Facilan PCL 100

FACILAN-PCL-100-175-750
105.00 € 105.00 €
Tax excl.
Diameter
Format
Quantity

In stock 5 units available for immediate shipping.
units available for shipping in 0 - 0 days Available for shipment within 0 - 0 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Monday 25 November
Available

Facilan PCL 100 filament is a homopolymer of polycaprolactone, a semi-crystalline aliphatic polyester, fully biodegradable and non-toxic, with a white final appearance, a glass transition temperature of -60 °C and a printing temperature of about 120 °C.

Facilan PCL 100 filament in the extrusion process

Image 1: Facilan PCL 100 filament in the extrusion process. Source: 3D4Makers.

 It is manufactured from a raw material produced in accordance with the European regulations EC No 1935/2004 and EC No 10/2011 for plastic materials and articles in contact with food.

A shoe insole 3D printed with Facilan PCL 100

Image 2: A shoe insole 3D printed with Facilan PCL 100. Source: 3D4Makers.

Facilan PCL 100 is a very flexible and tough filament. The material has incredible interlayer adhesion, which means greatly improved impact resistance, strength, durability and printability. Due to its low melting point (around 60°C), Facilan PCL100 filament can be remoulded in water at 55°C after printing, which is useful in applications where the 3D printed object must conform to, for example, a patient's body.

An ear splint 3D printed with Facilan PCL 100 filament

Image 3: An ear splint 3D printed with Facilan PCL 100 filament. Source: 3D4Makers.

Facilan PCL 100 is used by many leading universities and research centres worldwide for bioprinting and medical research. Its applications for medical research include artificial tracheas, tissue engineering scaffolds, bioabsorbable implants, drug-loaded implants, orthopaedic devices, orthodontic braces, smart materials and other cutting-edge applications. However, Facilan PCL 100 filament is not yet licensed for use in medical applications involving permanent implantation in the human body.

General information
Material PCL
Format 0.75 / 2.3 kg
Density 1.1 g/cm³
Filament diameter 1.75 / 2.85 mm
Filament tolerance - mm
Filament length (Ø 1.75 mm 750 g) 283.5 m / (Ø 2.85 mm 750 g) 106.9 m / (Ø 1.75 mm 2300 g) 869.3 m / (Ø 2.85 mm 2300 g) 327.8 m

Printing properties
Printing temperature 130 - 170 ºC
Print bed temperature 30 - 45 ºC
Chamber temperature -
Cooling fan 100 %
Recommended printing speed 20 - 40 mm/s

Mechanical properties
Izod impact strength (ISO 180-1) 8 KJ/m²
Elongation at break (ISO 527) 15 %
Tensile strength (ISO 527) 45 MPa
Tensile modulus (ISO 527) 320 MPa
Flexural strength (ISO 178) 18 MPa
Flexural modulus (ISO 178) 380 MPa
Surface hardness (ISO 868) Shore 46 D

Thermal properties
Softening temperature (ISO 75 B) 57 ºC

Other
HS Code 3916.9
Spool diameter (outer) - mm
Spool diameter (inner hole) - mm
Spool width - mm

Facilan PCL 100 filament should be 3D printed at 130-170°C at 10-30 mm/s, on a bed heated to 30-45°C, with the layer fan set to 100%. To allow cold extrusion (below 170°C), "M302 S120" should be added at the beginning of the g-code.

Regarding the adhesion to the bed, the manufacturer recommends the use of Ultimaker adhesion films or PEI surfaces. The recommended support material for Facilan PCL 100 filament is water soluble PVA or breakaway support.

For more detailed technical and safety information, please refer to the "Downloads" section.

Featured properties

Printing temperature
130 - 170 ºC
Filament diameter
1.75 / 2.85 mm
Food contact certificate
Yes
Density
1,1 g/cm³