IND405 HDT50 High Elongation resin - Loctite 3D

Compare

You must be logged in to manage your wishlist.

IND405 resin - Loctite 3D

Ref.: RS-LOC-IND405-HDT50-CLEAR-1KG

180.00 €

Tax excl.

Format

Colour

Quantity

In stock 7 units available for immediate shipping.
units available for shipping in 5 - 7 days Available for shipment within 5 - 7 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Thursday 26 December

Available

Returns

Ask about this product

The IND405 HDT50 High Elongation resin from the Loctite family of high impact resistant resins is a rigid and tough material for the 3D printing of parts with high elongation at break and excellent impact resistance, as well as an excellent surface finish. The properties of this resin are comparable to those of polypropylene (PP).

The IND405 HDT50 High Elongation resin is the perfect material for the additive manufacturing of production floor tools, fixtures, jigs, aids, housings and much more. The clear resin is ideal for clear prototypes, offering a high level of translucency for the demonstration of internal features (fluid routing, consumer goods). Parts printed with the IND406 HDT100 resin can be further post-processed by machining, tapping or polishing.

A part 3D printed with the Loctite IND405 HDT50 High Elongation resin

Image 1: A part 3D printed with the Loctite IND405 HDT50 High Elongation resin. Source: Loctite.

The IND405 HDT50 High Elongation resin has been formulated to print optimally on industrial DLP printers. Before printing with this material, the user should read safety and technical information available in the Downloads section. In the Usage Tips section useful resources can be found on printer compatibility, recommended post-processing settings, and proper resin storage.

Curing, washing, and sintering properties
Washing time	2.5 min
Curing time	10 - 20 min
Curing temperature	- ºC

General information
Manufacturer	Loctite
Material	Photopolymer
Format	1 kg / 5 kg
Technology	DLP/LCD
Wavelength	- nm
Viscosity	(ASTM D7867) @ 25 ºC: 2200-2400 cP
Density (solid)	(ASTM D1475) 1.121 g/cm³
Density (liquid)	(ASTM D1475) 1.046 g/cm³

Printing properties
Layer height	- µm
Layer exposure time	-
Layer off time	-
Lifting height	- mm
Bottom layer exposure	-

Mechanical properties
Izod impact strength	- KJ/m²
Charpy impact strength	- KJ/m²
Elongation at break	(ASTM D638) 101 ± 4 %
Tensile strength	(ASTM D638) 45 ± 2 MPa
Tensile modulus	(ASTM D638) 1434 ± 80 MPa
Flexural strength	- MPa
Flexural modulus	(ASTM D790) 1383 ± 63 MPa
Surface hardness	(ASTM D2240) Shore 76 D

Electrical properties
Volumetric resistivity	(ASTM D2240) 2.75E +15 Ω/cm
Surface electrical resistivity	(ASTM D2240) 7.79E +15 Ω
Dielectric strength	(ASTM D149) 24.9 kV/mm
Permittivity	(ASTM D150) 3.6-4.7

Thermal properties
Softening temperature	- ºC
Heat deflexion temperature	(ASTM D648) @ 0.45 MPa: 52.8 ºC / @ 1.82 MPa: 43.4 ºC
Thermal expansion coefficient	(ASTM E831) -30°C - 45°C: 98.47 µm/(m·K)
Vulcanisation temperature	(ASTM D150) 0.014-0.150 ºC

Specific properties
Maximum water absorption	24 h: 1 %

Other
HS Code	2916.1
Lifetime (since manufacturing)	- M

On the Henkel YouTube channel, various videos are available on:

How to work with 3D printing resins:
Video 1: The basics of printing with resin. Source: Henkel.
How to properly store 3D printing resins:
Video 2: How to properly store resins. Source: Henkel.
How to post-process parts 3D printed with resin:
Video 3: Resin post-processing tips. Source: Henkel.

The material's technical and safety datasheets can be found in the Downloads section. On the manufacturer's website the user can find the printer validation information as well as the recommended printing and postprocessing settings.