Tarfuse POM NAT filament
search
  • Tarfuse POM NAT filament
Compare
You must be logged in to manage your wishlist.

Tarfuse POM NAT filament

TARFUSE-POM-NATURAL-175-1000
44.95 € 44.95 €
Tax excl.
Diameter
Format
Colour
Quantity

In stock 7 units available for immediate shipping.
units available for shipping in 0 - 0 days Available for shipment within 0 - 0 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Tuesday 26 November
Available

Tarfuse POM NAT is 3D printing material developed and manufactured by Grupa Azoty. POM NAT belogs to their portfolio of technical filaments for advanced applications. The POM NAT filament is a polyacetal copolymer material (also known as polyoxymethylene, acetal or polyformaldehyde) characterized by high mechanical strength and excellent tribological parameters. This filament was specially designed for the additive manufacturing of functional technical parts that are required to work in high friction environments (parts up to 100 mm).

Parts 3D printed with the Tarfuse POM NAT filament exhibit a wide range of outstanding mechanical properties: negligible change in impact toughness in the temperature range -40 ºC to 110 ºC, exceptional mechanical strength and stiffness, high resistance to fatigue, and excellent dimensional stability. Furthermore, POM NAT offers elevated chemical resistance to most organic solvents, bases and acids up to pH> 4, high resistance to water, bacteria, fungi and insects. This filament is also user-friendly and safe to use since it does not emit toxic gases during the 3D printing process.

General information
Material POM
Format 1 kg
Density 1.42 g/cm³
Filament diameter 1.75 mm
Filament tolerance ± 0.05 mm
Filament length ±292.8 m

Printing properties
Printing temperature 210 - 240 ºC
Print bed temperature 100 - 130 ºC
Chamber temperature 70 - 140 ºC
Cooling fan -
Recommended printing speed 10 - 30 mm/s

Mechanical properties
Elongation at break (ISO 527-1,-2) XY: 11 %
Tensile strength (ISO 527-1,-2) XY: 50 MPa
Tensile modulus (ISO 527-1,-2) XY: 1870 MPa
Flexural strength - MPa
Flexural modulus - MPa
Surface hardness -

Thermal properties
Melting temperature (ISO 11357-1-3) 165 - 170 ºC
Softening temperature - ºC

Specific properties
Chemical resistance ✓

Other
HS Code 3916.9
Spool diameter (outer) - mm
Spool diameter (inner hole) - mm
Spool width - mm

The spool should be stored properly to avoid potential printing and part quality issues. It is recommended to store the spool in a tightly sealed plastic bag with a desiccant or in an intelligent filament container. In case the filament absorbs moisture, it should be dried for 4-6 hours at 140 ºC.

This material should be printed at a temperature of 210-240 °C on a bed heated to 100-130 °C. The recommended chamber temperature is 70-140 ºC and the optimum printing speed is 10-30 mm/s. The recommended bed material is PI with Dimafix or a cellulose mat (paper, wood, cork) with PVA adhesive.

Featured properties

Printing temperature
210 - 240 ºC
Filament diameter
1.75 mm
Density
1,42 g/cm³