PPS-CF - Bambu Lab

Name: PPS-CF - Bambu Lab
Brand: Bambu Lab
SKU: BL-PPS-CF
Price: 110.74 EUR
Availability: InStock

SKU: BL-PPS-CF-BLACK-175-750

110.74 €

Tax excl.

Diameter: 1.75 mm

Format: Spool 750 g

Colour: Black

Ver todas las opciones

Quantity

In stock 35 units available for immediate shipping.
units available for shipping in 10 - 15 days Disponible a partir de Available for shipment within 10 - 15 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Wednesday 15 July

Returns

Ask about this product

The PPS-CF filament from Bambu Lab, compatible only with X1E and H2D printers, is a carbon fiber-reinforced polyphenylene sulfide composite designed to meet the most demanding needs of professional 3D printing. Its formula combines the thermal and chemical resistance of PPS with the rigidity of carbon fiber, offering superior mechanical properties, excellent dimensional stability, and durability, making it the ideal choice for critical industrial applications.

Parts printed with Bambu PPS-CF filament

Photo 1: Parts printed with Bambu PPS-CF filament. Source: Bambu Lab

Ultra-High Thermal Resistance

This filament reaches a heat deflection temperature of up to 264 °C at 0.45 MPa, allowing continuous operation above 200 °C. Unlike materials such as PA-CF, limited to 190 °C or lower, PPS-CF delivers exceptional performance in industrial environments where heat resistance and stability under continuous load are essential.

Filament	Heat Deflection Temp / ℃ (0.45 MPa)
PLA Basic	57 ℃
ABS	87 ℃
PC	117 ℃
PA-CF	184 ℃
PA6-CF	186 ℃
PET-CF	205 ℃
PPA-CF	227 ℃
PPS-CF	264 ℃

Superior Fire Resistance

The PPS-CF filament is UL-94 V-0 certified, ensuring outstanding flame resistance. This makes it safe and reliable for electronics and automotive sectors, where fire protection is a critical requirement.

Unmatched Mechanical Properties

The combination of PPS and carbon fiber results in a filament with high stiffness, flexural and tensile strength, and excellent dimensional stability. This prevents deformation in large prints, delivering precise parts that meet the highest industrial standards.

Property	PET-CF	PPS-CF	Improvement %
Stiffness (Flexural Modulus - XY, dry)	5320 MPa	7160 MPa	+34.59%
Strength (Flexural Strength - XY, dry)	131 MPa	142 MPa	+8.40%

Chemical and Solvent Resistance

PPS-CF offers excellent resistance to solvents and chemicals, second only to PTFE. It is virtually insoluble in any solvent below 200 °C and maintains integrity against acids, bases, and salts under normal conditions, making it ideal for industrial environments where chemical stability is essential.

Minimal Moisture Absorption

With a water absorption rate of just 0.05%, PPS-CF retains its thermal and mechanical properties even in humid environments. Unlike conventional PA-CF, which softens and loses performance, this material preserves its strength and durability, ensuring consistent, reliable results.

Conclusion

The carbon fiber-reinforced PPS-CF filament is one of the most advanced solutions for professional 3D printing. Its heat resistance, fire certification, high-level mechanical properties, chemical stability, and low moisture absorption make it a benchmark material for industrial sectors requiring quality, safety, and precision.

Parts printed with Bambu PPS-CF filament

Photo 2: Parts printed with Bambu PPS-CF filament. Source: Bambu Lab

General information
Material	PPS CF
Format	750 g
Density	(ISO 1183) 1.26 g/cm³
Filament diameter	1.75 mm
Filament tolerance	± 0.05 mm
Filament length	247.5 m

Printing properties
Printing temperature	310 - 340 ºC
Print bed temperature	100 - 120°C
Chamber temperature	60 - 90°C
Cooling fan	0-40%
Recommended printing speed	< 100 mm/s
Recommended nozzle diameter	0.4 mm \| 0.6 mm ( recommended) \| 0.8 mm

Mechanical properties
Charpy impact strength	(ISO 179) 6.2 KJ/m²
Elongation at break	(ISO 527) 1.2 %
Tensile strength	(ISO 527) 87 MPa
Tensile modulus	(ISO 527) 8230 MPa
Flexural strength	(ISO 178) 36 MPa
Flexural modulus	(ISO 178) 7160 MPa

Thermal properties
Softening temperature	(ISO 306) 268 ºC

Other
HS Code	3916.9
Spool diameter (outer)	200 mm
Spool width	67 mm

⚠ Usage Precaution

These tips apply only to X1E/H2D printers

1. Printing Temperatures

Nozzle: 310–340 °C.
Chamber: 60–90 °C.
Tip: Higher temperatures improve mechanical properties, especially in the Z direction.

2. Filament Drying

Filament Dryer: 100–140 °C for 8–12 hours.
X1 printer bed: 110–120 °C for 10–12 hours (less effective than an oven).
⚠ Important: Do not exceed 160 °C to avoid damaging the spool.
Tip: Higher temperatures within the drying range produce better results.

3. Filament Storage

Use an airtight container with desiccant during printing to prevent moisture absorption.

4. Post-processing (Annealing)

Check the Technical Data Sheet, available in the Attachments tab, and the Work After Printing Finished section on Bambu Lab Wiki to enhance mechanical properties after printing.