XVN-50 resin - AmeraLabs

Name: XVN-50 resin - AmeraLabs
Brand: AmeraLabs
SKU: RS-AMERA-XVN50
Price: 74.00 EUR
Availability: InStock

Ref.: RS-AMERA-XVN50-BLACK-1000

74.00 €

Tax excl.

Format: 1 Kg

Type of resin: Black

Volume discounts

Buy 10 units

Save 10%

666.00 € Tax excl. Unit price 66.60 € 74.00 €

Buy 15 units

Save 12%

976.80 € Tax excl. Unit price 65.12 € 74.00 €

Quantity

In stock 4 units available for immediate shipping.
units available for shipping in 5 - 8 days Available for shipment within 5 - 8 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Tuesday 19 May

Returns

Ask about this product

The XVN-50 resin by AmeraLabs is a versatile 3D printing material designed for a wide range of engineering and industrial applications, including prototypes, jigs, fixtures, tooling, robotic components, and end-use parts. It offers an excellent balance of durability, flexibility, and precision, making it an ideal choice for reliable, highly detailed prints.

The new Matte Black formulation maintains the same mechanical properties and printing parameters as the previous version, so no changes to settings or existing workflows are required. This update enhances the visual finish of printed parts, delivering cleaner, smoother, and more uniform surfaces, along with more consistent pigmentation in an elegant deep matte black color.

Thanks to this improvement, models printed with XVN-50 resin achieve a more refined and professional finish while preserving the reliable performance and mechanical properties that define this resin. It is an ideal solution for functional engineering parts, detailed prototypes, and applications that require precision and strength.

Video 1: XVN-50 resin for engineering applications. Source: AmeraLabs.

The resin is compatible with MSLA 3D printers equipped with monochrome LCD and DLP technologies within the 365-420 nm UV wavelength range, such as the Phrozen Sonic Mini 8K or Elegoo Saturn 3 Ultra and similar devices. Specific printer settings for optimal performance can be found on the AmeraLabs website.

Image 1: Comparison between the new and old XVN-50 resin formulas. Source: AmeraLabs.

One of the key features of XVN-50 resin is its hard and glossy surface (82 Shore D), which enables precise dimensional replication with sharp, straight edges. This resin is engineered to produce dimensionally accurate and stable parts that resist cracking and warping caused by shrinkage. In addition, it provides a well-balanced combination of flexibility, stiffness, impact resistance, and tensile strength, making it ideal for demanding engineering applications.

The new formulation preserves these mechanical and strength properties, ensuring the same reliable behavior during printing and end-use performance, now enhanced with a uniform matte black aesthetic.

Comparison between finishes of the new and old formula.

Image 2: Comparison between finishes of the new and old formula. Source: AmeraLabs.

XVN-50 resin is easy to use, offering excellent printability, strong build plate adhesion, low odor, and stable pigment dispersion. Post-processing is straightforward; the resin cures quickly, does not remain sticky, and feels pleasant to the touch. 3D printed parts made with XVN-50 resin are easy to modify through drilling, cutting, threading, sanding, and painting for a professional-quality finish.

The improved pigment consistency also helps achieve parts with a more homogeneous and professional appearance, especially for technical models, visual prototypes, and functional components.

Browse our catalog of resin post-processing accessories to find the right tools. With a medium viscosity of 560 cPs, cleaning parts before post-curing is simple, ensuring all the original model features are preserved. More printing and post-processing tips, as well as technical information about XVN-50 resin, can be found in the Usage Tips section.

General information
Manufacturer	AmeraLabs
Material	Photopolymer
Format	0.5 L / 1 L / 5 L
Density	1.09 g/cm³
Technology	SLA / LED-LCD / DLP
Wavelength	365-420 nm
Viscosity	(ISO 2555 @ 25 °C) 560 mPa·s MPa
Maximum water absorption	(ASTM D570, 24 h) 3.12 %

Printing properties
Layer height	- µm
Layer exposure time	-
Layer off time	-
Bottom layer exposure	-
Bottom layer count	-

Curing and washing properties
Washing time	15 min
Curing time	5-60 min
Curing temperature	- ºC

Mechanical properties (uncured / cured)
Izod impact strength	(ASTM D256) 5.9 KJ/m²
Charpy impact strength	- KJ/m²
Elongation at break	(ISO 527) 51.2 %
Tensile strength	(ISO 527) 43.4 MPa
Tensile modulus	(ISO 527) 2030 MPa
Flexural strength	(ISO 178) 62.3 MPa
Flexural modulus	(ISO 178) 1820 MPa
Surface hardness	(ASTM D2240) Shore 82 D

Thermal properties (uncured / cured)
Softening temperature	(ASTM D1525) 65.2 ºC

Other
HS Code	2916.1
Lifetime (since manufacturing)	- M

printing

for those who are only beginning their adventure with resin 3d printing, we recommend reading the beginner's guide to ameralabs resins as well as referring to the troubleshooting guide prepared by ameralabs in case any problems occur while 3d printing with the xvn-50 resin.

it is crucial that the xvn-50 is not used with pdms-based resin trays due to its high reactivity, which can harm the pdms silicone layer. it is highly recommended to use this resin exclusively with resin trays with fep, nfep, pfa, or acf films.

detailed information on the printing and post-processing workflow with the xvn-50 resin can be found in the product’s technical datasheet in the attachments section as well in this blog post on the manufacturer’s website.

post-processing

parts 3d printed with the xvn-50 resin will achieve their specific properties only after being subjected to post-processing by washing and curing.

washing

ameralabs recommends using ipa alcohol for the washing and the washing time will largely depend on the washing equipment used. if a washing station is used, the average washing time is 15 minutes and a second wash of 10 minutes if required. if an ordinary bucket system and manual cleaning are used, the parts should be submerged for 10 minutes, swirled for 1 minutes, submerged for another 10 minutes in ipa, and swirled again for 1 minutes. if an ultrasonic cleaner is used, it is recommended not to go over 20 minutes of cleaning.

post-curing

once washed, the parts 3d printed with the xvn-50 resin must be dried and cured immediately either with the help of a curing station (with our without supports). the recommended curing times will depend on the used equipment but can range from anywhere between 5 to 60 minutes. the rule of thumb is that parts should be cured until not sticky anymore and until the surface is very hard to scratch.

safety

certain precautions must be taken when working with 3d printing resins. the user must ensure that the working space is adequately ventilated, and that protective gear such as goggles, gloves and garments are worn at all times. the xvn-50 resin should be stored in a tightly closed container/resin vat to avoid resin deterioration due to uv exposure. the container/vat should be kept in a cool, well ventilated area away from heat, sparks and open flame. to get a better idea of how to work with the ameralabs resins safely, please read the manufacturer's blog post on the most common resin safety myths.