Fiberon PA6-CF20

FIBERON-PA6CF20-BLACK-175-500
37.18 € 37.18 €
Tax excl.
Diameter
Format
Colour
Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 15 - 21 days Available for shipment within 15 - 21 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Tuesday 17 December - Monday 6 January
Available

The PA6-CF20 filament from the Fiberon line of high-performance polymers is a PA6-based material reinforced with 20% carbon fiber, offering exceptional strength, stiffness, and isotropic rigidity. With a heat resistance reaching up to 215 ºC, PA6-CF20 is suitable for demanding applications that require stability under high temperatures. It also features Fiber Adhesion™ Technology, which promotes superior layer adhesion, resulting in robust, cohesive printed parts. These properties make PA6-CF20 ideal for challenging uses in automotive, composite manufacturing, and industrial components, where performance and durability are critical. If a filament with even better mehanical properties and reduced moisture sensitivity is required, please see the Fiberon PA612-CF15 filament.

Part 3D printed with the PA6-CF20 filament

Image 1: Part 3D printed with the PA6-CF20 filament. Source: Fiberon.

The PA6-CF20 filament balances advanced properties with user-friendly printing characteristics, including low creep and compatibility with high-speed printing up to 300 mm/s. The filament does not require an actively heated chamber, enabling reliable results at room temperature. Optimal for 3D printers built for composite extrusion, such as the Raise3D E2CF or Bambu Lab X1C, PA6-CF20 also supports multimaterial systems, like Bambu Lab's AMS module. To ensure longevity and consistent print quality, an abrasion-resistant nozzle is recommended.

A resistent housing 3D printed with the PA6-CF20 filament

Image 2: A resistent housing 3D printed with the PA6-CF20 filament. Source: Fiberon.

To boost the thermal and mechanical performance, PA6-CF20 parts should undergo a 100 ºC annealing process for 16 hours. This process requires careful handling to prevent deformation. Guidelines include waiting 24 hours after printing (or drying at 80 ºC for 2 hours) to relieve internal stresses, ensuring uniform oven temperatures, and adding supports (PolyDissolve S1) for parts with overhangs, thin walls, or bridging structures. For optimal results, parts should be placed in the oven in the same orientation as during printing, ideally on the build plate itself, ensuring precise dimensional accuracy and long-term stability.

General information
Material PA
Format 500 g / 3 kg
Density (ISO 1183) 1.17 g/cm³
Filament diameter 1.75 mm
Filament length (Ø 1.75 mm-0.5 Kg) ±177.7 m / (Ø 1.75 mm-3 Kg) ±1066.0 m

Electrical properties
Surface electrical resistivity (ANSI ESD S11.11) OL, >10¹² Ohm

Printing properties
Printing temperature 280 - 300 ºC
Print bed temperature 40 - 50 ºC
Chamber temperature 20 - 25 ºC
Cooling fan ✗
Recommended printing speed Max. 300 mm/s
Recommended nozzle Hardened Steel

Mechanical properties
Charpy impact strength (ISO 179) 11.0 ± 0.3 KJ/m²
Elongation at break (ISO 527) XY: 2.1 ± 0.2 % / Z: 1.9 ± 0.4 %
Tensile strength (ISO 527) XY: 109.3 ± 2.4 MPa / Z: 54.0 ± 5.2 MPa
Tensile modulus (ISO 527) XY: 8636.5 ± 211.4 MPa / Z: 3759.5 ± 118.5 MPa
Flexural strength (ISO 306) XY: 161.0 ± 3.9 MPa / Z: - MPa
Flexural modulus (ISO 178) XY: 7037.6 ± 205.4 MPa / Z: - MPa
Surface hardness -

Thermal properties
Melting temperature (DSC) 218.5 ºC
Softening temperature - ºC
Heat deflexion temperature (ISO 75) @ 0.45 MPa: 215 ºC / @ 1.8 MPa: 173 ºC

Specific properties
Transparency ✗
Flammability classification UL 94 HB @ 1.5 mm
Chemical resistance ✓

Other
HS Code 3916.9
Spool diameter (outer) (0.5 kg) 200±1 mm / (3 kg) 250±1 mm
Spool diameter (inner hole) (0.5 kg) 55±1 mm / (3 kg) 55±1 mm
Spool width (0.5 kg) 65.6±2 mm / (3 kg) 117.2±2 mm

To achieve optimal print quality with the Fiberon PA6-CF20 filament, it is recommended to set the extrusion temperature between 280-300 ºC, and the print bed should be maintained between 40-50 ºC. It must be kept in mind that printing on a hotter bed will deactivate the Warp-Free technology. A room temperature for the build chamber is sufficient, and it is best to keep the cooling fan turned off. Fiberon PA6-CF20 supports high-speed printing with speeds of up to 300 mm/s, making it suitable for projects where efficiency is crucial.

Proper filament storage is essential for maintaining the quality of Fiberon PA6-CF20. To prevent compromised print quality due to moisture, it should be stored in a sealed container with desiccant. If the filament absorbs excess moisture, drying it at 100 ºC for 10 hours in a filament dryer is recommended (or PolyDryer at level 3 for 18 hours) to restore its optimal printing properties.

Since the Fiberon PA6-CF20 filament contains abrasive carbon fibers, it is highly recommended to use an abrasion resistant nozzle (hardnened steel, vanadium, ruby tip, etc) to avoid its excessive wear and, in consequence, inferior part quality.

Featured properties

Printing temperature
280 - 300 ºC
Filament diameter
1.75 mm
High speed compatible
Yes
Density
1.17 g/cm³