Fiberon PET-CF17 1.75 mm 500 g
search
  • Fiberon PET-CF17 1.75 mm 500 g
  • Fiberon PET-CF17 1.75 mm 3 kg
Compare
You must be logged in to manage your wishlist.

Fiberon PET-CF17

FIBERON-PETCF17-BLACK-175-500
20.65 € 20.65 €
Tax excl.
Diameter
Format
Colour
Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 15 - 21 days Available for shipment within 15 - 21 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Wednesday 8 January - Thursday 16 January
Available

The PET-CF17 filament, a carbon fiber reinforced PET from the Fiberon catalog, is an advanced composite material known for its high modulus, heat resistance, and dimensional stability, making it ideal for demanding engineering applications. Specifically designed for rapid prototyping and functional parts, this filament maintains impressive strength and an outstanding surface finish thanks to the addition of 17% quality carbon fibers. PET-CF17’s moisture resistance further enhances its reliability, ensuring consistent quality and minimal post-processing requirements for complex applications.

Part 3D printed with the PET-CF17 filament

Image 1: Part 3D printed with the PET-CF17 filament. Source: Fiberon.

The PET-CF17 filament balances advanced properties with user-friendly printing characteristics, including low creep and compatibility with high-speed printing up to 300 mm/s. The filament does not require an actively heated chamber, enabling reliable results at room temperature. Optimal for 3D printers built for composite extrusion, such as the Raise3D E2CF or Bambu Lab X1C, PET-CF17 also supports multimaterial systems, like Bambu Lab's AMS module. To ensure longevity and consistent print quality, an abrasion-resistant nozzle is recommended.

Custom car interior part 3D printed with the PET-CF17 filament

Image 2: Custom car interior part 3D printed with the PET-CF17 filament. Source: Fiberon.

To boost the thermal and mechanical performance, PET-CF17 parts should undergo a 120 ºC annealing process for 10 hours. This process requires careful handling to prevent deformation. Guidelines include waiting 24 hours after printing (or drying at 80 ºC for 2 hours) to relieve internal stresses, ensuring uniform oven temperatures, and adding supports (PolySupport for PA12) for parts with overhangs, thin walls, or bridging structures. For optimal results, parts should be placed in the oven in the same orientation as during printing, ideally on the build plate itself, ensuring precise dimensional accuracy and long-term stability.

General information
Material PET
Format 500 g / 3 kg
Density (ISO 1183) 1.34 g/cm³
Filament diameter 1.75 mm
Filament length (Ø 1.75 mm-0.5 Kg) ±155.1 m / (Ø 1.75 mm-3 Kg) ±930.8 m

Printing properties
Printing temperature 270 - 300 ºC
Print bed temperature 70 - 80 ºC
Chamber temperature 20 - 25 ºC
Cooling fan ✗
Recommended printing speed Max. 300 mm/s
Recommended nozzle Hardened Steel

Mechanical properties
Charpy impact strength (ISO 179) 5.1 ± 0.2 KJ/m²
Elongation at break (ISO 527) XY: 2.4 ± 0.5 % / Z: 0.8 ± 0.1 %
Tensile strength (ISO 527) XY: 65.9 ± 1.0 MPa / Z: 27.9 ± 1.3 MPa
Tensile modulus (ISO 527) XY: 5481.0 ± 223.7 MPa / Z: 3558.8 ± 260.4 MPa
Flexural strength (ISO 306) XY: 109.3 ± 2.0 MPa / Z: 43.4 ± 8.8 MPa
Flexural modulus (ISO 178) XY: 4744.4 ± 136.3 MPa / Z: 2768.2 ± 422.6 MPa
Surface hardness -

Electrical properties
Surface electrical resistivity (ANSI ESD S11.11) OL, > 10¹² Ohm

Thermal properties
Melting temperature (DSC) 241.3 ºC
Softening temperature (ISO 306) 238.4 ºC

Specific properties
Transparency ✗
Flammability classification UL 94 HB @ 1.5 mm

Other
HS Code 3916.9
Spool diameter (outer) (0.5 kg) 200±1 mm / (3 kg) 250±1 mm
Spool diameter (inner hole) (0.5 kg) 55±1 mm / (3 kg) 55±1 mm
Spool width (0.5 kg) 65.6±2 mm / (3 kg) 117.2±2 mm

To achieve optimal print quality with the Fiberon PET-CF17 filament, it is recommended to set the extrusion temperature between 270-300 ºC, and the print bed should be maintained between 70-80 ºC. A room temperature for the build chamber is sufficient, and it is best to keep the cooling fan turned off. Fiberon PET-CF17 supports high-speed printing with speeds of up to 300 mm/s, making it suitable for projects where efficiency is crucial.

Proper filament storage is essential for maintaining the quality of Fiberon PET-CF17. To prevent compromised print quality due to moisture, it should be stored in a sealed container with desiccant. If the filament absorbs excess moisture, drying it at 100 ºC for 10 hours in a filament dryer is recommended (or PolyDryer at level 3 for 18 hours) to restore its optimal printing properties.

Since the Fiberon PET-CF17 filament contains abrasive carbon fibers, it is highly recommended to use an abrasion resistant nozzle (hardnened steel, vanadium, ruby tip, etc) to avoid its excessive wear and, in consequence, inferior part quality.

Featured properties

Printing temperature
270 - 300 ºC
Filament diameter
1.75 mm
High speed compatible
Yes
Density
1.34 g/cm³