xPRO1100 Black resin Nexa 3D

Ref.: RS-NEXA-XPRO1100.BLACK-1500

240.00 €

Tax excl.

Format

Quantity

In stock 2 units available for immediate shipping.
units available for shipping in 5 - 9 days Available for shipment within 5 - 9 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Friday 27 December

Available

Returns

Ask about this product

The xPRO1100 Black resin from the Nexa3D portfolio of engineering resins is meticulously designed to meet the rigorous demands of industrial applications, offering unparalleled performance and reliability. With its versatile applications spanning across automotive components, aerospace prototypes, engineering parts, and consumer products, this resin sets a new standard in additive manufacturing.

Part 3D printed with the xPRO1100 Black resin

Image 1: Part 3D printed with the xPRO1100 Black resin. Source: Nexa3D.

Nexa3D's commitment to quality is demonstrated through extensive testing under hostile industrial environments. Parts 3D printed with the xPRO1100 Black resin undergo rigorous assessments, including glow-wire test, hot-wire ignition (HWI), flammability, and accelerated UV ageing, ensuring exceptional resistance to UV rays, extreme temperatures, chemical agents, and pressure.

Parts 3D printed with the xPRO1100 Black resin perform well in accelerated UV ageing tests

Image 2: Parts 3D printed with the xPRO1100 Black resin perform well in accelerated UV ageing tests. Source: Nexa3D.

One of the hallmark features of the xPRO1100 Black resin is its superior UV resistance, with minimal color alteration and negligible loss of properties even after prolonged exposure. Moreover, the xPRO1100 Black resin boasts industrial-grade chemical resistance, as evidenced by weight and mechanical performance measurements of submerged parts in substances like acetone, brake fluid, engine oil, and sodium hydroxide.

Part 3D printed with the xPRO1100 Black resin

Image 3: Part 3D printed with the xPRO1100 Black resin. Source: Nexa3D.

For comprehensive insights into the performance metrics, detailed test results are readily available in the Technical Datasheet in the Downloads section. Elevate your additive manufacturing capabilities with the xPRO1100 Black resin, engineered for precision, durability, and unmatched reliability in the most demanding industrial settings.

Curing, washing, and sintering properties
Washing time	-
Curing time	-
Curing temperature	- ºC

General information
Manufacturer	Nexa 3D
Material	Photopolymer
Format	1.5 kg / 5 kg
Technology	LED / LCD
Wavelength	- nm
Compatible 3D printers	Nexa 3D
Viscosity	(ASTM D7867) @ 25 ºC: 280 cP / @ 30 ºC: 190 cP
Density (solid)	(ASTM D792) 1.2 g/cm³
Density (liquid)	(ASTM D4052-18a) 1.11 g/cm³

Printing properties
Layer height	- µm
Layer exposure time	-
Layer off time	-
Lifting height	- mm
Bottom layer exposure	-
Bottom layer count	-

Mechanical properties
Izod impact strength	- KJ/m²
Charpy impact strength	(ISO179-1) 1.11 KJ/m²
Elongation at break	(ASTM D638) 4 %
Tensile strength	(ASTM D638) 71 MPa
Tensile modulus	(ASTM D638) 3010 MPa
Flexural strength	(ASTM D790) 125 MPa
Flexural modulus	(ASTM D790) 2790 MPa
Surface hardness	(ASTM D2240) Shore 84 D

Thermal properties
Softening temperature	77 ºC
Flammability classification	(UL94) HB (1.5 mm)
Glass transition temperature	(ASTM D4065) 141 ºC
Heat deflexion temperature	(ASTM D648) @ 0.45 MPa: 77-112 ºC / @ 1.82 MPa: 61-93 ºC

Specific properties
Maximum water absorption	(ASTM D570) 24 h: 0.14 % / 2500 h: 2 %

Other
HS Code	2916.1
Lifetime (since manufacturing)	- M

Parts 3D printed with the Nexa 3D xPRO1100 Black resin will achieve their specific properties only after being subjected to post-processing by washing and curing. If applicable, the support structures must be removed from the part before curing and the part must be washed. Nexa3D recommends using xClean (max. 2 minutes) followed by IPA alcohol (max. 5 minutes).

Once washed, the parts 3D printed with the xPRO1100 Black resin must be dried and then cured either with the help of an LED or wide spectrum lamp, or in the Nexa 3D Wash+Cure station developed especially for the washing and curing of parts 3D printed on the XiP 3D printer. The recommended washing, drying and curing times can be consulted on the manufacturer's website for each Nexa 3D resin. After the post-curing, parts 3D printed with the xPRO1100 Black resin can be subjected to an additional thermal treatment. The instructions can be found in the product's Technical Datasheet in the Downloads section.

Certain precautions must be taken when working with 3D printing resins. The user must ensure that the working space is adequately ventilated, and that protective goggles, gloves and garments are worn at all times. The xPRO1100 Black resin should be stored in a tightly closed container/resin vat to avoid resin deterioration due to UV exposure. The container/vat should be kept in a cool, well ventilated area away from heat, sparks and open flame.

More information on how to print and post-process the Nexa 3D resins can be found here.