Carbon Fiber PLA Proto-Pasta

FC-PROTO-PASTA-BLACK-175-500
44.95 € 44.95 €
Tax excl.
Diameter
Format
Colour
Quantity

In stock 8 units available for immediate shipping.
units available for shipping in 0 - 0 days
Available for shipment within 0 - 0 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Monday 7 October

The Carbon Fiber PLA filament is a material composed of a matrix of PLA polymer (85 - 90 %) and carbon fibres (10 - 15 %).

It is a synthetic fibre made up of very fine filaments composed almost entirely of carbon atoms.These filaments are so fine that several thousand of them have to be assembled to form a single carbon fibre. These carbon fibres are made from polyacrylonitrile.

Carbon fiber reinforcement improves the overall mechanical properties of the base plastic. In this case, a much stiffer PLA filament is achieved at the cost of less flexibility, which makes this material ideal for making parts that are not intended to bend, such as supports, tools, propellers or drone housings or similar.

This carbon fiber filament stiffness provides excellent structural strength and good inter-layer bonding with very low distortion.

PLA Carbon FiberPLA Carbon Fiber

Image 1:  PLA Carbon Fiber filament. Source: Proto-Pasta.

PLA (polylactic acid) is a biodegradable plastic obtained from natural resources, in particular from starch extracted from corn, beet and wheat.

PLA is one of the most widely used materials in 3D printing today because it does not give off harmful gases and is easy to print on. The ease of use of this material derives from several factors:

  1. It does not require hot bed, although if available, it is recommended to use it at about 60 ºC.
  2. It is generally printed at low temperatures (between 190ºC and 220ºC).
  3. It is a material with almost no warping (warping is the deformation of the pieces with respect to the base).

Thanks to the high percentage of PLA contained in the Carbon Fiber PLA filament, this material is very easy to print even using standard PLA configurations and without the need for a hot bed. Therefore, PLA with Carbon Fiber is compatible with most 3D FDM printers on the market.

Pieza impresa con PLA Fibra de carbono gris claro.

Image 2: Piece printed in 3D with PLA Light Grey Carbon Fiber filament. Source: Proto-Pasta.

Carbon fiber particles are abrasive particles, so they can wear out and damage the brass nozzle over time. For this reason, we recommend using a hardened steel nozzle, Nozzle XOlsson Ruby or 3D Solex NozzlesEverlast.

For this type of filament with fibers, it is recommended to use nozzles with an output diameter of at least 0.5 mm to avoid possible clogging and printing errors. In the case of carbon fiber PLA, success tests have been conducted with 0.5 mm nozzles and direct extrusion system.

As for the finish of this filament, it has a matt finish with a slight gloss due to the embedded carbon fibers.

General information

Material PLA
Format 125 g / 500 g
Density 1.15 g/cm³
Filament diameter 1.75 / 2.85 mm
Filament tolerance ± 0.05 mm
Filament length (Ø1.75 mm - 0.125 Kg) ± 45 m / (Ø1.75 mm - 0.5 Kg) ± 180 m / (Ø 2.85 mm - 0.125 Kg) ± 17 m / (Ø 2.85 mm - 0.5 Kg) ± 68 m

Printing properties

Printing temperature 195 - 225 ºC
Print bed temperature 50 - 60 ºC
Chamber temperature
Cooling fan
Recommended printing speed 20 - 40 mm/s

Mechanical properties

Elongation at break - %
Tensile strength - MPa
Tensile modulus - MPa
Flexural strength - MPa
Flexural modulus - MPa
Surface hardness -

Thermal properties

Melting temperature 150 ºC
Softening temperature - ºC

Specific properties

Transparency -

Other

HS Code 3916.9
Spool diameter (outer) 205 mm
Spool diameter (inner hole) 53 mm
Spool width 55 mm

The print is recommended to clean the nozzle by passing through it PLA or ABS to avoid leaving traces of carbon fiber in it. Carbon Fiber PLA in filament state is more fragile than the standard PLA so must be handled carefully to avoid breakage. Optimum printing temperature can range between 195ºC and 220ºC according to each 3D printer.

Printing of this filament is just as easy to standard PLA. Although it is not necessary to have a warm bed to print this filament, if she have put it at 50-60 ° C it is recommended. The adhesion of the first layer is key and probably the most important factors for good impressions. so you can use Magigoo, BuildTak or 3DLac.

Featured properties

Printing temperature
195 - 225 ºC
Filament diameter
1.75 / 2.85 mm
Density
1,15 g/cm³