Fiberon PETG-rCF08

FIBERON-PETGrCF08-BLACK-175-500
19.00 € 19.00 €
Tax excl.
Diameter
Format
Colour
Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 15 - 21 days Available for shipment within 15 - 21 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Wednesday 8 January - Thursday 16 January
Available

The PETG-rCF08 filament from the Fiberon catalog of filaments is a versatile engineering-grade material, formulated with a PETG base reinforced by an 8% load of recycled carbon fiber. This unique blend combines the broad performance profile of PETG with the enhanced mechanical and aesthetic qualities imparted by carbon fiber reinforcement. Designed to yield high dimensional accuracy, this filament is ideal for producing components with demanding tolerances, suitable for applications in automotive, consumer products, and rapid prototyping.

Component 3D printed with the PETG-rCF08 filament

Image 1: Component 3D printed with the PETG-rCF08 filament. Source: Fiberon.

As an entry-level composite filament, PETG-rCF08 balances advanced properties with user-friendly printing characteristics, including low creep and compatibility with high-speed printing up to 300 mm/s. The filament does not require an actively heated chamber, enabling reliable results at room temperature. Optimal for 3D printers built for composite extrusion, such as the Raise3D E2CF or Bambu Lab X1C, PETG-rCF08 also supports multimaterial systems, like Bambu Lab's AMS module. To ensure longevity and consistent print quality, an abrasion-resistant nozzle is recommended.

Drone made with parts 3D printed with the PETG-rCF08 filament

Image 2: Drone made with parts 3D printed with the PETG-rCF08 filament. Source: Fiberon.

With notable mechanical properties—such as a Charpy impact resistance of 4 kJ/m², elongation at break of 5.7%, tensile strength of 59.8 MPa, and flexural strength of 94.6 MPa—PETG-rCF08 provides a robust foundation for functional parts. Its tensile and flexural moduli, at 3710 MPa and 3779 MPa respectively, demonstrate solid structural integrity across varied applications. For projects requiring even higher strength and stiffness, the Fiberon PET-CF17 filament is an excellent alternative thanks to its higher carbon fiber contents.

General information
Material PETG
Format 500 g / 3 kg
Density (ISO 1183) 1.30 g/cm³
Filament diameter 1.75 mm
Filament length (Ø 1.75 mm-0.05 Kg) ±159.9 m / (Ø 1.75 mm-0.5 Kg) ±959.4 m

Printing properties
Printing temperature 240 - 270 ºC
Print bed temperature 60 - 70 ºC
Chamber temperature 20 - 25 ºC
Cooling fan 0 - 50 %
Recommended printing speed Max. 300 mm/s
Recommended nozzle Hardened Steel

Mechanical properties
Charpy impact strength (ISO 179) 4.0 ± 0.9 KJ/m²
Elongation at break (ISO 527) XY: 5.7 ± 1.0% / Z: 1.9 ± 0.3 %
Tensile strength (ISO 527) XY: 59.8 ± 0.3 MPa / Z: 41.1 ± 4.1 MPa
Tensile modulus (ISO 527) XY: 3710.1 ± 151.1 MPa / Z: 2651.9 ± 51.0 MPa
Flexural strength (ISO 306) XY: 94.6 ± 1.3 MPa / Z: 47.8 ± 2.4 MPa
Flexural modulus (ISO 178) XY: 3779.1 ± 40.6 MPa / Z: 1622.2 ± 104.6 MPa
Surface hardness -

Electrical properties
Surface electrical resistivity (ANSI ESD S11.11) OL, > 10¹² Ohm

Thermal properties
Softening temperature (ISO 306) 81.6 ºC
Heat deflexion temperature (ISO 75) @ 0.45 MPa: 68.6 ºC / @ 1.8 MPa: 65.7 ºC

Specific properties
Transparency ✗
Flammability classification UL 94 HB @ 1.5 mm

Other
HS Code 3916.9
Spool diameter (outer) (0.5 kg) 200±1 mm / (3 kg) 250±1 mm
Spool diameter (inner hole) (0.5 kg) 55±1 mm / (3 kg) 55±1 mm
Spool width (0.5 kg) 65.6±2 mm / (3 kg) 117.2±2 mm

To achieve optimal print quality with the Fiberon PETG-rCF08 filament, it is recommended to set the extrusion temperature between 240-270 ºC, and the print bed should be maintained between 60-70 ºC. A room temperature for the build chamber is sufficient, and it is best to keep the cooling fan at 0-50 % speed. Fiberon PETG-rCF08 supports high-speed printing with speeds of up to 300 mm/s, making it suitable for projects where efficiency is crucial.

Proper filament storage is essential for maintaining the quality of Fiberon PETG-rCF08. To prevent compromised print quality due to moisture, it should be stored in a sealed container with desiccant. If the filament absorbs excess moisture, drying it at 65 ºC for three hours in a filament dryer is recommended (or PolyDryer at level 2 for 6 hours) to restore its optimal printing properties.

Since the Fiberon PETG-rCF08 filament contains abrasive carbon fibers, it is highly recommended to use an abrasion resistant nozzle (hardnened steel, vanadium, ruby tip, etc) to avoid its excessive wear and, in consequence, inferior part quality. 

Featured properties

Printing temperature
240 - 270 ºC
Filament diameter
1.75 mm
High speed compatible
Yes
Recycled
Yes
Density
1.3 g/cm³