Panchroma PLA Luminous

Ref.: PCHR-PLA-LUMIN-BLUE-175-1000

24.79 €

Tax excl.

Diameter

Format

Colour

Volume discounts

Quantity	Discount	Price
5	5% 5%	23.55 € 23.55 €
10	8% 8%	22.81 € 22.81 €

Quantity

In stock 7 units available for immediate shipping.
units available for shipping in 15 - 21 days Available for shipment within 15 - 21 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Monday 21 July

Available

Returns

Ask about this product

The PLA Luminous filament from the Panchroma collection offers a fascinating dual effect: it displays a unique color in daylight, then glows in a similar hue when in the dark. This captivating glow is achieved by combining the base polymer with phosphorescent materials that absorb light and gradually release it, creating a soft, glowing effect in low light or complete darkness. Due to the inclusion of these phosphorescent materials, a hardened nozzle is recommended to avoid wear from the slightly abrasive components of the filament.

The PLA Luminous filament in light vs. dark

Image 1: The PLA Luminous filament in light vs. dark. Source: Panchroma.

Panchroma is a family of specially engineered polymer compounds that incorporate PLA. Each filament formulation is meticulously fine-tuned for its specific color and surface finish, ensuring the highest aesthetic quality and printability. These formulations can be reliably printed on any FFF/FDM 3D printer using typical PLA settings, providing both versatility and consistent results for a wide range of projects.

Objects printed with the PLA Luminous filament in light vs. dark

Image 2: Objects printed with the PLA Luminous filament in light vs. dark. Source: Panchroma.

For optimal results, PLA Luminous should be printed at an extrusion temperature between 190-230 ºC and a bed temperature of 25-60 ºC. The PLA Luminous filament supports a maximum printing speed of 200 mm/s, offering flexibility for a variety of print setups. While the spool will spin smoothly in the AMS, the filament’s abrasive nature may cause wear on the gears and PTFE tube over time. Therefore, the manufacturer recommend against using PLA Luminous with the Bambu Lab AMS to prevent premature wear and tear.

General information
Material	PLA
Format	1 kg
Density	1.19 g/cm³
Filament diameter	1.75 mm
Filament tolerance	±0.03 mm
Filament length	±349.4 m

Printing properties
Printing temperature	190 - 230 ºC
Print bed temperature	25 - 60 ºC
Chamber temperature	✗
Cooling fan	✓
Recommended printing speed	Max. 200 mm/s
Recommended nozzle	Hardened Steel

Mechanical properties
Charpy impact strength	(ISO 179) 3.3 ± 0.2 KJ/m²
Elongation at break	2 %
Tensile strength	(ISO 527) XY: 52.3 ± 0.3 MPa / Z: 40.5 ± 0.5 MPa
Tensile modulus	(ISO 527) XY: 3427 ± 65 MPa / Z: - MPa
Flexural strength	39 MPa
Flexural modulus	2700 MPa
Surface hardness	-

Thermal properties
Softening temperature	(ISO 306) 63 ºC

Other
HS Code	3916.9
Spool diameter (outer)	200 mm
Spool diameter (inner hole)	55 mm
Spool width	65.6 mm

Like any 3D printing filament, the Panchroma PLA filaments should be stored properly in order to avoid their deterioration and, in consequence, extrusion problems and inferior print quality. The spool can be stored in an airtight plastic bag, in a resealable bag with a desiccant capsule, or in a smart filament container. If the filament has absorbed too much moisture, it must be dried before printing in a filament dryer for 6 hours at 55 ºC or in the PolyDryer solution. The recommended settings are setting 1 for Panchroma PLA Silk and others, and settings 1-3 for PLA Matte and Satin.

The Panchroma PLA filaments should be extruded at a temperature of 190-230 ºC on a bed heated to 25-60 ºC. It is recommended to use the cooling fan at 100% but a printer with a heated chamber is not needed. As far as the printing speed, it is recommended to use max. 200 mm/s for the PLA Silk and other Panchroma PLA varieties, max. 300 mm/s for the PLA Satin and Matte PLA, and max. 400 mm/s for CoPE.

Complex parts can be 3D printed with the Panchroma PLA filaments with the help of support filaments such as the PolySupport filament or the PolyDissolve S1 filament.

Panchroma PLA Glow and Panchroma PLA Luminous are glow-in-the-dark materials enriched with an abrasive additive, making a hardened nozzle essential for printing. These filaments should not be used in AMS systems with plastic gears or tubes due to their abrasive nature.

Extra Tools to Enhance the Printing Experience

To further facilitate the 3D printing experience, support tools such as app.polymaker.com, an interactive comparison tool for mechanical, technical, and color properties among different filaments, and wiki.polymaker.com, a quick and comprehensive guide on using our products and 3D printing recommendations, can be utilized.