Timberfill pellets

Reference:

Brand: Fillamentum

This product could be delivered in a longer time than the standard.

Condition: New product

Format

Colour

Quantity

22,04 €

Ask for information

Biodegradable Timberfill pellets with spruce fibers. Look, feel and smell of wood.

Add to wishlist

More info
Data sheet
Download
Usage tips
Specifications

Timberfill by Fillamentum is a PLA-based material additivized with spruce fibers to give the 3D printed parts the look, feel and temporary smell of wood. Originally released in filament format, Timberfill is also available in pellet format for BAAM (Big Area Additive Manufacturing) and MAAM (Middle Area Additive Manufacturing) with the help of FGF manufacturing solutions such as the CEAD AM Flexbot, the CEAD E25 extruder, the Mahor V4 pellet extruder, or the Dyze Pulsar extruder.

A plant pot 3D printed with the Timberfill Light Wood Tone

Image 1: A plant pot 3D printed with Timberfill Light Wood Tone. Source: Fillamentum.

The Timberfill pellets come in the color Light Wood Tone, exhibit high mechanical resistance and hardness (Shore hardness 77 D), great interlayer adhesion, and a temperature resistance of up to 50 ºC. The Timberfill pellets are as easy to work with as standard PLA. The recommended processing temperature is 165-185 ºC.

Since Timberfill is a 100% bio-based material, it is fully biodegradable in industrial conditions. Industrial composting plants are usually more controlled than natural environments, and have the ideal pressure and temperature conditions for these materials to degrade in the shortest possible time.

Elongation at break (%)	2
Tensile strength (MPa)	39
Tensile modulus (MPa)	3200
Surface hardness	8
Biodegradable	Biodegradable
Fiber reinforced	Fiber reinforced
Hide color variations	(Hide color variations)

Timberfill pellet Datasheet

Download

Timberfil pellet Safe. Datasheet

Download

The proper storage of 3D printing materials is key to smooth extrusion, and great surface quality and mechanical properties of the 3D printed part. The Timberfill pellets should be stored in a closed package in dry conditions at temperature below 50 ºC, protected from UV-light at all times. If the pellets absorb excess moisture, they should be dried for 2-3 hours at 50 ºC. The recommended processing temperature for the Timberfill pellets is 165 - 185 ºC.

General Information
Material	PLA
Format	1 kg 5 kg 15 kg
Density	1.25 g/cm³
Color	Natural
Mechanical Properties
Izod Impact Strength	-
Charpy Impact Strength (ISO 179)	(unnotched) 22 kJ/m²
Ultimate Tensile Strength (ISO 527)	39 MPa
Maximum Strain at Break (ISO 527)	2 %
Tensile Strength	-
Tensile Modulus (ISO 527)	3200 MPa
Flexural Strength	-
Flexural Modulus	-
Surface Hardness (ISO 7619)	Shore 77 D
Thermal Properties
Processing Temperature (ISO 306)	165 - 185 ºC
Glass Transition Temperature	-
Melting Temperature (ISO 11357)	175 ºC
MFR Ratio (ISO 1133 @ 190 °C, 2.16 kg)	31 g /10 min
Electrical Properties
Volumetric Electrical Resistivity	10¹⁶ Ohm/cm
Additional Information
HS Code	3901.1

* The typical values detailed in this table should be considered as reference. We advise confirming the results and final properties with your own tests. For more information, consult the product's technical datasheet.