Woodfill ColorFabb pellets

Ref.: COLFB-PELLET-WOODFILL-20KG

220.32 €

Tax excl.

Format

Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 5 - 7 days Available for shipment within 5 - 7 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Wednesday 8 January - Friday 10 January

Available

Returns

Ask about this product

Colour traceability cannot be guaranteed as the shade varies between spools depending on the natural compounds used in each production process.

The Woodfill pellets are a material from the ColorFabb portfolio. They are made of 70 % PLA/PHA and 30 % recycled wood fiber. The base of these pellets, PLA/PHA, is a mix of PLA (polylactic acid) with PHA, also known as polyhydroxyalkanoates. It is a bio-polyester produced in nature by the action of bacteria by fermentation of sugar or lipids, and also a biodegradable plastic used in the production of biopolymers. PLA/PHA demonstrates greater strength than pure PLA.

Part 3D printed with the Woodfill material

Image 1: Part 3D printed with the Woodfill material. Source: ColorFabb.

The Woodfill pellets will emit a pleasant wood smell during 3D printing and the 3D printed parts will have a stunning natural surface finish. It must be kept in mind that the color of the pellets may vary between batches due to the nature of the resources used for the production of the pellets.

The Woodfill pellets are perfect for the additive manufacturing of various decorative objects or prototypes with the help of FGF manufacturing solutions such as the CEAD AM Flexbot solution, the CEAD E25 extruder, the Mahor V4 pellet extruder, or the Dyze Pulsar extruder. It is also possible to manufacture personalized 3D printing filament from the Woodfill pellets with the help of the Felfil ecosystem.

General information
Manufacturer	ColorFabb
Material	PLA/PHA
Format	20 kg
Density	1.15 g/cm³

Mechanical properties
Charpy impact strength	(ISO 179) (notched) 4.2 kJ/m² / (unnotched) 19.0 KJ/m²
Elongation at break	(ISO 527) 5.5 %
Tensile strength	(ISO 527) 46 MPa
Tensile modulus	(ISO 527) 3290 MPa
Flexural strength	(ISO 178) 70 MPa
Flexural modulus	(ISO 178) 3930 MPa
Surface hardness	-

Thermal properties
Melting temperature	(ISO 3146) 155 ºC
Softening temperature	- ºC
Processing temperature	170-190 ºC
MFR Ratio	-
Glass transition temperature	- ºC
Heat deflexion temperature	- ºC

Other
HS Code	3901.1

The proper storage of 3D printing materials is key to smooth extrusion, and great surface quality and mechanical properties of the 3D printed part. The ColorFabb Woodfill pellets should be stored in a closed package in dry conditions at temperature below 50 ºC, protected from UV-light at all times. If the pellets absorb excess moisture, they should be dried for 6 hours at 55 ºC (dehumidifying dryer preferred). The recommended processing temperature for the Woodfill pellets is 170-190 ºC.