Ref.: KAI-PELLETS-PWD-ABS-NATURAL-1KG

28.00 €

Tax excl.

Format

Colour

Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 0 - 0 days Available for shipment within 0 - 0 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Out of Stock

Returns

Ask about this product

These ABS pellets by Kai Parthy are an FGF 3D printing material to be used for direct extrusion or filament production. The Kai Parthy ABS pellets have a natural color and are made from the Terez 5010 ABS as the base material. The ABS pellets have a tensile strength of 46.3 MPa and a Vicat softening temperature of 97 ºC.

Along with PLA, ABS is one of the most common 3D printing materials. It is characterized by great mechanical strength, chemical resistance and resistance to high as well as low temperatures. Colorants can be added directly to the Kai Parthy ABS pellets to achieve personalized colors of the 3D printed parts or the fabricated filament.

The pellets have a powdery appearance due to their small particle size

Image 1: The pellets have a powdery appearance due to their small particle size. Source: Filament2Print.

A unique feature of this material is the very small particle size of 0.10-0.50 mm, which makes the pellets look like powder. Nevertheless, these ABS pellets are meant for FGF 3D printing and cannot be used on SLS 3D printing equipment at the risk of damaging the SLS 3D printer.

The best equipment for the processing of the Kai Parthy ABS pellets is the Mahor V4 pellet extruder or the Tumaker 3D printers for direct extrusion. It is also possible to make filament from the ABS pellets with the help of the Felfil EVO extruder.

General information
Manufacturer	Lay Filaments
Material	ABS
Format	1 kg
Density	1.05 g/cm³
Average granulation	0.10-0.50 mm

Mechanical properties
Charpy impact strength	(ISO 179/1eA) @ +23 ºC: 19 kJ/m² / @ -30 ºC: 10 KJ/m²
Elongation at break	(ISO 527) 2.4 %
Tensile strength	(ISO 527) 46.3 MPa
Tensile modulus	(ISO 527) 2200 MPa
Flexural strength	- MPa
Flexural modulus	(ISO 178) 2300 MPa
Surface hardness	-

Thermal properties
Melting temperature	- ºC
Softening temperature	(ISO 306) 97 ºC
Processing temperature	220 ºC
MFR Ratio	-
Glass transition temperature	- ºC
Heat deflexion temperature	- ºC

Specific properties
Chemical resistance	✓

Other
HS Code	3901.1

It is very important to store ABS pellets in an airtight bag to prevent them from absorbing moisture from the environment before use. If the pellets have moisture in them, the resulting parts or filament may contain small imperfections. Once the filament has been manufactured using ABS pellets, it is also recommended to store the filament properly.