Liqcreate Flexible-X resin

Ref.: LIQC-FLEXIBLEX-250

43.95 €

Tax excl.

Format

Volume discounts

Quantity	Discount	Price
10	10% 10%	39.56 € 39.56 €
15	12% 12%	38.68 € 38.68 €

Quantity

In stock 1 units available for immediate shipping.
units available for shipping in 3 - 4 days Available for shipment within 3 - 4 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Thursday 30 October

Returns

Ask about this product

The Flexible-X resin by Liqcreate, a Dutch designer and manufacturer of premium 3D printing resins, is an extremely flexible resin for DLP, LCD, SLA and MSLA 3D-printers. Parts 3D printed with the Flexible-X resin are characterized by high elongation at break (120-160 %), excellent rebound, good tear strength, and a soft touch. These properties make the Flexible-X resin ideal for the manufacturing of soft but extremely flexible parts for industrial uses.

Video 1: Testing parts 3D printed with the Flexible-X resin. Source: Liqcreate.

Due to the fact that flexible resins tend to be slightly more challenging to work with than rigid resins, it is recommended to consult the Liqcreate guide to 3D printing with their flexible resins available on the Liqcreate support page.

A flexible part 3D printed with the Flexible-X resin

Image 1: A flexible part 3D printed with the Flexible-X resin. Source: Liqcreate.

Thanks to the wide range of compatible light sources (385-420 nm), the Flexible-X resin can be used on many open source 3D printers by brands such as Anycubic, Creality or Phrozen. The full list of compatible printers is available here.

General information
Manufacturer	Liqcreate
Material	Photopolymer
Format	0.25 kg / 1 kg
Technology	SLA / LED-LCD / DLP
Wavelength	385 - 405 nm
Viscosity	@ 25 ºC: 950 cP
Density (liquid)	1.18 g/cm²

Mechanical properties
Izod impact strength	- KJ/m²
Charpy impact strength	- KJ/m²
Elongation at break	(ASTM D638M) 120 - 160 %
Tensile strength	(ASTM D638M) 2.4 MPa
Tensile modulus	- MPa
Flexural strength	- MPa
Flexural modulus	- MPa
Surface hardness	(ASTM D2240) Shore 55 A

Printing properties
Layer height	25 - 100 µm
Layer exposure time	-
Layer off time	-
Lifting height	- mm
Bottom layer exposure	-
Bottom layer count	-

Thermal properties
Softening temperature	- ºC

Specific properties
Maximum water absorption	(D570-98) 3.3 %

Curing, washing, and sintering properties
Washing time	4 - 5 min
Curing time	-
Curing temperature	- ºC

Other
HS Code	2916.1
Lifetime (since manufacturing)	- M

On the Liqcreate website the user can find a guide on how to process flexible 3D printing resins. More useful resources such as tips on how to use support structures with the Liqcreate resins, or on how to color, age or mix the resins can be found on the Liqcreate support page.

In order to ensure resin longevity and successful 3D prints, it is advised to store the Flexible-X resin in a clean and dry environment, out of direct sunlight and in a temperature of 5-30 ºC. Before use, the resin bottle should be shaken energetically for at least 1 minute (at least 3 minutes in the case of filled resins) and then left to rest for around 10 minutes to let the air bubble escape. Leftover resin can be poured back into the bottle but it should be first filtered to ensure there is no polymer residue present. Safety equipment such as protective garments, gloves and face protection is highly recommended for the handling of resin.

As far as the post-processing of the Flexible-X resin, a few simple steps must be followed. First, the 3D printed part has to be cleaned for a maximum of 6 minutes in Liqcreate Resin Cleaner, IPA alcohol or bioethanol, preferably ultrasonic or under agitation. Then the completely dried part has to be cured in a high-power UV curing chamber. The curing workflow is explained in detail by the manufacturer here. It absolutely crucial that the parts are dry before they are cured. The curing of wet or sticky parts will lead to mechanical and surface defects. The drying can be done by simply leaving the cleaned part in a well ventilated area for at least 30 minutes or with the help of pressurized air (2 minutes) for parts cleaned in IPA alcohol or ethanol.