PolyCore ABS-5012 pellets
search
  • PolyCore ABS-5012 pellets
  • PolyCore ABS-5022 pellets
Compare
You must be logged in to manage your wishlist.

PolyCore ABS pellets

POLY-PELLETS-ABS5012-25KG
218.75 € 218.75 €
Tax excl.
Format
Material
Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 15 - 21 days Available for shipment within 15 - 21 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Thursday 23 January - Friday 31 January
Available

The PolyCore ABS pellets by Polymaker are available in a 20 % glass fiber blend as ABS-5012 or a 20 % carbon fiber composite - ABS-5022.

Both varieties were developed specially for BAAM (Big Area Additive Manufacturing) and can be extruded with the help of equipment such as the CEAD AM Flexbot, the CEAD E25 extruder, the Mahor V4 pellet extruder, or the Dyze Pulsar extruder.

Both varieties of the PolyCore ABS pellets offer cost effectiveness and great printability, and are a great material for molding and tooling at low to middle temperatures. The PolyCore ABS-5012 pellets are ideal for the additive manufacturig of architecture molds and general prototyping.

Thanks to the carbon fiber included in their formula, the Polycore ABS-5022 pellets additionally demonstrate great mechanical properties, dimensional stability, and high thermal conductivity (low coefficient of thermal expansion). This makes the PolyCore ABS-5022 pellets suitable for applications that require thermal resistance and durability, for example low-to-middle temperature composite tooling or marine prototyping.  

General information
Manufacturer Polymaker
Material ABS
Format 25 kg
Density 1.2 g/cm³

Mechanical properties
Charpy impact strength (ASTM D256) ABS-5012: 9.2 ± 0.2 kJ/m² / ABS-5022: 9.5 ± 0.6 KJ/m²
Elongation at break (ASTM D638) ABS-5012: 2.3 ± 0.1 % / ABS-5022: 2.2 ± 0.2 %
Tensile strength (ASTM D638) ABS-5012: 90.6 ± 0.9 MPa / ABS-5022: 132.2 ± 2.0 MPa
Tensile modulus (ASTM D638) ABS-5012: 7343 ± 158 MPa / ABS-5022: 11515 ± 224 MPa
Flexural strength (D790) ABS-5012: 119.3 ± 2.7 MPa / ABS-5022: 185.7 ± 3.8 MPa
Flexural modulus (D790) ABS-5012: 6328 ± 317 MPa / ABS-5022: 9574 ± 277 MPa
Surface hardness -

Thermal properties
Melting temperature 220 ºC
Softening temperature - ºC
Processing temperature 230-240 ºC
MFR Ratio (@ 220 ºC, 10 kg) ABS-5012: 12.7 g/10 min / ABS-5022: 11 g/10 min
Glass transition temperature - ºC
Heat deflexion temperature - ºC

Other
HS Code 3901.1

Proper storage of 3D printing materials is key to smooth extrusion and high surface quality and mechanical properties of the 3D printed part. PolyCore ABS pellets should be stored in a sealed package under dry conditions at a temperature below 50°C, protected from UV light at all times. If the pellets absorb excess moisture, they should be dried for 3-4 hours at 80°C. The recommended processing temperature for PolyCore ABS pellets is 210 to 230°C.