IND405 HDT50 High Elongation resin - Loctite 3D

Reference:

Brand: Loctite

Condition: New product

10 Item Items

Format

Colour

Quantity

180,00 €

Ask for information

Resin for rigid and tough parts with high elongation at break and great surface finish.

Add to wishlist

More info
Data sheet
Download
Usage tips
Specifications

The IND405 HDT50 High Elongation resin from the Loctite family of high impact resistant resins is a rigid and tough material for the 3D printing of parts with high elongation at break and excellent impact resistance, as well as an excellent surface finish. The properties of this resin are comparable to those of polypropylene (PP).

The IND405 HDT50 High Elongation resin is the perfect material for the additive manufacturing of production floor tools, fixtures, jigs, aids, housings and much more. The clear resin is ideal for clear prototypes, offering a high level of translucency for the demonstration of internal features (fluid routing, consumer goods). Parts printed with the IND406 HDT100 resin can be further post-processed by machining, tapping or polishing.

A part 3D printed with the Loctite IND405 HDT50 High Elongation resin

Image 1: A part 3D printed with the Loctite IND405 HDT50 High Elongation resin. Source: Loctite.

The IND405 HDT50 High Elongation resin has been formulated to print optimally on industrial DLP printers. Before printing with this material, the user should read safety and technical information available in the Downloads section. In the Usage Tips section useful resources can be found on printer compatibility, recommended post-processing settings, and proper resin storage.

Elongation at break (%)	101
Tensile strength (MPa)	45
Tensile modulus (MPa)	1434
Flexural modulus (MPa)	1383
Surface hardness	8

On the Henkel YouTube channel, various videos are available on:

How to work with 3D printing resins:

Video 1: The basics of printing with resin. Source: Henkel.
How to properly store 3D printing resins:

Video 2: How to properly store resins. Source: Henkel.
How to post-process parts 3D printed with resin:

Video 3: Resin post-processing tips. Source: Henkel.

The material's technical and safety datasheets can be found in the Downloads section. On the manufacturer's website the user can find the printer validation information as well as the recommended printing and postprocessing settings.

General information
Manufacturer	Loctite
Technology	DLP
Material	Photopolymer
Wavelength	-
Format	1 kg 5 kg
Color	Black Clear
Compatible 3D printers	DLP
Printing properties
Layer height	-
Layer exposure time	-
Layer cooling time	-
Lifting height	-
Exposure of lower layers	-
Number of bottom layers	-
Curing and washing properties
Washing time	2.5 min
Curing time	10-20 min
Curing temperature	-
Mechanical properties
Izod impact resistance (ASTM D256)	51 ± 4 J/m
Charpy impact resistance	-
Elongation at break (ASTM D638)	101 ± 4 %
Tensile strength (ASTM D638)	45 ± 2 MPa
Tensile modulus (ASTM D638)	1434 ± 80 MPa
Bending strength	-
Bending modulus (ASTM D790)	1383 ± 63 MPa
Surface hardness (ASTM D2240)	Shore 76 D
Thermal properties
Softening temperature	-
Brightness value	-
Electrical properties
Dielectric strength (ASTM D149)	24.9 kV/mm
Volumetric strength (ASTM D257)	2.75E+15 Ω·cm
Surface resistance (ASTM D257)	7.79E+15 Ω
Additional information
Service life	-
HS Code	2916.1

* The typical values listed in this table should be considered as a reference. Actual values may vary depending on the 3D printer model used, part design and printing conditions. We recommend confirming the final results and properties with your own tests. For further information please refer to the product data sheet.