ABS pellets (in powder) - Kai Parthy

Reference:

Brand: Lay Filaments

This product is NOT an SLS powder and should never be used as such at the risk of damaging the SLS printer.

Condition: New product

9 Item Items

Format

Colour

Quantity

28,00 €

Ask for information

ABS pellets in powder format (very small particle size), for extruding in pellets extruders.

Add to wishlist

More info
Data sheet
Usage tips
Specifications

These ABS pellets by Kai Parthy are an FGF 3D printing material to be used for direct extrusion or filament production. The Kai Parthy ABS pellets have a natural color and are made from the Terez 5010 ABS as the base material. The ABS pellets have a tensile strength of 46.3 MPa and a Vicat softening temperature of 97 ºC.

Along with PLA, ABS is one of the most common 3D printing materials. It is characterized by great mechanical strength, chemical resistance and resistance to high as well as low temperatures. Colorants can be added directly to the Kai Parthy ABS pellets to achieve personalized colors of the 3D printed parts or the fabricated filament.

The pellets have a powdery appearance due to their small particle size

Image 1: The pellets have a powdery appearance due to their small particle size. Source: Filament2Print.

A unique feature of this material is the very small particle size of 0.10-0.50 mm, which makes the pellets look like powder. Nevertheless, these ABS pellets are meant for FGF 3D printing and cannot be used on SLS 3D printing equipment at the risk of damaging the SLS 3D printer.

The best equipment for the processing of the Kai Parthy ABS pellets is the Mahor V4 pellet extruder or the Tumaker 3D printers for direct extrusion. It is also possible to make filament from the ABS pellets with the help of the Felfil EVO extruder.

Tensile strength (MPa)	46

It is very important to store ABS pellets in an airtight bag to prevent them from absorbing moisture from the environment before use. If the pellets have moisture in them, the resulting parts or filament may contain small imperfections. Once the filament has been manufactured using ABS pellets, it is also recommended to store the filament properly.

General information
Material	ABS
Format	1 Kg bag
Density (ISO 1183)	1.05 g/cm³
Particle or grain size	0.10-0.50 mm
Colour	Natural
Mechanical properties
Izod impact resistance	-
Charpy impact resistance (ISO 179/1eA, notched)	@ +23 ºC 19 kJ/m² @ -30 ºC 10 kJ/m²
Ultimate breaking strength	-
Maximal deformation at break (ISO 527)	2.4 %
Tensile strength (ISO 527)	46.3 MPa
Tensile modulus (ISO 527)	2200 MPa
Bending strength	-
Bending modulus (ISO 178)	2300 MPa
Surface hardness	-
Thermal properties
Processing temperature	220 ºC
Vicat softening temperature (ISO 306)	97 ºC
Glass transition temperature	-
Melting temperature	-
MFR Ratio	-
Additional information
HS Code	3901.1

* The typical values listed in this table should be considered as a reference. We advise you to confirm the final results and properties with your own tests. For further information please refer to the product data sheet.