	(ASTM D790) (3D printing) XY: 66.6 ± 3.5 MPa; Z: 27.2 ± 2.1 MPa / (Injection molding) 149.6 ± 2.1 MPa
Flexural modulus	(ASTM D790) (3D printing) XY: 3320 ± 160 MPa, Z: 1646 ± 170 MPa / (Injection molding) 7094 ± 89 MPa
Surface hardness	-

Thermal properties
Melting temperature	220 ºC
Softening temperature	- ºC
Processing temperature	210-230 ºC
MFR Ratio	(@ 220 ºC, 10 kg) 6-10 g/10 min
Glass transition temperature	- ºC
Heat deflexion temperature	- ºC

Other
HS Code	3901.1

The proper storage of 3D printing materials is key to smooth extrusion, and great surface quality and mechanical properties of the 3D printed part. The PolyCore ASA-3012 pellets should be stored in a closed package in dry conditions at temperature below 50 ºC, protected from UV-light at all times. If the pellets absorb excess moisture, they should be dried for 4 hours at 80 ºC. The recommended processing temperature for the PolyCore ASA-3012 pellets is 210 - 230 ºC.