FTile Silica - Colfeed4Print

Ref.: COLFEED-FTILE-SILICA-175-10M

160.00 €

Tax excl.

Diameter

Format

Quantity

Do you need more than 1 units?
Please, contact us.

In stock 1 units available for immediate shipping.
units available for shipping in 0 - 0 days Available for shipment within 0 - 0 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Monday 18 November

Available

Returns

Ask about this product

The FTile Silica filament by Colfeed4Print is a composite material made up of inorganic silica frit and a PLA matrix. This filament was designed for the additive manufacturing of complex designs that will turn into colored glass glazes after a thermal treatment at 800-900 ºC.

Pattern 3D printed with the FTile Silica filament before firing

Image 1: Pattern 3D printed with the FTile Silica filament before firing. Source: Colfeed4Print.

Frit is a powdered glass material that is used in the creation of ceramic objects via ceramic 3D printing. In the case of the FTile Silica filament by Colfeed4print, the silica frit (silicon dioxide, 40 vol. %) is mixed with high quality biodegradable PLA as the binder to create the FTile Silica filament. During the firing process of the part 3D printed with the FTile Silcia filament, the PLA binder burns away, leaving behind the solidified frit particles fused together to form the final glass object.

Pattern 3D printed with the FTile Silica filament after firing

Image 2: Pattern 3D printed with the FTile Silica filament after firing. Source: Colfeed4Print.

The FTile Silica filament is a great solution for artists and designers who want to create highly customized and complex sculptures, art installations, and decorative objects with glazed ceramic reliefs with a glassy look with the help of additive manufacturing.

General information
Manufacturer	Colfeed4Print
Material	Ceramic + binder
Format	10 m
Density	1.84 g/cm³
Filament diameter	1.75 mm
Filament tolerance	±0.15 mm
Filament length	10 m
Amount of filler (volume)	40 %
Amount of filler (mass)	60 %

Mechanical properties
Elongation at break	- %
Tensile strength	- MPa
Tensile modulus	- MPa
Flexural strength	- MPa
Flexural modulus	- MPa
Surface hardness	-

Printing properties
Printing temperature	165-175 ºC
Print bed temperature	40-80 ºC
Recommended printing speed	10-60 mm/s
Recommended nozzle diameter	Min. 0.4 mm

Thermal properties
Melting temperature	150 ºC
Softening temperature	- ºC

Other
HS Code	3916.9

The FTile Silica filament is delivered in a vacuum sealed bag with desiccant. Once opened, the filament should be stored properly to prevent it from absorbing moisture from the air. The best way to store filaments in a tightly sealed bag with desiccant, in a vacuum sealed container or in an intelligent filament container.

The manufacturer recommends printing the FTile Silica filament at 165-175 ºC on a bed heated to 40-80 ºC at a speed of 10-60 mm/s. More printing tips can be found in the technical datasheet in the Downloads section.

It is highly recommended to wear standard safety equipment during the printing and post-processing of parts 3D printed with the FTile Silica filament - safety goggles, gloves, breathing equipment and protective garments, according to needs.