PolyCore TPU-2000 pellets

Ref.: POLY-PELLETS-TPU2000-25KG

383.99 €

Tax excl.

Format

Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 15 - 21 days Available for shipment within 15 - 21 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Friday 24 January - Monday 3 February

Available

Returns

Ask about this product

TPU, or Thermoplastic Polyurethane, is a versatile and popular material for 3D printing. Known for its flexibility and durability, TPU offers a unique combination of properties that make it ideal for producing flexible and rubbery parts. It has excellent layer adhesion, making it easy to print with minimal warping.

The PolyCore TPU-2000 pellets by Polymaker are a material with a Shore hardness of 95 A. They were developed specially for MAAM (Middle Area Additive Manufacturing) and can be extruded with the help of equipment such as the CEAD AM Flexbot, the CEAD E25 extruder, the Mahor V4 pellet extruder, or the Dyze Pulsar extruder.

TPU is resistant to abrasion and chemicals, making it suitable for a wide range of applications, including custom gaskets and seals, commodity articles such footwear, and even prosthetics. TPU's ability to withstand repeated bending and stretching, along with its low friction coefficient, makes TPU an excellent choice for creating functional, impact-absorbing, and wearable 3D-printed items.

General information
Manufacturer	Polymaker
Material	TPU/TPE
Format	25 kg
Density	1.3 g/cm³

Mechanical properties
Elongation at break	(ASTM D638) (XY) 558.5 ± 57.8 %
Tensile strength	(ASTM D638) (XY) 36.9 ± 3.2 MPa
Tensile modulus	(ASTM D638) (XY) 12.3 ± 0.3 MPa
Flexural strength	- MPa
Flexural modulus	- MPa
Surface hardness	(ASTM D2240) Shore 95 A

Thermal properties
Melting temperature	187 ºC
Softening temperature	- ºC
Processing temperature	205-215 ºC
MFR Ratio	(@ 230 ºC, 2.16 kg) 5.6 g/10 min
Glass transition temperature	- ºC
Heat deflexion temperature	- ºC

Other
HS Code	3901.1

Proper storage of 3D printing materials is crucial for smooth extrusion and high surface quality and mechanical properties of the 3D printed part. PolyCore TPU-2000 pellets should be stored in a sealed package under dry conditions at a temperature below 50°C, protected from UV light at all times. If the pellets absorb excess moisture, they should be dried for 12 hours at 70°C. The recommended processing temperature for PolyCore TPU-2000 pellets is 205 to 215°C.