CarbonX™ PEEK CF10

Ref.: 3DXTECH-PEEK-CF-175-500

325.00 €

Tax excl.

Diameter

Format

Volume discounts

Quantity	Discount	Price
10	10% 10%	292.50 € 292.50 €

Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 10 - 15 days Available for shipment within 10 - 15 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Monday 7 July - Monday 14 July

Available

Returns

Ask about this product

In the world of FDM/FFF 3D printing, there is a family of materials that has stood out clearly above all others for some years now, the PAEK family (polyaryletherketone or polyaryletherketone ether ketone). The materials belonging to this class are semi-crystalline plastics, which withstand high temperatures (around 200 ºC) while maintaining high mechanical strength values.

The PAEK family includes PEEK, PEKK and PEI. All of them have high mechanical strength, chemical resistance and high temperature flammability.

PEEK (polyetheretheretherketone) is one of the world's highest performing polymers. PEEK has exceptional mechanical, thermal and chemical resistance properties, making it an ideal material for some of the most demanding applications such as seals, gears, bushings, bearings, pump and compressor components. Industries such as automotive, aerospace, defence, defence, semiconductor and oil/gas depend on PEEK for applications where failure is not an option.

CarbonX™ PEEK CF10 filament is a filament composed of PEEK and reinforced with carbon fibre, which gives the material exceptional stiffness, strength and dimensional stability.

Some of the most important properties of CarbonX™ PEEK CF10 filament are the following:

Superior mechanical properties, especially at elevated temperatures.
Excellent chemical resistance.
Low coefficient of linear thermal expansion (CTE).
Almost zero moisture absorption.
Low emission of toxic fumes and gases.
PEEK has excellent resistance to hydrolysis in boiling water and superheated steam (sterilisation/autoclave) at temperatures above 250°C.

This filament is an advanced material that requires the use of a industrial 3D printer that reaches printing temperatures of 380-410°C and a chamber temperature of up to 140°C. Due to its difficulty in printing, this filament is recommended for expert users.

General information
Material	PEEK/PEKK
Format	500 g
Density	(ISO 1183) 1.39 g/cm³
Filament diameter	1.75 mm
Filament tolerance	± 0.05 mm
Filament length	± 150 m

Electrical properties
Surface electrical resistivity	(ASTM D257) 10⁹ Ohm/sq

Printing properties
Printing temperature	400 ºC
Print bed temperature	130 - 140 ºC
Chamber temperature	140 ºC
Cooling fan	✗
Recommended printing speed	10 - 50 mm/s

Mechanical properties
Elongation at break	(ISO 527) 3 %
Tensile strength	(ISO 527) 105 MPa
Tensile modulus	(ISO 527) 8100 MPa
Flexural strength	(ISO 178) 136 MPa
Flexural modulus	(ISO 178) 8300 MPa
Surface hardness	-

Thermal properties
Melting temperature	343 ºC
Softening temperature	264 ºC

Specific properties
Transparency	-
Chemical resistance	✓

Other
HS Code	3916.9
Spool diameter (outer)	200 mm
Spool diameter (inner hole)	52 mm
Spool width	55 mm

The use of PEEK CF requires extensive experience in the 3D printing industry and a qualified 3D printer, as it requires an extrusion temperature of 380-410°C, a base temperature of 130-150°C and a chamber temperature of up to 140°C, therefore it is recommended to use industrial 3D printers that meet all requirements.

To ensure good adhesion to the substrate and to avoid warping, the use of Nano Polymer Adhesive is recommended.

In the case of PEEK CF filament, it is recommended to use a nozzle with at least 0.5 mm output diameter to avoid clogging. In addition, it is highly recommended that the nozzle be made of hardened steel, as carbon fibre can be very abrasive.