PA11 Onyx - Nylon-11 powder

PA11-ONYX-FRESH-2KG
198.00 € 198.00 €
Tax excl.
Type
Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 10 - 14 days Available for shipment within 10 - 14 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Wednesday 15 January - Tuesday 21 January
Available

Aliphatic polyamides or nylons have been, since their appearance, one of the most widely used families of thermoplastic polymers in practically all industrial sectors, from textiles to aeronautics.

Nylon-11 is one of the polymers included in this family. Along with nylon-12, it is one of the aliphatic polyamides with the lowest melting temperature and lowest hygroscopicity, making it ideal for use in 3D SLS printing.

This last property is of great importance. During the 3D printing process the powder is heated to high temperatures, removing the hydration water during the process. A material with a high water absortion vapacity will release high amounts of water during the printing process, reducing its volume and being able to interfere in the sintering process.

higroscopicidad poliamidas

Image 1: Nylons water absortion plot. Source: http://www.plastix-world.com

Although PA11 is not as common as PA12 in 3D printing due to its higher melting point and requiring an inert atmosphere, its better mechanical properties make it a perfect material for those components subjected to more demanding conditions.

PA11 Onyx is a nylon-11 powder specially formulated by Sinterit for its Lisa Pro printer. It stands out mainly for its good mechanical properties, especially its impact resistance.

It has an ultimate tensile strength of 54 MPa with an elongation of 40%, a flexural strength of 62 MPa, as well as an impact resistance of 179 KJ/m2, which makes it a highly versatile material. Furthermore, its low hygroscopicity makes its dimensional stability very good, especially in environments with high variations in temperature and humidity.

Video 1: PA11 Onyx promotional video. Source: Sinterit

Among its main applications we can find:

  • Due to its low water absorption and its high dimensional stability, it is an ideal material to produce hydraulic components, pipes or medical catheters.
  • Protectors, housings and components subjected to impact stress, such as housings for field work products or sports protectors.
  • Components that are subjected to harsh conditions of humidity, temperature, chemical environment or solar radiation.

Muestras PA11

Image 2:Housings printed with PA11 Onyx. Source:Sinterit

For all these reasons it is an ideal material for those more demanding applications where PA12 is not enough.

General information
Manufacturer Sinterit
Material PA
Format 4 L, 2 kg / 12 L, 6 Kg
Technology SLS
Average granulation 40 µm
Material refreshing ratio 50 %
Compatible 3D printers Lisa Pro, Lisa X, Nils 480

Mechanical properties
Izod impact strength - KJ/m²
Charpy impact strength 179 KJ/m²
Elongation at break (ISO 37) 40 %
Tensile strength (ISO 37) 54 MPa
Tensile modulus 1680 MPa
Flexural strength ( ISO 178) 62 MPa
Flexural modulus 1290 MPa
Surface hardness (ISO 868) Shore 74 D

Thermal properties
Melting temperature 201 ºC
Softening temperature 185 ºC

Other
HS Code 3908.1
General information
Manufacturer Sinterit
Technology SLS
Material Nylon-11
Format 4 L bottle (2 Kg)
Granulation 20 - 80 µm
Material refreshing ratio 50 %
Color Black
Compatible 3D printers Lisa Pro
Mechanical properties
Tensile strength 54 MPa (PN-EN ISO 37-2007)
Tensile Modulus -
Elongation at break  40 % (PN-EN ISO 37-2007)
Flexural strength 62 MPa (PN-EN ISO 178:2011)
Flexural modulus -
Charpy impact strength 179 KJ/m2 (Sinterit's internal procedure)
Surface hardness 74 Shore-D (PN-EN ISO 868:2005)
Thermal properties
Softening temperature (Vicat A50 / B50) -
Melting point 201 ºC (Sinterit's internal procedure)
Heat deflection temperature B -
Surface roughness
Mean roughness (Ra) in XZ/YZ planes -
Mean roughness (Ra) in XY plane -
Mean roughness depth (Rz) in XZ/YZ planes -
Mean roughness depth (Rz) in XY plane -


* The typical values detailed in this table should be considered as a reference. Actual values may vary depending on the 3D printer model used, part design and printing conditions. We recommend confirming the results and final properties with own tests. For more information you should consult the technical data sheet of the product.

General information
Manufacturer Sinterit
Technology SLS
Material Nylon-11
Format 4 L bottle (2 Kg)
12 L bottle (6 Kg)
Granulation 20 - 80 µm
Material refreshing ratio 50 %
Color Black
Compatible 3D printers Lisa Pro, Lisa X, Nils 480
Mechanical properties
Tensile strength 54 MPa (PN-EN ISO 37-2007)
Tensile Modulus -
Elongation at break  40 % (PN-EN ISO 37-2007)
Flexural strength 62 MPa (PN-EN ISO 178:2011)
Flexural modulus -
Charpy impact strength 179 KJ/m2 (Sinterit's internal procedure)
Surface hardness 74 Shore-D (PN-EN ISO 868:2005)
Thermal properties
Softening temperature (Vicat A50 / B50) -
Melting point 201 ºC (Sinterit's internal procedure)
Heat deflection temperature B -
Surface roughness
Mean roughness (Ra) in XZ/YZ planes -
Mean roughness (Ra) in XY plane -
Mean roughness depth (Rz) in XZ/YZ planes -
Mean roughness depth (Rz) in XY plane -
Aditional information
HS Code 3908.1


* The typical values detailed in this table should be considered as a reference. Actual values may vary depending on the 3D printer model used, part design and printing conditions. We recommend confirming the results and final properties with own tests. For more information you should consult the technical data sheet of the product.