IND249 Black resin - Loctite 3D
search
  • IND249 Black resin - Loctite 3D
  • IND249 Black resin - Loctite 3D
Compare
You must be logged in to manage your wishlist.

IND249 Black resin - Loctite 3D

RS-LOC-IND249-BLACK-1KG
260.00 € 260.00 €
Tax excl.
Format
Colour
Quantity

In stock 4 units available for immediate shipping.
units available for shipping in 5 - 7 days Available for shipment within 5 - 7 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Friday 22 November
Available

The low-viscosity high-resolution IND249 Black resin from the Loctite family of high temperature resistant resins enables the additive manufacturing of exceptionally strong and durable parts with intricate geometries and great thermal resistance (HDT of 115 ºC at 0.45 MPa). Furthermore, the resulting parts exhibit high accuracy and are easily post-processable.

The IND249 Black resin

Image 1: The IND249 Black resin. Source: Loctite.

The IND249 Black resin is the perfect material for functional part production, e.g. mold tooling at high temperatures or the preparation of manufacturing aids in sectors such as industrial manufacturing or consumer goods.

The IND249 Black resin has been formulated to print optimally on industrial DLP printers. Before printing with this material, the user should read safety and technical information available in the Downloads section. In the Usage Tips section useful resources can be found on printer compatibility, recommended post-processing settings, and proper resin storage.

Curing, washing, and sintering properties
Washing time 2 min
Curing time 10 - 30 min
Curing temperature - ºC

General information
Manufacturer Loctite
Material Photopolymer
Format 1 kg / 5 kg
Technology DLP
Wavelength - nm
Viscosity (ASTM D7867) 444-461 cP
Density (solid) (ASTM D792) 1.17-1.20 g/cm³
Density (liquid) (ASTM D792) 1.09-1.10 g/cm³

Mechanical properties
Izod impact strength - KJ/m²
Charpy impact strength - KJ/m²
Elongation at break (ASTM D638) 4 - 7 %
Tensile strength (ASTM D638) 83 - 98 MPa
Tensile modulus (ASTM D638) 2980 - 3350 MPa
Flexural strength (ASTM D790) 127 - 153 MPa
Flexural modulus (ASTM D790) 3170 - 3600 MPa
Surface hardness (ASTM D2240) Shore 81 - 88 D

Printing properties
Layer height - µm
Layer exposure time -
Layer off time -
Lifting height - mm
Bottom layer exposure -
Bottom layer count -

Thermal properties
Softening temperature 117 ºC
Heat deflexion temperature (ASTM D648) @ 0.45 MPa: 113-117 ºC / @ 1.82 MPa: 96-101 ºC

Specific properties
Maximum water absorption (ASTM D570) 24 h: 0.5-0.7 % / 72 h: 0.7-0.9 %

Other
HS Code 2916.1
Lifetime (since manufacturing) - M

On the Henkel YouTube channel, various videos are available on:

  1. How to work with 3D printing resins:

    Video 1: The basics of printing with resin. Source: Henkel.
  2. How to properly store 3D printing resins:

    Video 2: How to properly store resins. Source: Henkel.
  3. How to post-process parts 3D printed with resin:

    Video 3: Resin post-processing tips. Source: Henkel.

The material's technical and safety datasheets can be found in the Downloads section. On the manufacturer's website the user can find the printer validation information as well as the recommended printing and postprocessing settings.

Featured properties

Technology
DLP

Related products