PolyMax Tough PLA

Ref.: PLA-POLYMAX-WHITE-175-750

36.95 €

Tax excl.

Diameter

Format

Colour

Quantity

In stock 10 units available for immediate shipping.
units available for shipping in 0 - 0 days Available for shipment within 0 - 0 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Thursday 26 December

Available

Returns

Ask about this product

The PolyMax Tough PLA is the most powerful PLA on the market today because it combines the qualities of easy printing with any 3D printer (FFF/FDM) on the market with mechanical characteristics superior to ABS.

With the creation of this material, Polymaker has been able to outperform other common 3D printing materials (PLA and ABS) with superior impact resistance compared to other PLA and better overall mechanical properties than ABS. Such is its impact resistance, which is 9 times more resistant than other regular PLA and 20% higher than ABS.

Video 1: Flex test . Source: 3D Printing Solutions

Another aspect that stands out is the guarantee that it offers when printing large pieces without deformations (warping or cracking), even without hot base or in a printer that is not closed.

Large 3D printing without warping or cracking

Image 1: Large 3D printing without warping or cracking. Source: Polymaker

Thanks to PolyMaker's proprietary "Jam-Free" technology, this material greatly improves thermal stability by increasing the softening temperature and thus being a "Free of Jams" filament.

Great finish

Image 2: Great finish. Source: Polymaker

PolyMaker to maintain its high level in the filaments for 3D printing, guarantees the quality of its products and in this case in particular the PolyMax Tough PLA filament, realizing up to eight controls with a high level of exigency to guarantee simple, reliable 3D accurate to 3D printing users. In addition, all coils of this material are dried before being packaged in a reusable bag which is introduced into a box of high quality and hardness to keep the filament intact. Thanks to the reusable bag mentioned above, users can store the Polymax PLA in it when they are not using it and thus ensure that the material retains all its qualities intact. The outside of the box shows the general product information: color, diameter, filament quantity and recommended printing temperatures. PolyMax PLA coils have calibrated marks that indicate the approximate amount of filaments remaining, which helps to know if the amount of material available is sufficient for the next 3D impression.

Packaging

Imge 3: Packaging. Source: Polymaker

All of the above demonstrates why the PolyMax Tough PLA is one of the best and most versatile filaments on the market.

General information
Material	PLA
Format	750 g / 3000 g
Density	(ISO 1183) 1.17 - 1.24 g/cm³
Filament diameter	1.75 / 2.85 mm
Filament tolerance	± 0.05 mm
Filament length	(Ø 1.75 mm) ± 251 m / (Ø 2.85 mm) ± 94 m

Printing properties
Printing temperature	190 - 230 ºC
Print bed temperature	25 - 60 ºC
Chamber temperature	✗
Cooling fan	✓
Recommended printing speed	60 mm/s

Mechanical properties
Charpy impact strength	(ISO 179) 12.2 KJ/m²
Elongation at break	(ISO 527) 1.4 %
Tensile strength	(ISO 527) 28.1 MPa
Tensile modulus	(ISO 527) 1879 MPa
Flexural strength	(ISO 178) 48 MPa
Flexural modulus	(ISO 178) 2119 MPa
Surface hardness	-

Thermal properties
Melting temperature	149 ºC
Softening temperature	61 ºC

Specific properties
Transparency	✗

Other
HS Code	3916.9
Spool diameter (outer)	200 mm
Spool diameter (inner hole)	53 mm
Spool width	46 mm

3D printing with PLA is simpler and easier than with ABS. It is not necessary that the printer dock is hot, but if possible it is recommended that the base is at about 40-50 °C, to prevent any small sign of "warping" appears. The extruder temperature must be between 190 and 220 °C depending on the color and the 3D printer used. In our blog article 3D printing is explained about the main concerns of 3D printing PLA and ABS.

If your printer has a fan nozzle it is recommended that you activate it for best results. If you need to print very thin and tall pieces, you will see that the PLA plastic doesn´t give you enough time to harden each layer, so that the piece will be as if it had melted. To solve this problem we give a very simple advice, it prints at the same time at least two pieces, and place them separate at the base. Thus while the extruder is moved from one piece to another, the plastic has time to harden each layer in achieving a better result.
The adhesion of the first layer is key and probably the most important factors for good impressions. so you can use Blue Tape, BuildTak, Magigoo or 3DLac.

It is also advisable to set the "raft", which is to create a first thick layer, such as media, who will not suffer that contraction and on which to print the piece. The disadvantage of using the "raft" is that this first layer will have a less smooth.
It is advisable to lower the density of "infill" parameter for the part to store less heat. As for the "brim" (the membrane that is created around the piece) parameter is recommended to set it to never greater thicknesses of 5mm to help the first layer will not peel.

As for the interior temperature where printed it is recommended to be controlled and no drafts.